Catalytic regeneration of Diesel Particulate Filters: Comparison of Pt and CePr active phases

Diesel Particulate Filters (DPFs) have been loaded with the same amount (0.6 wt.%) of either Pt or an optimized CePr active phase, and an experimental set-up has been designated and used to investigate the catalytic combustion of soot under realistic reaction conditions. Both active phases were stable under reaction conditions, with no evidences of deactivation in consecutive combustion experiments. The presence of H2O and CO2 together with NOx and O2 in the gas mixture slightly delays soot combustion to higher temperatures, but the effect is equal for the Pt and CePr active phases. The mass of soot loaded into the filters had no effect in the catalytic regeneration of the DPFs for soot:catalyst weigh ratios below 0.4, while it was hindered above this ratio. The Pt and CePr active phases behave equal until 0.6 soot:catalyst weigh ratio and Pt performance was slightly better for higher soot loading. This difference is explaining according to the main soot combustion mechanisms occurring during Pt–DPF (NO2-assited) and CePr–DPF regeneration (active oxygen). The CO2 selectivity is near 100% for both catalysts in all the experimental reaction conditions evaluated. According to this study, the CePr active phase seems to be a promising candidate to replace Pt in real applications.The financial support of Generalitat Valenciana (Project PROMETEOII/2014/010)), Spanish Ministry of Economy and Competitiveness (Project CTQ2012-30703) and European Union (FEDER funding) is acknowledged

Effect of RhOx/CeO2 Calcination on Metal-Support Interaction and Catalytic Activity for N2O Decomposition

The effect of the calcination conditions on the catalytic activity for N2O decomposition of 2.5% RhOx/CeO2 catalysts has been investigated. Ramp and flash calcinations have been studied (starting calcinations at 25 or 250/350 °C, respectively) both for cerium nitrate and ceria-impregnated rhodium nitrate decomposition. The cerium nitrate calcination ramp has neither an effect on the physico-chemical properties of ceria, observed by XRD, Raman spectroscopy and N2 adsorption, nor an effect on the catalysts performance for N2O decomposition. On the contrary, flash calcination of rhodium nitrate improved the catalytic activity for N2O decomposition. This is attributed to the smaller size of RhOx nanoparticles obtained (smaller than 1 nm) which allow a higher rhodium oxide-ceria interface, favoring the reducibility of the ceria surface and stabilizing the RhOx species under reaction conditions.The authors thank the financial support of Generalitat Valenciana (Project Prometeo 2009/047), the Spanish Ministry of Economy and Competitiveness (Project CTQ2012-30703), and the UE (FEDER funding)

Arxiu històric del Camp de la Bota i la Mina. Historia i funció d'un arxiu comunitari

Treballs Finals de Grau d'Informació i Documentació, Facultat d'Informació i Mitjans Audiovisuals, Universitat de Barcelona, Curs: 2018-2019, Jornet i Benito, NúriaEl Pla de Transformació de la Mina de l’any 2000 i l’obertura del Fòrum, realitzats sense deixar rastre de l’antic Camp de la Bota, va fer sorgir un grup de persones, encapçalades per l’antic pedagog i escolapi, Josep Maria Monferrer, decidides a recuperar la memòria del barri. Era el naixement de l’Arxiu Històric i Centre de Documentació del Camp de la Bota i la Mina. Un arxiu, entitat o centre de documentació lligat a un grup de persones amb la voluntat de recollir informació d’aquell espai. Podríem definir o parlar dels arxius independents o comunitaris, també anomenats populars, com a pràctiques arxivístiques, molt vinculades a moviments, comunitats, grups i persones, sovint a banda de les institucions i estructures oficials. Aquestes persones s’encarreguen de recopilar, conservar i difondre documentació que l’arxivística oficial no recull i/o reflecteix i ho fan d’una manera voluntària i sovint amb connotacions polítiques i socials. L’Arxiu Històric del Camp de la Bota i la Mina el podríem incloure dins aquesta categoria d’unitat d’informació. Es tracta d’un centre amb informació d’una zona considerada com a força marginal de la ciutat de Sant Adrià de Besòs. Té un fort vincle social i un fort compromís de lluita veïnal, fins i tot amb un cert component polític, per la dignitat de les persones que hi habiten. També està molt vinculat al seu creador, el president i educador Josep Maria Monferrer i Celades. Gràcies a un projecte d’aprenentatge i servei (APS) iniciat al curs 2017-2018 sobre els barris de la Mina i del Camp de la Bota es veu la necessitat de documentar l’existència de l’arxiu, les seves característiques i la feina realitzada a partir de la implicació i la voluntat del seu titular, així com plantejar possibles alternatives de futur per a aquest arxiu. Es tracta d’un treball que pretén copsar l’estat de la situació de l’arxiu, fer-ne una aproximació, una descripció i unes propostes de futur, sense pretendre ser tècnic. L’arxiu es troba en un moment especial. El seu titular, Josep Maria Monferrer, és un home de 77 anys que està al capdavant de la gestió del centre i que s’està plantejant quina continuïtat i perspectives de futur pot tenir l’arxiu

Propuesta educativa del módulo profesional de F.O.L. en el ciclo formativo de grado medio de Técnico en cocina y gastronomía

Este Trabajo de Fin de Máster lo integra una programación didáctica de 15 unidades didácticas pensadas para impartir en el marco del grado medio de Técnico en cocina y gastronomía dentro del módulo profesional de F.O.L. Para idear esta propuesta se ha tenido en cuenta las particularidades y el contexto que se encuentra en el hipotético caso de impartirla en el I.E.D. Diego de Praves de Valladolid.Máster en Profesor de Educación Secundaria Obligatoria y Bachillerato, Formación Profesional y Enseñanzas de Idioma

Effect of the CeZrNd mixed oxide synthesis method in the catalytic combustion of soot

Ce0.64Zr0.27Nd0.09Oδ mixed oxides have been prepared by three different methods (nitrates calcination, coprecipitation and microemulsion), characterized by N2 adsorption, XRD, H2-TPR, Raman spectroscopy and XPS, and tested for soot combustion in NOx/O2. The catalyst prepared by microemulsion method is the most active one, which is related to its high surface area (147 m2/g) and low crystallite size (6 nm), and the lowest activity was obtained with the catalyst prepared by coprecipitation (74 m2/g; 9 nm). The catalyst prepared by nitrates precursors calcination is slightly less active to that prepared by microemulsion, but the synthesis procedure is very straightforward and surfactants or other chemicals are not required, being very convenient for scaling up and practical utilization. The high activity of the catalyst prepared by nitrates calcination can be attributed to the better introduction of Nd cations into the parent ceria framework than on catalysts prepared by coprecipitation and microemulsion, which promotes the creation of more oxygen vacancies.The authors thank the Spanish Catalyst Society-SECAT for the grant of J.G.M. and both the Spanish Ministry of Economy and Competitiveness and the FEDER funding of UE for the financial support to the Project CTQ2012-30703

Evaluación del estado dentario y gingival de estudiantes de la Universidad Nacional de Córdoba y su correlación con el grado de conocimiento en salud bucal

El propósito de este trabajo de investigación es conocer la situación de los estudiantes universitarios pertenecientes a la Universidad Nacional de Córdoba, con respecto a su salud bucal y determinar si aquellos que cursan carreras de las ciencias de la salud poseen más conciencia y autocuidado con respecto a su propia salud. Para ello, se profundiza a través de la búsqueda bibliográfica sobre la problemática a nivel mundial de las enfermedades bucodentales de mayor prevalencia, caries y enfermedad periodontal, y sus consecuencias, físicas, psicológicas y sociales tanto individuales como poblacionales. Se plantea la preocupación de los Estados que ven a estas dolencias como un problema de salud pública a nivel mundial, describiendo así metas y objetivos para disminuir la incidencia de estas patologías y mejorar el estado de salud bucal de la población. Se aborda también la problemática de los estudiantes universitarios, sujetos de estudio en este trabajo, desde el punto de vista de la motivación en salud, sobretodo de aquellos alumnos de las carreras del área de salud particularmente los de Odontología. Luego de la contextualización teórica se plantean los objetivos generales y específicos propuestos y los materiales y métodos utilizados para alcanzarlos. Más adelante se presentan los resultados obtenidos y en base a ellos se realiza un análisis de los mismos y de lo encontrado en la bibliografía consultada a nivel mundial sobre trabajos relacionados reportados por otros investigadores para finalmente arribar a la conclusión final sobre todo lo expuest

Preparation of RhOx/CeyPr1−yO2 N2O decomposition catalysts by rhodium nitrate impregnation with different solvents

The effect of the solvent (water, ethanol or acetone) used to impregnate CeyPr1−yO2 (y = 1, 0.9 or 0.5) supports with rhodium nitrate, in order to prepare N2O decomposition catalysts, has been studied. RhOx/CeyPr1−yO2 catalysts were prepared and characterized by N2 adsorption at −196 °C, XRD, Raman spectroscopy, TEM, XPS and H2-TPR. The activity for N2O decomposition of the catalysts studied was related with the RhOx-support interaction, and both the nature of the ceria support and of the solvent used for rhodium impregnation affected such interaction. Ceria doping with 10% praseodymium had a positive effect in the RhOx-support interaction, but the benefit on the catalytic activity was only obtained for water impregnation because the temperature peaks created during calcination of ethanol and acetone-impregnated catalysts promoted Ce0.9Pr0.1O2 and RhOx sintering. The interaction between RhOx and Ce0.5Pr0.5O2 was not as good as that with Ce0.9Pr0.1O2. The best catalyst was obtained by impregnating Ce0.9Pr0.1O2 with a water solution of rhodium. However, if acetone or ethanol must be used for any reason the pure ceria support is more suitable (under the calcination conditions of this study; 250 to 500 °C at 10 °C/min) because do not sinters during solvents combustion.Financial support of Generalitat Valenciana (Project Prometeo 2009/047), The Spanish Ministry of Economy and Competitiveness (Project CTQ2012-30703), and the UE FEDER funding

The influence of promoters (Zr, La, Tb, Pr) on the catalytic performance of CuO-CeO2 systems for the preferential oxidation of CO in the presence of CO2 and H2O

CuO supported on CeO2 and Ce0.9X0.1O2, where X is Zr, La, Tb or Pr, were synthesized using nitrate precursors, giving rise ceria based materials with a small particle size which interact with CuO species generating a high amount of interfacial sites. The incorporation of cations to the ceria framework modifies the CeO2 lattice parameter, improving the redox behavior of the catalytic system. The catalysts were characterized by X-ray fluorescence spectrometry (XRFS), X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), Raman spectroscopy, thermoprogrammed reduction with H2 (H2-TPR) and X-ray photoelectron spectroscopy (XPS). The catalysts were tested in the preferential oxidation of CO under a H2-rich stream (CO-PROX), reaching conversion values higher than 95% between 115 and 140 °C and being the catalyst with 6 wt.% of Cu supported on Ce0.9Zr0.1O2 (sample 6CUZRCE) the most active catalyst. The influence of the presence of CO2 and H2O was also studied simulating a PROX unit, taking place a decrease of the catalytic activity due to the inhibitor effect both CO2 and H2O.The projects CTQ2012-37925-C03-03 and CTQ2012-30703 of Ministerio de Economía y Competitividad (Spain), the project of Excellence P12 RNM 1565 (Junta de Andalucía, Spain), the project of Excellence PROMETEUII/2014/010 (Generalitat Valenciana) and the UE (FEDER funding) are acknowledged for the financial support

Operaciones simuladas: EFOS y EDOS (Artículo 69–B del Código Fiscal de la Federación)

La presente ponencia tuvo como objetivo describir el artículo 69 – B del CFF, como medida de contrarrestar esquemas de prácticas fiscales indebidas a través de operaciones simuladas que utilizan las empresas EFOS y EDOS. Se utilizó estadística descriptiva y se presenta los resultados recolectados en una tabla y en una gráfica de pastel en porcentaje. La población fueron las empresas que se encuentran en la lista de contribuyentes del SAT, de acuerdo con la reforma donde se adiciona y se aprueba el artículo 69–B del Código Fiscal de la Federación, con un total de 12505 empresas presuntas de operaciones simuladas, de los cuales 10519 son empresas definitivas que representan un 42%, es decir, que no lograron desvirtuar los hechos, así mismo, 903 empresas tienen sentencia favorable que representan un 4%, es decir, que interpusieron un medio de defensa, del mismo modo, 783 empresas están como presuntos, lo que representa un 3%, por lo que tendrán desvirtuar los hechos y por último, 301 empresas desvirtuados, que representan el 1%, ya que manifestaron ante la autoridad fiscal la suficiente información y documentación para desvirtuar los hechos.Los resultados obtenidos entre los años 2014 y 2018 por el uso indebido de comprobantes fiscales digitales por internet, derivado de operaciones inexistentes en México, se identificaron a 8204 empresas factureras, las cuales generaron 8 millones de facturas apócrifas, lo cual genero significativamente un monto de  $ 354 mil 512 millones de pesos de evasión fiscal y que impactan en la recaudación fiscal y a su vez tiene consecuencias significativas del 1.4% en el PIB. Sin embargo, en los resultados obtenidos con base al análisis de datos históricos, se concluyó que la lista de contribuyentes del SAT se ha incrementado, es decir, la problemática continua, ya que de los años 2014 a 2018 fueron de 8204 a 12505 empresas al 18 de mayo del 2021.&nbsp