Effects of coronal substrates and water storage on the microhardness of a resin cement used for luting ceramic crowns

Composite resin and metallic posts are the materials most employed for reconstruction of teeth presenting partial or total destruction of crowns. Resin-based cements have been widely used for cementation of ceramic crowns. The success of cementation depends on the achievement of adequate cement curing. Objectives: To evaluate the microhardness of Variolink® II (Ivoclar Vivadent, Schaan, Liechtenstein), used for cementing ceramic crowns onto three different coronal substrate preparations (dentin, metal, and composite resin), after 7 days and 3 months of water storage. The evaluation was performed along the cement line in the cervical, medium and occlusal thirds on the buccal and lingual aspects, and on the occlusal surface. Material and Methods: Thirty molars were distributed in three groups (N=10) according to the type of coronal substrate: Group D- the prepared surfaces were kept in dentin; Groups M (metal) and R (resin)- the crowns were sectioned at the level of the cementoenamel junction and restored with metallic cast posts or resin build-up cores, respectively. The crowns were fabricated in ceramic IPS e.max® Press (Ivoclar Vivadent, Schaan, Liechtenstein) and luted with Variolink II. After 7 days of water storage, 5 specimens of each group were sectioned in buccolingual direction for microhardness measurements. The other specimens (N=5) were kept stored in deionized water at 37ºC for three months, followed by sectioning and microhardness measurements. Results: Data were first analyzed by three-way ANOVA that did not reveal significant differences between thirds and occlusal surface (p=0.231). Two-way ANOVA showed significant effect of substrates (

Correlation between margin fit and microleakage in complete crowns cemented with three luting agents

Microleakage can be related to margin misfit. Also, traditional microleakage techniques are time-consuming. This study evaluated the existence of correlation between in vitro margin fit and a new microleakage technique for complete crowns cemented with 3 different luting agents. Thirty human premolars were prepared for full-coverage crowns with a convergence angle of 6 degrees, chamfer margin of 1.2 mm circumferentially, and occlusal reduction of 1.5 mm. Ni-Cr cast crowns were cemented with either zinc phosphate (ZP) (S.S. White), resin-modified glass-ionomer (RMGI) (Rely X Luting Cement) or a resin-based luting agent (RC) (Enforce). Margin fit (seating discrepancy and margin gap) was evaluated according to criteria in the literature under microscope with 0.001 mm accuracy. After thermal cycling, crowns were longitudinally sectioned and microleakage scores at tooth-cement interface were obtained and recorded at ×100 magnification. Margin fit parameters were compared with the one-way ANOVA test and microleakage scores with Kruskal-Wallis and Dunn's tests (alpha=0.05). Correlation between margin fit and microleakage was analyzed with the Spearman's test (alpha=0.05). Seating discrepancy and marginal gap values ranged from 81.82 µm to 137.22 µm (p=0.117), and from 75.42 µm to 78.49 µm (p=0.940), respectively. Marginal microleakage scores were ZP=3.02, RMGI=0.35 and RC=0.12 (p;0.05). Conclusion: Margin fit parameters and microleakage showed no strong correlations; cast crowns cemented with RMGI and RC had lower microleakage scores than ZP cement

Master Prato: Jogo em Realidade Aumentada para Auxílio no Desenvolvimento de Hábitos Alimentares Saudáveis em Crianças

Os maus hábitos alimentares desde a infância é um dos fatores que acarretama obesidade e por consequência o desenvolvimento de doenças ligadas a esta. Assim, este artigo apresenta o Master Prato, um jogo que utiliza a realidade aumentada (RA) para auxiliar o aprendizado de crianças na combinação de refeições saudáveis. No jogo podem-se criar pratos com vários alimentos à disposição e desta forma, receber uma pontuação sobre o quão saudável foi a refeição criada. O jogo é personalizável, e para cada jogador são feitos cálculos para identificar a necessidade de consumo de nutrientes para cada um montar o seu prato. Foi feita uma avaliação por nutricionistas com o foco no envolvimento, funcionalidades, estética e as informações presentes. Com os resultados obtidos constatou-se que o jogo se mostrou relevante para ser aplicado na educação

Effect of an additional hydrophilic versus hydrophobic coat on the quality of dentinal sealing provided by two-step etchand-rinse adhesives

OBJECTIVE: To test the hypothesis that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the addition of an extra layer of the respective adhesive or the application of a more hydrophobic, non-solvated resin. MATERIAL AND METHODS: full-crown preparations were acid-etched with phosphoric acid for 15 s and bonded with Adper Single Bond (3M ESPE), Excite DSC (Ivoclar/Vivadent) or Prime & Bond NT (Dentsply). The adhesives were used according to the manufacturers' instructions (control groups) or after application to dentin they were a) covered with an extra coat of each respective system or b) coated with a non-solvated bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE). Fluid flow rate was measured before and after dentin surfaces were acid-etched and bonded with adhesives. RESULTS: None of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin. Application of an extra coat of the adhesive did not reduce the fluid flow rate of adhesive-bonded dentin (p>0.05). Conversely, the application of a more hydrophobic non-solvated resin resulted in significant reductions in the fluid flow rate (p<0.05) for all tested adhesives. CONCLUSIONS: The quality of the dentinal sealing provided by etch-and-rinse adhesives can be significantly improved by the application of a more hydrophobic, non-solvated bonding agent

Efeito da solução desinfetante de iodo a 2% sobre a adesão à dentina

INTRODUCTION: Disinfection of dentin surfaces is desirable so long as it does not interfere with subsequent bonding of adhesive resins. OBJECTIVE: To test the null hypothesis that bond strengths to dentin are not affected by previous application of an iodine disinfecting solution. MATERIALS AND METHODS: Twenty-four extracted non-carious molars were selected. Occlusal enamel was removed producing a flat dentin substrate. Test teeth were all treated with 2% Iodine disclosing/disinfecting solution (I2DDS) for 20 sec and rinsed for 20 sec followed by the application of self- or total- etching bonding systems, generating five adhesive groups (n=3): Single Bond; ; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. The control groups (n=3 per adhesive) had no disclosing/disinfectant application prior to adhesive application. A 4-mm thick resin restoration was built up on each tooth for microtensile testing. Statistical analyses between experimental and control groups were performed by student's t-test (alpha= 0.05). RESULTS: In general, experimental groups (previously treated with I2DDS) showed significantly lower bond strength values when compared with their respective controls (p;0.05). CONCLUSION: Acetone-base adhesive systems seem not to be affected by the application of I2DDS prior to etching and bonding procedures.INTRODUÇÃO: A desinfecção das superfícies de dentina é desejada desde que não haja interferência na adesão dos agentes adesivos. OBJETIVO: Testar a hipótese nula de que a resistência adesiva não é afetada pela aplicação prévia de uma solução desinfetante de iodo. MATERIAL AND MÉTODO: Vinte e quatro molares hígidos foram selecionados. O esmalte oclusal destes dentes foi removido, e sobre as superfícies planas de dentina expostas foi aplicada da solução desinfetante de Iodo a 2% (I2DDS), que permaneceu sobre a superfície por 20 s e foi lavada por 20 s com água deionizada. Sobre as superfícies desinfetadas foram aplicados um dos seguintes sistemas adesivos (n=3): Single Bond; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. Os grupos controle (n=3) não tiveram a supeficie de dentina tratada com I2DDS antes dos precedimentos adesivos. Em todos os grupos, após hibridização da dentina, foi construída uma "restauração" de resina composta com cerca de 4 mm de espessura. Após 7 dias de armazenagem em água destilada, os dentes foram secionados de modo a originarem espécimes a serem submetidos ao teste de microtração (palitos). Análise estatística para comparação dos dados foi realizada pelo teste t de student (alfa=0,05). RESULTADOS: De forma geral, os grupos experimentais (tratados com I2DDS) apresentraram resistência adesiva significativamente menor do que os respectivos grupos controle (p;0.05). Assim, a hipótese nula deve ser rejeitada para os adesivos a base de etanol e/ou a base de água, mas aceita para o adesivo a base de acetona. CONCLUSÃO: O uso da solução experimental de iodo previamente à realização dos procedimentos adesivos afetou a efetividade da união à dentina apenas quando do emprego de sistemas adesivos a base de etanol e/ou água

Influence of carbamide peroxide-based bleaching agents on the bond strength of resin-enamel/dentin interfaces

In this bond strength study, a bleaching agent containing 10% carbamide peroxide was applied over composite-teeth bonded interfaces of two adhesive systems applied to enamel and dentin. Sixteen human third molars were used for bonding procedures. Single Bond (SB) and Clearfil SE Bond (CB) were applied to enamel and dentin according to the manufacturers' instructions. A resin composite cube-like structure was incrementally built on the bonded surfaces. The restored teeth were sectioned into 0.7 mm thick slices that were trimmed at enamel or dentin bonded interfaces to an hourglass shape with a cross-sectional area of approximately 0.5 mm². Specimens were assigned to 8 groups (n = 10) according to the following factors under study: dental substrate (enamel and dentin); adhesive system (SB and CB) and treatment (10% carbamide peroxide and not bleached/control). The bleaching gel (Opalescence) was applied at the bonded interfaces for 6 hours during 14 days and after daily treatment specimens were stored in artificial saliva. Unbleached specimens were stored in artificial saliva for 14 days. Specimens were tested for tension and the data were analyzed by three-way ANOVA and Tukey's test (p < 0.05). Enamel tensile bond strength of CB was reduced after carbamide peroxide application. The bleaching treatment did not alter dentin bond strength of both adhesives. The results suggest that bleaching significantly affects bond strength of CB to enamel, but no influence on bond strength to dentin was noted for both adhesive systems

Effects of coronal substrates and water storage on the microhardness of a resin cement used for luting ceramic crowns

Composite resin and metallic posts are the materials most employed for reconstruction of teeth presenting partial or total destruction of crowns. Resin-based cements have been widely used for cementation of ceramic crowns. The success of cementation depends on the achievement of adequate cement curing. Objectives: To evaluate the microhardness of Variolink&#174; II (Ivoclar Vivadent, Schaan, Liechtenstein), used for cementing ceramic crowns onto three different coronal substrate preparations (dentin, metal, and composite resin), after 7 days and 3 months of water storage. The evaluation was performed along the cement line in the cervical, medium and occlusal thirds on the buccal and lingual aspects, and on the occlusal surface. Material and Methods: Thirty molars were distributed in three groups (N=10) according to the type of coronal substrate: Group D- the prepared surfaces were kept in dentin; Groups M (metal) and R (resin)- the crowns were sectioned at the level of the cementoenamel junction and restored with metallic cast posts or resin build-up cores, respectively. The crowns were fabricated in ceramic IPS e.max&#174; Press (Ivoclar Vivadent, Schaan, Liechtenstein) and luted with Variolink II. After 7 days of water storage, 5 specimens of each group were sectioned in buccolingual direction for microhardness measurements. The other specimens (N=5) were kept stored in deionized water at 37&#186;C for three months, followed by sectioning and microhardness measurements. Results: Data were first analyzed by three-way ANOVA that did not reveal significant differences between thirds and occlusal surface (p=0.231). Two-way ANOVA showed significant effect of substrates (p<0.001) and the Tukey test revealed that microhardness was significantly lower when crowns were cemented on resin cores and tested after 7 days of water storage (p=0.007). Conclusion: The type of material employed for coronal reconstruction of preparations for prosthetic purposes may influence the cement properties