39 research outputs found
Surface Roughness of Commercial Composites after Different Polishing Protocols: An Analysis with Atomic Force Microscopy
Polishing may increase the surface roughness of composites, with a possible effect on bacterial growth and material properties. This preliminary in vitro study evaluates the effect of three different polishing systems (PoGo polishers, Enhance, Venus Supra) on six direct resin composites (Gradia Direct, Venus, Venus Diamond, Enamel Plus HFO, Tetric Evoceram, Filtek Supreme XT)
Effect of surface roughness of biomaterials on Staphylococcus epidermidis adhesion
Background: Implant-related infections are caused by adhesion of bacteria to the surface of biomaterials. In this in vitro research, we evaluated the ability of Staphylococcus epidermidis (ATCC35984) to adhere to the surface of solid biomaterials at different levels of roughness below 30 nm Ra and investigated the minimum level of roughness required to promote bacterial adhesion on five kinds of biomaterials: oxidized zirconium-niobium alloy (Oxinium), cobalt-chromium-molybdenum alloy (Co-Cr-Mo), titanium alloy (Ti-6Al-4 V), commercially pure titanium (Cp-Ti) and stainless steel (SUS316L), samples of which were categorized into a fine group and a coarse group according to surface roughness. The test specimens were physically analyzed and the viable bacterial density of the adhered bacteria was quantitatively determined (n = 20).Results: The amount of bacteria that adhered to the biomaterials in the coarse group was higher than those in the fine group. Oxinium, Ti-6Al-4 V and SUS316L in particular demonstrated statistically significant differences between the two groups (P < 0.05). Of the materials, the Co-Cr-Mo specimens exhibited significantly lower amounts of adhered bacteria than the Ti-6Al-4 V, Cp-Ti and SUS316L specimens in the fine group. Similarly, the Co-Cr-Mo specimens in the coarse group exhibited significantly lower values than the other four materials.Conclusions: These results suggest that minimum level of roughness affecting initial bacterial adherence activity differs according to the type of biomaterial used, and that even a surface roughness of below 30 nm Ra in Oxinium, Ti-6Al-4 V and SUS316L can promote bacterial adhesion. Relative hydrophobic Co-Cr-Mo surfaces were less susceptible to bacterial adherence
Early Staphylococcal Biofilm Formation on Solid Orthopaedic Implant Materials: In Vitro Study
Biofilms forming on the surface of biomaterials can cause intractable implant-related infections. Bacterial adherence and early biofilm formation are influenced by the type of biomaterial used and the physical characteristics of implant surface. In this in vitro research, we evaluated the ability of Staphylococcus epidermidis, the main pathogen in implant-related infections, to form biofilms on the surface of the solid orthopaedic biomaterials, oxidized zirconium-niobium alloy, cobalt-chromium-molybdenum alloy (Co-Cr-Mo), titanium alloy (Ti-6Al-4V), commercially pure titanium (cp-Ti) and stainless steel. A bacterial suspension of Staphylococcus epidermidis strain RP62A (ATCC35984) was added to the surface of specimens and incubated. The stained biofilms were imaged with a digital optical microscope and the biofilm coverage rate (BCR) was calculated. The total amount of biofilm was determined with the crystal violet assay and the number of viable cells in the biofilm was counted using the plate count method. The BCR of all the biomaterials rose in proportion to culture duration. After culturing for 2-4 hours, the BCR was similar for all materials. However, after culturing for 6 hours, the BCR for Co-Cr-Mo alloy was significantly lower than for Ti-6Al-4V, cp-Ti and stainless steel (P0.05). These results suggest that surface properties, such as hydrophobicity or the low surface free energy of Co-Cr-Mo, may have some influence in inhibiting or delaying the two-dimensional expansion of biofilm on surfaces with a similar degree of smoothness