Análise comparativa do desgaste de materiais odontológicos através de Tribômetro Callowear – ensaio “in vitro”

The aim of present study was to evaluate the wear coeficient of different dental materials submited to ballcrattering test. Different restorative materials were compared to bovine enamel. The samples were made with nylon matrix stripes and had 7mm diameter and 2mm thickness. The samples were submitted to the ballcratering test in a Calowear tribometer (CSEM Instruments Advanced Mechanical Surface Testing) and maded six measures in each sample with different revolutions of the ball: 10, 20, 30, 40, 50 and 60 revolutions. After the crattering generation the samples were avaliated to a Zeiss Axiotech Vario Microscope with SVGA Cam and all cratters photographed. After, the photos were evaluated at UTHSCSA ImageTool for Windows 3.0 and the meaning of measured radius were inserted at SigmaPlot, that gave the wear coefficients by linear regression. To bovine enamel the coefficient was 3,83 X 10-14 m²/N, to microhybrid resin was 3,6542 x 10-14 m²/N, 2,06 x 10-12 m²/N to amalgam and 2,18 x 10-12 m²/N to acrylic resin. In conclusion, bovine teeth presented higher wear resistance and lower wear coefficient than composite resin, amalgam and acrylic resin.O objetivo do presente estudo foi avaliar o coeficiente de resistência ao desgaste de diferentes materiais odontológicos submetidos ao ensaio de micro-abrasão através da metodologia de ball-crattering. Para isso foram avaliados diferentes materiais restauradores em comparação com o esmalte bovino. As amostras foram confeccionadas através de matrizes de nylon bipartida, com 7mm de diâmetro e 2mm de espessura em negativo e após, a resistência ao desgaste foi avaliada em um ensaio de micro abrasão (Ball cratering test) realizado em tribômetro modelo Calowear (CSEM Instruments Advanced Mechanical Surface Testing). Em cada corpo de prova foram feitas seis medições com variação no número de voltas realizadas pela esfera: 10, 20, 30, 40, 50 e 60 voltas. Após a realização das crateras o corpo de prova foi levado a um Zeiss Axiotech Vario Microscope com câmera SVGA acoplada onde foram fotografadas todas as crateras geradas e após, foram analisadas em UTHSCSA ImageTool for Windows versão 3.0, os valores de raio médio das marcas foram, então levados ao SigmaPlot versão 8.0 que através da correlação dos dados determinou o coeficiente de desgaste através de uma regressão linear. Para os corpos de esmalte bovino foi encontrado o coeficiente de desgaste de 3,83 X 10-14 m²/N, para resina composta micro híbrida 3,6542 x 10-14 m²/N, para amálgama de prata 2,06 x 10-12 m²/N e para resina acrílica autopolimerizável foi de 2,18 x 10-12 m²/N. Após a execução dos ensaios chega-se a conclusão que o esmalte bovino apresentou maior resistência e menor coeficiente de desgaste, seguido por resina composta, amálgama de prata e resina acrílica autopolimerizável

An innovative series of layered nanostructured aminoalkylsilica hybrid material

Uma nova série de amostras de material híbrido à base de sílica, contendo o grupo catiônico amoniopropil ligado na forma pendente, foi obtida usando-se o método sol-gel de síntese, variando-se a razão molar entre o precursor inorgânico e o precursor orgânico. A análise termogravimétrica mostrou que as amostras são termicamente estáveis até 260 °C. Os resultados obtidos por difratometria de raios X, microscopia eletrônica de transmissão, ressonância magnética nuclear de 29Si e análise elementar são compatíveis com o modelo estrutural de camadas de silsesquioxano com distâncias basais de até 5,4 nm, contendo sílica amorfa no espaço entre as camadas.An innovative series of silica-based hybrid materials containing pendant cationic ammoniumpropyl groups was obtained using the sol-gel method, by varying the molar ratio of the inorganic and organic precursors. Thermogravimetric analysis showed that samples were thermally stable up to 260 °C. Results obtained by X-ray diffractometry, transmission electron microscopy, 29Si nuclear magnetic resonance and elemental analysis were compatible with a silsesquioxane layered structural model showing basal distances up to 5.4 nm, containing amorphous silica in the interlayer space

An innovative series of layered nanostructured aminoalkylsilica hybrid material

Uma nova série de amostras de material híbrido à base de sílica, contendo o grupo catiônico amoniopropil ligado na forma pendente, foi obtida usando-se o método sol-gel de síntese, variando-se a razão molar entre o precursor inorgânico e o precursor orgânico. A análise termogravimétrica mostrou que as amostras são termicamente estáveis até 260 °C. Os resultados obtidos por difratometria de raios X, microscopia eletrônica de transmissão, ressonância magnética nuclear de 29Si e análise elementar são compatíveis com o modelo estrutural de camadas de silsesquioxano com distâncias basais de até 5,4 nm, contendo sílica amorfa no espaço entre as camadas.An innovative series of silica-based hybrid materials containing pendant cationic ammoniumpropyl groups was obtained using the sol-gel method, by varying the molar ratio of the inorganic and organic precursors. Thermogravimetric analysis showed that samples were thermally stable up to 260 °C. Results obtained by X-ray diffractometry, transmission electron microscopy, 29Si nuclear magnetic resonance and elemental analysis were compatible with a silsesquioxane layered structural model showing basal distances up to 5.4 nm, containing amorphous silica in the interlayer space

Estudo experimental do supercondutor MgB/sub 2/

04