Low Thermal Expansion Glass Ceramics by sintering and concurrent crystallization of Li2O.Al2O3.XSiO2 glass particles

Tesis doctoral inédita leída en la Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química Inorgánica. Fecha de lectura: 05-02-201

Synthesis and characterization of thermoluminescent glass-ceramics Li2O–Al2O3–SiO2:CeO2

ABSTRACT: Vitroceramic powders of Li2O–Al2O3–SiO2 systems (LAS), doped with 1% (LAS:1Ce) and 10% (LAS:10Ce) molar of cerianite (CeO2) were synthesized by means of the gelification technique of metal formates of aluminum and lithium, in the presence of tetraethoxy silane and CeO2. The gels obtained were dried (120 °C, 2.5 h), calcined (480 °C, 5 h) and sinterized (1250 °C, 30 min). The sinterized samples were characterized by X-ray difraction (XRD), scanning electron microscopy (SEM) and microchemical analysis (EDS). There is evidence for a mixture of two phases of 64% β-spodumene (Li2O–Al2O3–4SiO2) and 36% β-eucryptite (Li2O–Al2O3–2SiO2). The LAS:1Ce system was enriched in aluminum, the LAS:10Ce system showed areas of heterogeneous composition; some regions with a shortage of CeO2, while others zones with cerium cumulus. From the microscopy images it was found that CeO2 acts as a densificant agent in LAS system, favoring the sintering in the host. The chemical route and the sintering processes utilized allow the production of samples exhibiting an acceptable linear correlation between total thermoluminescent emission intensity and the irradiation dose when the CeO2 concentration is low (less than 1%), opening the possibility of using this kind of glass-ceramic in dosimetry

Investigaciones Teológicas-Eclesiales I

La labor del teólogo, como investigador, es la de aportar a la comprensión de situaciones que presentan confusión. La Teología, en diálogo constante con las demás ciencias humanas, puede brindar luces en momentos de ofuscación y desesperanza. Reflexiones teológicas-eclesiales / hace aportes en temas como la Familia; la Excomunión; el Amor y la Sabiduría; el Matrimonio; la Palabra de Dios; la Mujer; el Mundo Laical; la Fe y la Política; y, la Constitución Lumen Gentium. Sus autores, desde el abordaje académico y científico, presentan un texto de fácil comprensión para lectores con una educación mínimamente formal en torno a estudios de historia y religión. A la vez, ofrece horizontes de profundización a los investigadores del fenómeno histórico y cultural de la religión, dando continuidad a la serie de publicaciones sobre Investigaciones teológicas eclesiales

In situ formation of zirconia in the bone substitute synthesis based on aluminazircon matriz infiltrated with hydroxyapatite

El desarrollo de materiales capaces de satisfacer los requerimientos de un sustituto óseo, es un gran desafío científico y tecnológico desde el punto de vista de la biocompatibilidad así como del control de la microestructura porosa que promueva la oseointegracion y aumente el desempeño mecánico de los implantes. En este trabajo, se presenta la preparación de materiales porosos mediante el uso repetido de la técnica de infiltración con suspensiones cerámicas. Los materiales obtenidos fueron caracterizados por difracción de rayos X (XRD), microscopía electrónica de barrido (SEM), medidas de absorción de agua y ensayos de resistencia a la compresión. Se encontró que la infiltración de una espuma comercial de poliuretano con suspensiones mixtas de circón y alúmina permite la formación insitu de circonia dentro de una matriz con porosidad similar a la presente en la espuma de partida. La matriz infiltrada con hidroxiapatita presentó poros con diámetro de alrededor de 300 mm y una resistencia promedio a la compresión de 5,44 ± 0,94 MPa, características que son típicas de un buen sustituto óseo. / Abstract: The development of materials capable to satisfy the requirements of a bone substitute is a great scientific and technological challenge from the point of view of biocompatibility as much as the porous microstructure control that promotes osteointegration and improves the implant mechanical performance. In this work, the preparation of macroporous materials through the repeated use of the infiltration technique with ceramic suspensions is presented. The obtained materials were characterized by X ray diffraction (XRD), scanning electron microscopy (SEM), water absorption measurements and compressive strength tests. It was found that commercial polyurethane foam infiltration with mixed alumina and zircon suspensions allows the Insitu transformation of zirconia into a matrix with similar porosity to the original foam. The matrix infiltrated with hydroxyapatite showed pore diameters of 300 mm and an average compressive strength of 5, 44 ± 0, 94 MPa, both characteristics are typical of a well bone substitute

SÍNTESIS Y CARACTERIZACIÓN DE -ALÚMINA NANOMETRICA

Partículas nanométricas de alúmina fueron sintetizadas mediante rutas de química coloidal, partiendo de hidróxido de aluminio, ácido fórmico y etanol como solvente. Se evaluó el efecto del medio de reacción, el tiempo de maduración, el modificador superficial y la presencia de semillas de á-Al2O3. Se determinó que la combinación de un pH de 2,40 ± 1, y la presencia de semillas de á-Al2O3 asistidas con modificadores superficiales permiten obtener partículas nanométricas más pequeñas, las cuales se aglomeran en forma de xerogel después del tratamiento térmico de sinterización. Según la microscopia electrónica de transmisión TEM, la alúmina sintetizada presentó tamaños de partícula del orden de 7,5 nm a 200 nm, y se generaron tamaños secundarios de 2 mm como resultado de la sinterización a 1200 ºC, según se observó en la microscopia electrónica de barrido SEM. Siguiendo las transformaciones estructurales del material sintetizado con la temperatura, mediante espectroscopía infrarroja y difracción de rayos X se determinó la presencia de á-alúmina a partir de los 1000°C, verificándose que es una ruta de síntesis tipo bohemita, la cual es útil para obtener á-alúmina nanométrica. El potencial uso del material sinterizado fue valorado mediante propiedades mecánicas, para lo cual se encontró en la alúmina nanométrica sinterizada una resistencia a la flexión 2,6 veces superior que la proporcionó una muestra de alúmina micrométrica de aplicación en cerámica dental