Effect of cooling protocol on mechanical properties and microstructure of dental veneering ceramics

Objectives: Understand how cooling protocols control the microstructure and mechanical properties of veneering porcelains. Methods: Two porcelain powders were selected, one used to veneer metallic frameworks (VM13) and one for zirconia frameworks (VM9). After the last firing cycle, the monolithic specimens were subjected to two cooling protocols: slow and fast. Flexural strength (FS) was evaluated by three-point beam bending and fracture toughness (KIC) was evaluated by the single-edge V-notch beam (SEVNB) method. Scanning electron microscopy (SEM) was performed to determine the leucite crystal volume fraction (%), particle size, and matrix microcrack density. The results were compared by analysis of variances (ANOVA) and Tukey's multiple comparison test. Results: The mechanical properties were significantly (p < 0.05) higher for the VM13 porcelain (FS = 111.0 MPa, KIC = 1.01 MPa.√m) compared to VM9 (FS = 79.6 MPa, KIC =0.87 MPa.√m) regardless of cooling protocol due to ∼250% higher volume fraction of leucite crystals. The slow cooled VM13 and fast cooled VM9 resulted in the highest and lowest mechanical properties, respectively, while the VM9 slow cooled properties were similar to the VM13 fast cooled. The SEM revealed that the slow cooling significantly increased the volume fraction of leucite crystals by 33–41 %. Across both porcelains, a significant linear correlation between both mechanical properties (strength and toughness) and leucite crystal content was found. Slow cooling was also associated with increased crystal growth resulting in more matrix microcracking. Significance: Controlled crystallization using slow cooling can be applied as a means of strengthening dental porcelains. However, the benefits of slow cooling may be partially offset by increasing the microcrack density in the glass matrix. To achieve the maximum benefit of slow cooling, it is recommending to develop heat treatments to produce porcelain with fine-grained and homogenously dispersed leucite crystals to achieve minimal glass matrix microcracking