Bond strength of a pit-and-fissure sealant associated to etch-and-rinse and self-etching adhesive systems to saliva-contaminated enamel: individual vs. simultaneous light curing

This study evaluated in vitro the shear bond strength (SBS) of a resin-based pit-and-fissure sealant [Fluroshield (F), Dentsply/Caulk] associated with either an etch-and-rinse [Adper Single Bond 2 (SB), 3M/ESPE] or a self-etching adhesive system [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] to saliva-contaminated enamel, comparing two curing protocols: individual light curing of the adhesive system and the sealant or simultaneous curing of both materials. Mesial and distal enamel surfaces from 45 sound third molars were randomly assigned to 6 groups (n=15), according to the bonding technique: I - F was applied to 37% phosphoric acid etched enamel. The other groups were contaminated with fresh human saliva (0.01 mL; 10 s) after acid etching: II - SB and F were light cured separately; III - SB and F were light cured together; IV - S3 and F were light cured separately; V - S3 and F were light cured simultaneously; VI - F was applied to saliva-contaminated, acid-etched enamel without an intermediate bonding agent layer. SBS was tested to failure in a universal testing machine at 0.5 mm/min. Data were analyzed by one-way ANOVA and Fisher's test (α=0.05).The debonded specimens were examined with a stereomicroscope to assess the failure modes. Three representative specimens from each group were observed under scanning electron microscopy for a qualitative analysis. Mean SBS in MPa were: I-12.28 (±4.29); II-8.57 (±3.19); III-7.97 (±2.16); IV-12.56 (±3.11); V-11.45 (±3.77); and VI-7.47 (±1.99). In conclusion, individual or simultaneous curing of the intermediate bonding agent layer and the resin sealant did not seem to affect bond strength to saliva-contaminated enamel. S3/F presented significantly higher SBS than the that of the groups treated with SB etch-and-rinse adhesive system and similar SBS to that of the control group, in which the sealant was applied under ideal dry, noncontaminated conditions.Este estudo avaliou in vitro a resistência ao cisalhamento (RC) de um selante resinoso [Fluroshield (F), Dentsply/Caulk] em associação com um sistema adesivo de condicionamento total [Adper Single Bond 2 (SB), 3M/ESPE] ou auto-condicionante [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] após contaminação salivar do esmalte, comparando dois protocolos: fotopolimerização individual do sistema adesivo e do selante ou simultânea de ambos os materiais. Superfícies mesiais e distais de esmalte de 45 terceiros molares hígidos foram aleatoriamente alocadas em 6 grupos (n=15), de acordo com a técnica adesiva empregada: I - F foi aplicado sobre o esmalte condicionado com ácido fosfórico a 37%. Os demais grupos foram contaminados com saliva (0,01 mL por 10 s) após o condicionamento ácido. II - SB e F foram fotopolimerizados separadamente; III - SB e F foram fotopolimerizados simultaneamente; IV - S3 e F foram fotopolimerizados separadamente; V - S3 e F foram fotopolimerizados simultaneamente; VI - F foi aplicado sobre o esmalte condicionado e contaminado sem sistema adesivo. RC foi testada em uma máquina universal de ensaios (0,5 mm/min; 50 kgf) e os dados analisados por ANOVA a 1 fator e teste exato de Fisher (α=0,05). As interfaces adesivas foram analisadas quanto ao padrão de fraturas em estereomicroscópio. Três espécimes de cada grupo foram analisados qualitativamente em microscópio eletrônico de varredura. As médias de RC em MPa foram: I-12,28 (±4,29); II-8,57 (±3,19); III-7,97 (±2,16); IV-12,56 (±3,11); V-11,45 (±3,77); e VI-7,47 (±1,99). Conclui-se que a fotopolimerização individual ou simultânea do sistema adesivo e do selante não afetou os valores de RC ao esmalte contaminado. S3/F apresentou RC estatisticamente maior do que os grupos tratados com o sistema adesivo etch-and-rinse SB e estatisticamente semelhante ao grupo controle, no qual o selante foi aplicado em condições ideais, na ausência de contaminação salivar

Bonding agent underneath sealant: shear bond strength to oil-contaminated

This study evaluated in vitro the shear bond strength of a resin-based pit-and-fissure sealant (Fluroshield - F) associated with either an ethanol-based (Adper Single Bond 2 - SB) or an acetone-based (Prime & Bond - PB) adhesive system under conditions of oil contamination. Mesial and distal enamel surfaces from 30 sound third molars were randomly assigned to 2 groups (n=30): I - no oil contamination; II - oil contamination. Contamination (0.25 mL during 10 s) was performed after 37% phosphoric acid etching with an air/oil spray. The specimens were randomly assigned to subgroups, according to the bonding protocol adopted: subgroup A - F was applied to enamel without an intermediate bonding agent layer; In subgroups B and C, SB and PB, respectively, were applied, light-cured, and then F was applied and light-cured. Shear bond strength was tested at a crosshead speed of 0.5 mm/min in a universal testing machine. Means (± SD) in MPa were: IA-11.28 (±1.84); IIA-12.02 (±1.15); IB-9.73 (±2.38); IIB-9.62 (±2.29); IC-28.30 (±1.63); and IIC-25.50 (±1.91). It may be concluded that the oil contamination affected negatively the sealant bonding to enamel and the acetone-based adhesive system (PB) layer applied underneath the sealant was able to prevent its deleterious effects to adhesion.Este estudo avaliou in vitro a resistência ao cisalhamento (RC) de um selante resinoso [Fluroshield (F); Dentsply/Caulk] em associação com um sistema adesivo com solvente a base de etanol [Adper Single Bond 2 (SB); 3M/ESPE] ou a base de acetona [Prime & Bond (PB); 3M/ESPE] após contaminação com óleo do esmalte. Superfícies mesiais e distais de esmalte de 30 terceiros molares hígidos foram aleatoriamente alocadas em 2 grupos (n=30): I - contaminação com óleo; II - sem contaminação. A contaminação foi realizada (0,25 mL;10 s) com um jato de ar/óleo após o condicionamento do esmalte com ácido fosfórico a 37%. Os espécimes foram aleatoriamente alocados em subgrupos, de acordo com a técnica adesiva empregada: A - F foi aplicado sobre o esmalte condicionado sem sistema adesivo; B - SB + F; C - PB + F. RC foi testada em uma máquina universal de ensaios (0,5 mm/min; 50 kgf) e os dados analisados por ANOVA e t-teste (α=0,01). As médias de RC em MPa foram: IA-11,28 (±1,84); IIA-12,02(±1,15); IB-9,73 (±2,38); IIB-9,62 (±2,29); IC-28,30 (±1.63); e IIC-25,50 (±1,91). Conclui-se que a contaminação com o óleo afetou a adesão do selante resinoso ao esmalte e o sistema adesivo com solvente a base de acetona (Prime & Bond) aplicado sob o selante foi capaz de impedir os efeitos deletérios da contaminação com óleo

Non-contact profilometry of eroded and abraded enamel irradiated with an Er:YAG laser

Literature has reported positive results regarding the use of lasers in the control of erosive lesions; however, evaluating whether they are effective in the control of the progression of erosive/abrasive lesions is important. Objectives: This study aimed to evaluate the effect of the Er:YAG laser irradiation in controlling the progression of erosion associated with abrasive lesions in enamel. Material and methods: Bovine incisors were sectioned, flattened and polished. Forty-eight enamel slabs were subjected to treatment in an intraoral phase. Twelve volunteers used an intraoral appliance containing one slab that was irradiated with an Er:YAG laser (5.2 J/cm2, 85 mJ, 2 Hz) and another non-irradiated slab on each side of the appliance, during one phase of 5 d, under a split-mouth design. Devices were subjected to erosive challenges (1% citric acid, 5 min, 3 times a day) and abrasive challenges one h after (brushing force of 1.5 N for 15 s) randomly and independently on each side of the device. Measurements of enamel loss were performed via 3D optical profilometry (μm). We analyzed data using the Kruskal-Wallis and Mann-Whitney tests and morphological characteristics via scanning electron microscopy. Results: Following erosive and abrasive challenges, the group that was irradiated with the Er:YAG laser presented less loss of structure than the non-irradiated group. The group that underwent erosion and irradiation did not exhibit a significant difference from the non-irradiated group. Conclusion: Irradiation with the Er:YAG laser did not control the loss of structure of enamel subjected to erosion but did control abrasion after erosion

Surface and subsurface erosion of primary enamel by acid beverages over time

This study evaluated the influence of a cola-type soft drink and a soy-based orange juice on the surface and subsurface erosion of primary enamel, as a function of the exposure time. Seventy-five primary incisors were divided for microhardness test (n=45) or scanning electron microscopy (SEM) analysis (n=30). The specimens were randomly assigned to 3 groups: 1 - artificial saliva (control); 2 - cola-type soft drink; and 3 - soy-based orange juice. Immersion cycles in the beverages were undertaken under agitation for 5 min, 3 times a day, during 60 days. Surface microhardness was measured at 7, 15, 30, 45 and 60 days. After 60 days, specimens were bisected and subsurface microhardness was measured at 30, 60, 90, 120, 150 and 200 µm from the surface exposed. Data were analyzed by ANOVA and Tukey’s test (a=0.05). Groups 2 and 3 presented similar decrease of surface microhardness. Regarding subsurface microhardness, group 2 presented the lowest values. SEM images revealed that after 60 days the surfaces clearly exhibited structural loss, unlike those immersed in artificial saliva. It may be concluded that erosion of the surfaces exposed to the cola-type soft drink was more accentuated and directly proportional to the exposure time.Este estudo avaliou a influência de um refrigerante a base de cola e um suco de laranja a base de soja na erosão da superfície e subsuperfície do esmalte do dente decíduo, em função do tempo de exposição. Setenta e cinco incisivos decíduos foram divididos para o teste de microdureza (n=45) ou para a análise em microscópio eletrônico de varredura (MEV) (n=30). Os espécimes foram alocados aleatoriamente em 3 grupos: I - saliva artificial (controle); II - refrigerante a base de cola; e III - suco de laranja a base de soja. Ciclos de imersão nas bebidas foram realizados sob agitação durante 5 min, 3 vezes ao dia, durante 60 dias. A microdureza superficial foi mensurada aos 7, 15, 30, 45 e 60 dias. Após 60 dias, os espécimes foram seccionados e a microdureza subsuperficial foi mensurada aos 30, 60, 90, 120, 150 e 200 μm. Os dados foram analisados pelos testes ANOVA e Tukey (α=5%). Os grupos II e III apresentam uma diminuição similar da microdureza superficial. O grupo II apresentou menores valores de microdureza subsuperficial. As imagens de MEV revelaram que após 60 dias as superficies mostraram perdas de estruturas claramentes identificadas, diferentemente das superfícies imersas em saliva artificial. Pode-se concluir que a erosão das superficies expostas ao refrigerante a base de cola foi mais acentuada e diretamente proporcional ao tempo de exposição à bebida.The authors would like to acknowledge the contribution of Ms. Fatima Rizoli during the development of the experimental period. Authors are also grateful to Dr. Alberto Moreira Jorge Jr. from the Laboratory of Structural Characterization, Department of Material Engineering, Federal University of São Carlos, Brazil, for his assistance during SEM analysi

Selective Removal of Necrotic Dentin in Primary Teeth Using Laser Irradiation: One-Year Clinical Evaluation of Composite Restorations

Introduction: This study aimed to evaluate the child’s salivary cortisol levels, clinical performance and marginal adaptation of restorations after selective removal of necrotic dentin in primary teeth using Er: YAG laser irradiation.Methods: A double-blind clinical study was performed in children at 7-10 years. Children who had at least 2 teeth with carious lesions involving the occlusal and proximal surfaces of primary molars counterparts were selected. Removal of necrotic dentin was performed by 2 methods: Er: YAG laser irradiation and bur-preparation. Cortisol levels (n = 24) was evaluated by ELISA. Clinical analysis (n = 20) was performed after the restorations polish, 6 and 12 months after restorative procedure using United States Public Health Service (USPHS) method and photographs. Scanning electron microscopy (SEM) was used to analyz the marginal gap formation (n = 20). The analysis of the data was performed by 95% confidence interval, Shapiro-Wilk test, Friedman and Wilcoxon post hoc tests (α = 5%).Results: Cortisol levels were higher during selective removal of necrotic dentin, regardless of the method used (P > 0.05). After 12 months, there was no evidence of the difference in the restorations performed on cavities prepared by both methods. SEM analysis revealed that the laser-irradiated teeth showed 10% of gaps in the full extent of restoration. For bur-prepared teeth, 20% of gaps were found at the cavosurface margin.Conclusion: The salivary cortisol levels on children that received Er: YAG laser irradiation for removal the necrotic dentin was similar to the control group. Class II restorations evaluated after 1 year period did not suffer interference by the use of Er: YAG laser irradiation

Evaluation of Enamel Roughness in Vitro After Orthodontic Bracket Debonding Using Different Methods of Residual Adhesive Removal

Objective:The aim of the present study was to compare different techniques for resin remnant removal (RRR) after orthodontic bracket debonding and to evaluate alterations on the dental enamel caused by these methods. The null hypothesis tested was that there is no difference between RRR techniques in relationship the changes caused on the dental enamel.Methods:A total of 75 bovine mandibular permanent incisors were used in the study. Brackets were bonded and debonded in each tooth in two experimental regions. Five RRR techniques were used in the experimental groups (n=15): Group 1-diamond bur (6-bladed), Group 2-diamond bur (12-bladed), Group 3-diamond bur (30-bladed), Group 4-aluminum oxide sandblasting (AOS), and Group 5-Er:YAG laser. Enamel surface was evaluated using profilometry, and surface roughness analysis was performed at three time intervals: before bracket bonding, after RRR techniques, and after final polishing. Qualitative analyses of the enamel surfaces were performed using scanning electron microscopy.Results:Multiblade burs showed the best results, and the 30-bladed bur created a less irregular enamel surface. AOS caused greater enamel wear, and Er:YAG laser caused more surface irregularity.Conclusion:The null hypothesis was rejected. The multiblade burs were the least harmful than the other techniques. Enamel surface roughness after using the 30-blade bur was similar to the original enamel. These results indicate that the type of bur tested (30-bladed) can be indicated to remove resin remnants after bracket debonding

Clinical evaluation of the failure rate of metallic brackets bonded with orthodontic composites

The purpose of the present study was to evaluate in vivo the failure rate of metallic brackets bonded with two orthodontic composites. Nineteen patients with ages ranging from 10.5 to 38.7 years needing corrective orthodontic treatment were selected for study. The enamel surfaces from second premolars to second premolars were treated with Transbond Plus-Self Etching Primer (3M Unitek). Next, 380 orthodontic brackets were bonded on maxillary and mandibular teeth, as follows: 190 with Transbond XT composite (3M Unitek) (control) and 190 with Transbond Plus Color Change (3M Unitek) (experimental) in contralateral quadrants. The bonded brackets were light cured for 40 s, and initial alignment archwires were inserted. Bond failure rates were recorded over a six-month period. At the end of the evaluation, six bond failures occurred, three for each composite. Kaplan-Meyer method and log-rank test (Mantel-Cox) was used for statistical analysis, and no statistically significant difference was found between the materials (p=0.999). Both Transbond XT and Transbond Plus Color Change composites had low debonding rates over the study period

Terapia fotodinâmica: tratamento promissor na odontologia?

A terapia fotodinâmica (TFD) vem sendo pesquisada na odontologia a fim de estabelecer protocolos eficientes e indolores aos pacientes. É uma técnica sem efeitos colaterais, com custo acessível e que pode reduzir o tempo de reparação e a frequência de aparecimento de lesões. Os resultados podem ser observados poucas horas após a primeira irradiação com o laser. Três componentes são essenciais para a aplicação da técnica: a fonte de luz, o corante (fotossensibilizador) e o oxigênio. O objetivo dessa revisão de literatura é esclarecer o uso da terapia fotodinâmica na odontologia através de alguns estudos realizados nos últimos anos