Evaluation of the possibility of using diatomite natural mineral as a composite agent in acrylic coating

WOS: 000427736200014In the present study the possibility of the commercially available acryl and diatomite earth (DE) mineral as a composite coating for corrosion protection of Mg alloys has been evaluated. The acrylic coating is used as a top coating in a wide field of applications like automotive, aerospace, medicine and electronics where it shows beneficial properties. Diatomite-dispersed acrylic paint was applied over the substrate by conventional spray technique with an air pressure of 3 kg cm(-2). Firstly the acryl was mixed with hardener and then the DE was added to the mixture. Four types of coating with 0, 2, 4, 8 g/L DE have been prepared. The results show that adding up to 4 g/L of the DE improved the corrosion resistance and produced a coating with acceptable surface roughness

Waterborne hyperbranched alkyd-acrylic resin obtained by miniemulsion polymerization

Abstract Four waterborne hyperbranched alkyd-acrylic resins (HBRAA) were synthesized by miniemulsion polymerization from a hyperbranched alkyd resin (HBR), methyl methacrylate (MMA), butyl acrylate (BA) and acrylic acid (AA), by using benzoyl peroxide (BPO) and ammonium persulfate (AP) as initiators. The reaction between HBR and acrylic monomers was evidenced by differential scanning calorimetric (DSC), nuclear magnetic resonance (NMR) and gel permeation chromatography (GPC). The conversion percentage, glass transition temperature (Tg), content of acrylic polymer (determined by soxhlet extraction) and molecular weight increased with the content of acrylic monomers used in the synthesis. The main structure formed during the synthesis was the HBRAA. The analysis by dynamic light scattering (DLS) showed that the particle size distribution of HBRAA2, HBRAA3 and HBRAA4 resins were mainly monomodal. The film properties (gloss, flexibility, adhesion and drying time) of the HBRAA were good