Impedance analysis of secondary phases in a Co-implanted ZnO single crystal

published_or_final_versio

Mechanism of ferromagnetism in non-magnetic ion-doped zinc oxides

Zinc oxide (ZnO) that contains non-magnetic ionic dopants, such as nitrogen (N)-doped zinc oxide (ZnO:N), has been observed to exhibit ferromagnetism. Ferromagnetism is proposed to arise from the Coulomb excitation in the localized states that is induced by the oxygen vacancy, V O. A model based on the Coulomb excitation that is associated with the electron–phonon interaction theoretically explains the ferromagnetic mechanism of ZnO:N. This study reveals that the ferromagnetism will be induced by either deep localized states with a small V O concentration or shallow localized states with a high V O concentration. Additionally, electron–phonon coupling either suppresses the ferromagnetism that is induced by the deep donor states of V O or enhances the ferromagnetism that is induced by the shallow donor states of V O

One-step synthesis of ZnO nanosheets: a blue-white fluorophore

Zinc oxide is synthesised at low temperature (80°C) in nanosheet geometry using a substrate-free, single-step, wet-chemical method and is found to act as a blue-white fluorophore. Investigation by atomic force microscopy, electron microscopy, and X-ray diffraction confirms zinc oxide material of nanosheet morphology where the individual nanosheets are polycrystalline in nature with the crystalline structure being of wurtzite character. Raman spectroscopy indicates the presence of various defects, while photoluminescence measurements show intense green (centre wavelength approximately 515 nm) blue (approximately 450 nm), and less dominant red (approximately 640 nm) emissions due to a variety of vacancy and interstitial defects, mostly associated with surfaces or grain boundaries. The resulting colour coordinate on the CIE-1931 standard is (0.23, 0.33), demonstrating potential for use as a blue-white fluorescent coating in conjunction with ultraviolet emitting LEDs. Although the defects are often treated as draw-backs of ZnO, here we demonstrate useful broadband visible fluorescence properties in as-prepared ZnO