A comparative study of ultrasonic direct contact, immersion, and layer resonance methods for assessment of enamel thickness in teeth

Wear of dental enamel is a growing problem, but is clinically difficult to diagnose and monitor. An accurate and easy-to-use non-destructive method for the measurement of enamel thickness would be useful for early diagnosis of enamel loss and for monitoring progression. Ultrasound has been identified by several researchers as a potential tool suitable for enamel thickness measurement. However, in vitro studies have shown that while the method is feasible, it suffers from wide variability. The methods proposed to date rely on the measurement of the time of flight of an ultrasonic pulse through the enamel layer. This requires the operator to locate the enamel-dentine junction. In this work, three methods are evaluated to try to reduce this variability and to investigate some practicalities of the approach. Time-of-flight methods using both contact and immersion transducers were used. Immersion transducers gave the most accurate results, within 10-15 per cent of values deduced from tooth sections, but would be harder to arrange for in vivo measurements. Preliminary studies have also shown that it is possible to achieve a resonance in the enamel layer and to measure thickness that way. While this approach needs further experimental refinement, it has the potential to be used for much thinner enamel layer thicknesses

Fluoride content and recharge ability of five glassionomer dental materials

<p>Abstract</p> <p>Background</p> <p>The relationship between fluoride content and fluoride release for glass-ionomer cements is not well understood. The aim of this laboratory study was: to determine the fluoride concentrations at the surfaces of glass-ionomer materials with respect to different storage media and different pH environments; to examine the recharge ability of the materials after NaF immersion; and to assess the morphological changes at the material surfaces using scanning electron microscope and energy dispersive spectroscopic techniques (SEM/EDS).</p> <p>Methods</p> <p>Five glass-ionomer materials, Fuji Triage (FT), Fuji II LC (FII), Fuji VIII (FVIII), Fuji IX GP (FIX), and Ketac N100 (KN), were analyzed in this study. Resin-based fluoride releasing material Helioseal F (HSF) was used as a comparison material. The sample consisted of 120 cured cement disks (n = 20 disks of each tested material, 10 × 1.5 mm). Five disks of each material were stored in 4 different storage media (I- saline, II- acidic solution ph = 2.5, III- acid solution ph = 5.5, IV- NaF solution (c = 500/106). After 7 days, two disks of each material were transferred from media I, II and III to the NaF solution for 3 min. EDS analysis was conducted in 3 randomly selected spots of each experimental disk. SEM was used to determine morphological characteristics of the material surface. Differences between the experimental groups have been analyzed using Student's t-test with the level of significance set at p < 0.001.</p> <p>Results</p> <p>FT showed the highest fluoride content at the surface of the material. The lowest amounts of fluoride ions were detected at the surfaces of the FT disks stored at low pH environments, and this difference was statistically significant (p < 0.001). Glass-ionomers showed significantly higher fluoride concentrations when compared to the HSF (p < 0.001). After immersion in the NaF solution, fluoride concentrations at the surfaces of the disks increased when compared with previous storage media (FT>FVIII>KN>FII>FIX). SEM analysis of the surface morphology revealed numerous voids, cracks and microporosities in all experimental groups, except for KN and HSF. More homogenous material structure with more discrete cracks was observed in samples stored at neutral pH environment, compared to disks stored in acidic solutions.</p> <p>Conclusion</p> <p>The tested materials could be considered as promising dental materials with potential prophylactic characteristics due to their relatively high fluoride content, but also the ability to extensively reabsorb fluoride ions, especially in acidic environments.</p

The oral microbiome – an update for oral healthcare professionals

For millions of years, our resident microbes have coevolved and coexisted with us in a mostly harmonious symbiotic relationship. We are not distinct entities from our microbiome, but together we form a 'superorganism' or holobiont, with the microbiome playing a significant role in our physiology and health. The mouth houses the second most diverse microbial community in the body, harbouring over 700 species of bacteria that colonise the hard surfaces of teeth and the soft tissues of the oral mucosa. Through recent advances in technology, we have started to unravel the complexities of the oral microbiome and gained new insights into its role during both health and disease. Perturbations of the oral microbiome through modern-day lifestyles can have detrimental consequences for our general and oral health. In dysbiosis, the finely-tuned equilibrium of the oral ecosystem is disrupted, allowing disease-promoting bacteria to manifest and cause conditions such as caries, gingivitis and periodontitis. For practitioners and patients alike, promoting a balanced microbiome is therefore important to effectively maintain or restore oral health. This article aims to give an update on our current knowledge of the oral microbiome in health and disease and to discuss implications for modern-day oral healthcare

Reduction in Fracture Resistance of the Root with Aging

Introduction: The incidence of vertical root fracture in endodontically treated teeth increases with patient age. This study evaluated the microstructure, chemical composition, and mechanical properties of radicular dentin as a function of aging. Methods: Single-rooted teeth were obtained from adult donors ranging from age 15 to older than 80 years. Beams were extracted from the middle third of the root and subjected to 4-point flexure to failure to evaluate strength of dentin in terms of donor age. Based on the strength distribution, the fatigue strength of root tissue from young (= 55 years) donor teeth was evaluated via cyclic flexure loading. The microstructure and chemical composition of radicular dentin from the 2 groups were evaluated as a function of distance from the root apex using microscopy and Raman spectroscopy, respectively. Results: The strength decreased with age by approximately 25 MPa per decade, which resulted in a significant difference (P <= .0001) between the young (199 +/- 36 MPa) and old (122 +/- 11 MPa) groups. There was also a significant difference (P <= .0001) in fatigue strength between the young and old age groups. Both the mineral-to-collagen ratio and degree of cross-linking increased with age, with the largest changes identified in the apical and middle thirds, respectively. Conclusions: There is a reduction in the damage tolerance of radicular dentin with increasing age. This degradation appears to result from changes in the microstructure, corresponding chemical composition, and increase in collagen cross-linking with age, and is most severe near the root apex

Effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading

This study evaluated the effect of air-particle abrasion protocols on the biaxial flexural strength, surface characteristics and phase transformation of zirconia after cyclic loading. Disc-shaped zirconia specimens (Ø: 15mm, thickness: 1.2mm) (N=32) were submitted to one of the air-particle abrasion protocols (n=8 per group): (a) 50μm Al2O3 particles, (b) 110μm Al2O3 particles coated with silica (Rocatec Plus), (c) 30μm Al2O3 particles coated with silica (CoJet Sand) for 20s at 2.8bar pressure. Control group received no air-abrasion. All specimens were initially cyclic loaded (×20,000, 50N, 1Hz) in water at 37°C and then subjected to biaxial flexural strength testing where the conditioned surface was under tension. Zirconia surfaces were characterized and roughness was measured with 3D surface profilometer. Phase transformation from tetragonal to monoclinic was determined by Raman spectroscopy. The relative amount of transformed monoclinic zirconia (FM) and transformed zone depth (TZD) were measured using XRD. The data (MPa) were analyzed using ANOVA, Tukey's tests and Weibull modulus (m) were calculated for each group (95% CI). The biaxial flexural strength (MPa) of CoJet treated group (1266.3±158(A)) was not significantly different than that of Rocatec Plus group (1179±216.4(A,B)) but was significantly higher than the other groups (Control: 942.3±74.6(C); 50μm Al2O3: 915.2±185.7(B,C)). Weibull modulus was higher for control (m=13.79) than those of other groups (m=4.95, m=5.64, m=9.13 for group a, b and c, respectively). Surface roughness (Ra) was the highest with 50μm Al2O3 (0.261μm) than those of other groups (0.15-0.195μm). After all air-abrasion protocols, FM increased (15.02%-19.25%) compared to control group (11.12%). TZD also showed increase after air-abrasion protocols (0.83-1.07μm) compared to control group (0.59μm). Air-abrasion protocols increased the roughness and monoclinic phase but in turn abrasion with 30μm Al2O3 particles coated with silica has increased the biaxial flexural strength of the tested zirconia