Effect of oxidizing concentration on the corrosion resistance of the cerium conversion coating on galvanized steel

Ce-based conversion films have been assessed as alternatives for replacement of Cr6+-based films,which have been forbidden for their toxicity and carcinogenic properties. However, corrosion protection associated with chromate films is difficult to achieve by other surface treatments. Experimental results have revealed that to obtain the highly satisfactory results provided by chromate-based conversion coatings, it is necessary to improve the anticorrosive properties of the new chromium-free coatings. The present work deals with the effect of the oxidant concentration in the cerium-based conversion baths on the corrosion resistance of the films deposited on galvanized steel. Electrogalvanized steel sheets were exposed to cerium chloride-based baths with different concentrations of oxidant for a minute. The surface of the treated samples was analyzed by XPS and SEM-EDXS, while its corrosion resistance was investigated using electrochemical tests (EIS) conducted in a 0.05 M NaCl solution and the impedance spectra evolution analyzed as a function of the exposure time. The results showed a direct relationship between oxidant concentration and corrosion resistance. When the oxidant concentration rose from2mL.L-1 to 12mL.L-1, the corrosion resistance increased about 5 times, and this was attributed to the decrease in the Ce3+/Ce4+ relationship of the conversion film.Fil: Culcasi, José Daniel. Universidad Nacional de La Plata; ArgentinaFil: Elsner, Cecilia Ines. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata; ArgentinaFil: Di Sarli, Alejandro Ramón. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; ArgentinaFil: Palomino, Luis. Universidade de Sao Paulo; BrasilFil: Tomachuk, Celia Regina. Instituto de Investigaciones Energéticas y Nucleares. San Pablo; BrasilFil: Costa, Ilda. Instituto de Investigaciones Energéticas y Nucleares. San Pablo; Brasi

Materializando el futuro

Desde el año 2007, desde la Dirección y Comisión de Carrera de Ingeniería en Materiales se han realizado visitas y charlas en escuelas técnicas y otras escuelas secundarias públicas de la región.Estas charlas tenían como principal objetivo la promoción de la carrera. Por otra parte, desde el año 2009 la Facultad de Ingeniería ha desarrollado distintas actividades tendientes a fortalecer el ingreso y la permanencia en la facultad, en particular para las carreras de bajo índice de ingreso. Dichas actividades incluyen la realización de videos institucionales y la realización, desde la Secretaría de Extensión, de seminarios en el Colegio Nacional Rafael Hernández, tendientes a dar una visión clara y actual de la práctica de la Ingeniería, acercando al estudiante a las distintas especialidades desde el estímulo a partir de dinámicas pedagógicas recreativas, de su curiosidad e interés y privilegiando el proceso de construcción colectiva. Tomando en consideración estos antecedentes y, teniendo en cuenta que los bajos indicadores de ingreso y permanencia de los sectores populares en carreras tecnológicas muchas veces se encuentran ligadas al desconocimiento de posibilidades académicas, económicas (becas) y de estrategias y lógicas del sector, así como de estrategias pedagógicas que los contengan, se planteó el proyecto de extensión de la Facultad de Ingeniería “Materializando el futuro”. Este proyecto tiene por objetivo estimular el pensamiento crítico de los estudiantes secundarios, poniendo en juego los elementos del conocimiento formal en relación a su vida cotidiana, con la intención de dar a conocer las aplicaciones prácticas de la ingeniería y analizarlas desde una perspectiva científica, tecnológica y soberana.Sección: Mecánica.Facultad de Ingenierí

Materializando el futuro

Desde el año 2007, desde la Dirección y Comisión de Carrera de Ingeniería en Materiales se han realizado visitas y charlas en escuelas técnicas y otras escuelas secundarias públicas de la región.Estas charlas tenían como principal objetivo la promoción de la carrera. Por otra parte, desde el año 2009 la Facultad de Ingeniería ha desarrollado distintas actividades tendientes a fortalecer el ingreso y la permanencia en la facultad, en particular para las carreras de bajo índice de ingreso. Dichas actividades incluyen la realización de videos institucionales y la realización, desde la Secretaría de Extensión, de seminarios en el Colegio Nacional Rafael Hernández, tendientes a dar una visión clara y actual de la práctica de la Ingeniería, acercando al estudiante a las distintas especialidades desde el estímulo a partir de dinámicas pedagógicas recreativas, de su curiosidad e interés y privilegiando el proceso de construcción colectiva. Tomando en consideración estos antecedentes y, teniendo en cuenta que los bajos indicadores de ingreso y permanencia de los sectores populares en carreras tecnológicas muchas veces se encuentran ligadas al desconocimiento de posibilidades académicas, económicas (becas) y de estrategias y lógicas del sector, así como de estrategias pedagógicas que los contengan, se planteó el proyecto de extensión de la Facultad de Ingeniería “Materializando el futuro”. Este proyecto tiene por objetivo estimular el pensamiento crítico de los estudiantes secundarios, poniendo en juego los elementos del conocimiento formal en relación a su vida cotidiana, con la intención de dar a conocer las aplicaciones prácticas de la ingeniería y analizarlas desde una perspectiva científica, tecnológica y soberana.Sección: Mecánica.Facultad de Ingenierí

Materializando el futuro

Desde el año 2007, desde la Dirección y Comisión de Carrera de Ingeniería en Materiales se han realizado visitas y charlas en escuelas técnicas y otras escuelas secundarias públicas de la región.Estas charlas tenían como principal objetivo la promoción de la carrera. Por otra parte, desde el año 2009 la Facultad de Ingeniería ha desarrollado distintas actividades tendientes a fortalecer el ingreso y la permanencia en la facultad, en particular para las carreras de bajo índice de ingreso. Dichas actividades incluyen la realización de videos institucionales y la realización, desde la Secretaría de Extensión, de seminarios en el Colegio Nacional Rafael Hernández, tendientes a dar una visión clara y actual de la práctica de la Ingeniería, acercando al estudiante a las distintas especialidades desde el estímulo a partir de dinámicas pedagógicas recreativas, de su curiosidad e interés y privilegiando el proceso de construcción colectiva. Tomando en consideración estos antecedentes y, teniendo en cuenta que los bajos indicadores de ingreso y permanencia de los sectores populares en carreras tecnológicas muchas veces se encuentran ligadas al desconocimiento de posibilidades académicas, económicas (becas) y de estrategias y lógicas del sector, así como de estrategias pedagógicas que los contengan, se planteó el proyecto de extensión de la Facultad de Ingeniería “Materializando el futuro”. Este proyecto tiene por objetivo estimular el pensamiento crítico de los estudiantes secundarios, poniendo en juego los elementos del conocimiento formal en relación a su vida cotidiana, con la intención de dar a conocer las aplicaciones prácticas de la ingeniería y analizarlas desde una perspectiva científica, tecnológica y soberana.Sección: Mecánica.Facultad de Ingenierí

Tinplate: Evaluation of its Corrosion Behavior in Aqueous Media

Las primeras etapas del deterioro de chapas comerciales de hojalata expuestas a distintas soluciones salinas fueron estudiadas mediante técnicas electroquímicas y de análisis de superficie complementadas por microscopia óptica y electrónica de barrido. Sus resultados fueron analizados e interpretados utilizando modelos capaces de describir adecuadamente la degradación metálica de interfaces tan complejas como reactivas. Se concluyó que: 1) el deterioro de la superficie metálica ocurre mayormente durante las primeras 24 horas de inmersión, alcanzándose luego un comportamiento relativamente estable y reproducible con independencia del medio utilizado; 2) excepto en las soluciones “buffer” basadas en bórax o carbonato donde los escasos productos de corrosión aportaron un efecto protector, en los restantes medios tales productos fueron, en general variantes no protectoras de un oxihidróxido de hierro; y 3) estos resultados coinciden con las velocidades de corrosión determinadas electroquímicamente y, por ende, con el lapso de vida útil del recubrimiento.The first deterioration steps suffered by commercially available tinplate sheets exposed to different saline solutions were studied using electrochemical and surface analysis techniques, as well as optical and electronic scanning microscopy. Their results were analyzed and interpreted utilizing models able to adequately describe the degradation of those as complex as reactive metallic interfaces. It was concluded that: 1) independently of the medium, the main degradation of the metallic surface takes place within the first 24h immersion, but then its behavior is relatively stable and reproducible; 2) except in the buffer solutions based on borax or carbonate where the scarce corrosion products provided a protective effect, in the other electrolyte medium such products were, in general, a variety of non-protective iron oxyhydroxides; and 3) these results are in agreement with the electrochemically determined corrosion rates and, therefore, with the coating useful life.Centro de Investigación y Desarrollo en Tecnología de Pintura

Efectos del tratamiento de homogeneizado en la extrudabilidad de la aleación AA-6063

Los procesos de plantas industriales son el único modelo que reproduce de forma exacta las transformaciones que sufre el material a lo largo de la cadena de producción, es común entonces encontrarnos con la afirmación: “El mejor laboratorio que reproduce las condiciones de proceso es la planta misma”. En el proceso de fabricación de productos de extrusión de Aluminio se parte del barrote colado y se busca a través de un proceso de homogeneizadosolubilizado romper la estructura de colada y optimizar la microestructura de cara al proceso de extrusión. Las distintas estructuras de colada encontradas en los barrotes producto de los gradientes térmicos inherentes al proceso industrial, junto con la dispersión en los ciclos de homogeneizado-solubilizado dieron como resultado una amplia variabilidad en las microestructuras observadas. Se caracterizó y estudió la microestructura de los barrotes, tamaño de grano, fases AlFeSi y SiMg2 presentes, en dos condiciones: a) En bruto de colada y b) luego del homogeneizado-solubilizado. Se relacionó lo observado con la calidad superficial del producto terminado. En el presente trabajo se encuentra una marcada consistencia entre el la calidad superficial de los perfiles de extrusión y el criterio de extrudabilidad que se desprende del estudio de la microestructura. Se concluye finalmente que luego del homogeneizadosolubilizado, es el grado de transformación β→α-AlFeSi, su fragmentación y esferoidización, lo que define la calidad superficial del producto.Facultad de Ingenierí

Effect of zinc crystals size on galvanized steel deformation and electrochemical behavior

Hot-dip galvanized steel sheets with different spangle sizes were deformed by means of rolling and tension. The change of preferential crystallographic orientation and of superficial characteristics due to the deformation was analyzed by means of both X-rays diffraction and optical and scanning electronic microscopy. A correlation between such changes and the involving deformation modes was intended to be done and the spangle size influence on these modes was studied. Coating reactivity change due to the deformation was investigated by means of quasi-steady DC electrochemical tests. The results allow to infer that, in great spangle samples, the main deformation mechanism is twinning whereas in small spangle ones, pyramidal slip systems happen as well. The increase of the reactivity with the deformation is greater in tension than in rolling and it is more important in small than in great spangle samples.Facultad de Ingenierí

Tinplate: Evaluation of its Corrosion Behavior in Aqueous Media

Las primeras etapas del deterioro de chapas comerciales de hojalata expuestas a distintas soluciones salinas fueron estudiadas mediante técnicas electroquímicas y de análisis de superficie complementadas por microscopia óptica y electrónica de barrido. Sus resultados fueron analizados e interpretados utilizando modelos capaces de describir adecuadamente la degradación metálica de interfaces tan complejas como reactivas. Se concluyó que: 1) el deterioro de la superficie metálica ocurre mayormente durante las primeras 24 horas de inmersión, alcanzándose luego un comportamiento relativamente estable y reproducible con independencia del medio utilizado; 2) excepto en las soluciones “buffer” basadas en bórax o carbonato donde los escasos productos de corrosión aportaron un efecto protector, en los restantes medios tales productos fueron, en general variantes no protectoras de un oxihidróxido de hierro; y 3) estos resultados coinciden con las velocidades de corrosión determinadas electroquímicamente y, por ende, con el lapso de vida útil del recubrimiento.The first deterioration steps suffered by commercially available tinplate sheets exposed to different saline solutions were studied using electrochemical and surface analysis techniques, as well as optical and electronic scanning microscopy. Their results were analyzed and interpreted utilizing models able to adequately describe the degradation of those as complex as reactive metallic interfaces. It was concluded that: 1) independently of the medium, the main degradation of the metallic surface takes place within the first 24h immersion, but then its behavior is relatively stable and reproducible; 2) except in the buffer solutions based on borax or carbonate where the scarce corrosion products provided a protective effect, in the other electrolyte medium such products were, in general, a variety of non-protective iron oxyhydroxides; and 3) these results are in agreement with the electrochemically determined corrosion rates and, therefore, with the coating useful life.Centro de Investigación y Desarrollo en Tecnología de Pintura

Caracterización y desarrollo de peliculas pasivantes libres de cromo hexavalente sobre recubrimientos galvánicos

En este trabajo se analiza el efecto protector de diversas películas pasivantes comerciales (basadas en Cr+6 convencional, en circonatos y recubrimiento orgánico sin iones metálicos) aplicadas sobre chapas recubiertas con aleación 55% Al-Zn. También se estudia el efecto anticorrosivo de la concentración de H2O2 en soluciones de CeCl3 utilizadas en el tratamiento de pasivación de aceros electrocincados expuestos a la acción de una solución 0,05 M NaClFacultad de Ingenierí

Tinplate: Evaluation of its Corrosion Behavior in Aqueous Media

Las primeras etapas del deterioro de chapas comerciales de hojalata expuestas a distintas soluciones salinas fueron estudiadas mediante técnicas electroquímicas y de análisis de superficie complementadas por microscopia óptica y electrónica de barrido. Sus resultados fueron analizados e interpretados utilizando modelos capaces de describir adecuadamente la degradación metálica de interfaces tan complejas como reactivas. Se concluyó que: 1) el deterioro de la superficie metálica ocurre mayormente durante las primeras 24 horas de inmersión, alcanzándose luego un comportamiento relativamente estable y reproducible con independencia del medio utilizado; 2) excepto en las soluciones “buffer” basadas en bórax o carbonato donde los escasos productos de corrosión aportaron un efecto protector, en los restantes medios tales productos fueron, en general variantes no protectoras de un oxihidróxido de hierro; y 3) estos resultados coinciden con las velocidades de corrosión determinadas electroquímicamente y, por ende, con el lapso de vida útil del recubrimiento.The first deterioration steps suffered by commercially available tinplate sheets exposed to different saline solutions were studied using electrochemical and surface analysis techniques, as well as optical and electronic scanning microscopy. Their results were analyzed and interpreted utilizing models able to adequately describe the degradation of those as complex as reactive metallic interfaces. It was concluded that: 1) independently of the medium, the main degradation of the metallic surface takes place within the first 24h immersion, but then its behavior is relatively stable and reproducible; 2) except in the buffer solutions based on borax or carbonate where the scarce corrosion products provided a protective effect, in the other electrolyte medium such products were, in general, a variety of non-protective iron oxyhydroxides; and 3) these results are in agreement with the electrochemically determined corrosion rates and, therefore, with the coating useful life.Centro de Investigación y Desarrollo en Tecnología de Pintura