In vitro evaluation of the precision of working casts for implant-supported restoration with multiple abutments

OBJECTIVE: The purpose of this study was to compare the accuracy of two working cast fabrication techniques using strain-gauge analysis. METHODS: Two working cast fabrication methods were evaluated. Based on a master model, 20 working casts were fabricated by means of an indirect impression technique using polyether after splinting the square transfer copings with acrylic resin. Specimens were assigned to 2 groups (n=10): Group A (GA): type IV dental stone was poured around the abutment analogs in the conventional way; Group B (GB), the dental stone was poured in two stages. Spacers were used over the abutment analogs (rubber tubes) and type IV dental stone was poured around the abutment analogs in the conventional way. After the stone had hardened completely, the spacers were removed and more stone was inserted in the spaces created. Six strain-gauges (Excel Ltd.), positioned in a cast bar, which was dimensionally accurate (perfect fit) to the master model, recorded the microstrains generated by each specimen. Data were analyzed statistically by the variance analysis (ANOVA) and Tukey's test (α= 5%). RESULTS: The microstrain values (µepsilon) were (mean±SD): GA: 263.7±109.07µepsilon, and GB: 193.73±78.83µepsilon. CONCLUSION: There was no statistical difference between the two methods studied

Avaliação da resistência ao cisalhamento da união entre duas ligas a base de CoCr e uma cerâmica

INTRODUCTION: Based on the importance of the integrity of the metal/ceramic interface, the purpose of this work was to evaluate the shear bond strength of the metal-ceramic union of two Co-Cr alloys (Wirobond C, Bego; Remanium 2000, Dentaurum) combined with Omega 900 ceramic (Vita Zahnfabrik). MATERIAL and METHOD: Eleven cylindrical matrixes were made for each alloy, and the metallic portion was obtained with the lost wax casting technique with standardized waxing of 4mm of height and of 4mm of diameter. The ceramic was applied according to the manufacturer’s recommendations with the aid of a teflon matrix that allowed its dimension to be standardized in the same size as the metallic portion. The specimens were submitted to the shear bond test in an universal testing machine (EMIC), with the aid of a device developed for such intention, and constant speed of 0.5mm/min. RESULTS and CONCLUSIONS: The mean resistance was 48.387MPa for Wirobond C alloy, with standard deviation of 17.718, and 55.956MPa for Remanium 2000, with standard deviation of 17.198. No statistically significant difference was observed between the shear strength of the two metal-ceramic alloys. ______________________________________________________________________________________________________________ RESUMOINTRODUÇÃO: Baseados na importância da integridade da interface metal-cerâmica, este trabalho tem como objetivo avaliar a resistência ao cisalhamento da união metal-cerâmica de duas ligas de Co-Cr (Wirobond C, Bego; Remanium 2000, Dentaurum) combinadas com a cerâmica Omega 900 (Vita Zahnfabrik). MATERIAIS E MÉTODOS: Foram confeccionados 11 corpos-de-prova cilíndricos para cada liga utilizada, sendo que a porção metálica foi obtida por fundição pela técnica da cera perdida, através de enceramentos padronizados com 4mm de altura por 4mm de diâmetro. A aplicação da cerâmica foi realizada segundo recomendações do fabricante, com auxílio de uma matriz de teflon que permitia sua padronização com as mesmas dimensões da porção metálica. Os corpos-de-prova foram submetidos ao ensaio de resistência ao cisalhamento em máquina de ensaios universal (EMIC), com auxílio de dispositivo desenvolvido para tal propósito, sob velocidade constante de 0,5mm/ min. RESULTADOS E CONCLUSÕES: As médias de resistência obtidas foram 48,387 MPa para a liga Wirobond C, com desvio padrão de 17,718, e 55,956 MPa para a Remanium 2000, com desvio padrão de 17,198. Após análise de variância foi possível observar que não há diferença estatisticamente significante entre os valores de resistência ao cisalhamento das duas ligas metalocerâmicas

Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks

Objectives. The aim of this study was to evaluate the effect of thermal and mechanical cycling alone or in combination, on the flexural strength of ceramic and metallic frameworks cast in gold alloy or titanium. Methods. Metallic frameworks (25 mm x 3 mm x 0.5 mm) (N = 96) cast in gold alloy or commercial pure titanium (Ti cp) were obtained using acrylic templates. They were airborne particle-abraded with 150 mu m aluminum oxide at the central area of the frameworks (8 mm x 3 mm). Bonding agent and opaque were applied on the particle-abraded surfaces and the corresponding ceramic for each metal was fired onto them. The thickness of the ceramic layer was standardized by positioning the frameworks in a metallic template (height: I mm). The specimens from each ceramic-metal combination (N = 96, n = 12 per group) were randomly assigned into four experimental fatigue conditions, namely water storage at 37 degrees C for 24 h (control group), thermal cycling (3000 cycles, between 4 and 55 degrees C, dwell time: 10 s), mechanical cycling (20,000 cycles under 10 N load, immersion in distilled water at 37 degrees C) and, thermal and mechanical cycling. A flexural strength test was performed in a universal testing machine (crosshead speed: 1.5 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey`s test (alpha = 0.05). Results. The mean flexural strength values for the ceramic-gold alloy combination (55 +/- 7.2MPa) were significantly higher than those of the ceramic-Ti cp combination (32 +/- 6.7 MPa) regardless of the fatigue conditions performed (p < 0.05). Mechanical and thermo-mechanical fatigue decreased the flexural strength results significantly for both ceramic-gold alloy (52 +/- 6.6 and 53 +/- 5.6 MPa, respectively) and ceramic-Ti cp combinations (29 +/- 6.8 and 29 +/- 6.8 MPa, respectively) compared to the control group (58 +/- 7.8 and 39 SA MPa, for gold and Ti cp, respectively) (p < 0.05) (Tukey`s test). While ceramic-Ti cp combinations failed adhesively at the metal-opaque interface, gold alloy frameworks exhibited a residue of ceramic material on the surface in all experimental groups. Significance. Mechanical and thermo-mechanical fatigue conditions decreased the flexural strength values for both ceramic-gold alloy and ceramic-Ti cp combinations with the results being significantly lower for the latter in all experimental conditions. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved

Effect of mechanical cycling on the flexural strength of densely sintered ceramics

Objectives. The aim of this study was to evaluate the effect of mechanical cycling on the biaxial flexural strength of two densely sintered ceramic materials. Methods. Disc shaped zirconia (In-Ceram Zirconia) and high alumina (Procera AllCeram) ceramic specimens (diameter: 15 min and thickness: 1.2 mm) were fabricated according to the manufacturers' instructions. The specimens from each ceramic material (N = 40, n = 10/per group) were tested for flexural strength either with or without being subjected to mechanical cycling (20,000 cycles under 50 N load, immersion in distilled water at 37 degrees C) in a universal testing machine (1 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 0.05). Results. High alumina ceramic specimens revealed significantly higher flexural strength values without and with mechanical cycling (647 +/- 48 and 630 +/- 143 MPa, respectively) than those of zirconia ceramic (497 +/- 35 and 458 +/- 53 MPa, respectively) (p <0.05). Mechanical cycling for 20,000 times under 50 N decreased the flexural strength values for both high alumina and Significance. High alumina ceramic revealed significantly higher mean flexural strength values than that of zirconia ceramic tested in this study either with or without mechanical cycling conditions. (C) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved