Fabrication and Characterization of Planar-Structure Perovskite Solar Cells

Currently organic-inorganic hybrid perovskite solar cells (PSCs) is one kind of promising photovoltaic technology due to low production cost, easy fabrication method and high power conversion efficiency. Charge transport layers are found to be critical for device performance and stability. A traditional electron transport layer (ETL), such as TiO2 (Titanium dioxide), is not very efficient for charge extraction at the interface. Compared with TiO2, SnO2 (Tin (IV) Oxide) possesses several advantages such as higher mobility and better energy level alignment. In addition, PSCs with planar structure can be processed at lower temperature compared to PSCs with other structures. In this thesis, planar-structure perovskite solar cells with SnO2 as the electron transport layer are fabricated. The one-step spin-coating method is employed for the fabrication. Several issues are studied such as annealing the samples in ambient air or glovebox, different concentration of solution used for the samples, the impact of using filter for solutions on samples. Finally, a reproducible fabrication procedure for planer-structure perovskite solar cells with an average power conversion efficiency of 16.8%, and a maximum power conversion efficiency of 18.1% is provided

Submicron cubic boron nitride as hard as diamond

Here, we report the sintering of aggregated submicron cubic boron nitride (sm-cBN) at a pressure of 8 GPa. The sintered cBN compacts exhibit hardness values comparable to that of single crystal diamond, fracture toughness about 5-fold that of cBN single crystal, in combination with a high oxidization temperature. Thus, another way has been demonstrated to improve the mechanical properties of cBN besides reducing the grain size to nano scale. In contrast to other ultrahard compacts with similar hardness, the sm-cBN aggregates are better placed for potential industrial application, as their relative low pressure manufacturing perhaps be easier and cheaper. (C) 2015 AIP Publishing LLC