Thermo-Responsive Hydrophilic Support for Polyamide Thin-Film Composite Membranes with Competitive Nanofiltration Performance

Poly(N-isopropylacrylamide) (PNIPAAm) was introduced into a polyethylene terephthalate (PET) nonwoven fabric to develop novel support for polyamide (PA) thin-film composite (TFC) membranes without using a microporous support layer. First, temperature-responsive PNIPAAm hydrogel was prepared by reactive pore-filling to adjust the pore size of non-woven fabric, creating hydrophilic support. The developed PET-based support was then used to fabricate PA TFC membranes via interfacial polymerization. SEM–EDX and AFM results confirmed the successful fabrication of hydrogel-integrated non-woven fabric and PA TFC membranes. The newly developed PA TFC membrane demonstrated an average water permeability of 1 L/m2 h bar, and an NaCl rejection of 47.0% at a low operating pressure of 1 bar. The thermo-responsive property of the prepared membrane was studied by measuring the water contact angle (WCA) below and above the lower critical solution temperature (LCST) of the PNIPAAm hydrogel. Results proved the thermo-responsive behavior of the prepared hydrogel-filled PET-supported PA TFC membrane and the ability to tune the membrane flux by changing the operating temperature was confirmed. Overall, this study provides a novel method to fabricate TFC membranes and helps to better understand the influence of the support layer on the separation performance of TFC membranes

Thermo-responsive hydrophilic support for polyamide thin-film composite membranes with competitive nanofiltration performance

Poly(N-isopropylacrylamide) (PNIPAAm) was introduced into a polyethylene terephthalate (PET) nonwoven fabric to develop novel support for polyamide (PA) thin-film composite (TFC) membranes without using a microporous support layer. First, temperature-responsive PNIPAAm hydrogel was prepared by reactive pore-filling to adjust the pore size of non-woven fabric, creating hydrophilic support. The developed PET-based support was then used to fabricate PA TFC membranes via interfacial polymerization. SEM–EDX and AFM results confirmed the successful fabrication of hydrogel-integrated non-woven fabric and PA TFC membranes. The newly developed PA TFC membrane demonstrated an average water permeability of 1 L/m2 h bar, and an NaCl rejection of 47.0 % at a low operating pressure of 1 bar. The thermo-responsive property of the prepared membrane was studied by measuring the water contact angle (WCA) below and above the lower critical solution temperature (LCST) of the PNIPAAm hydrogel. Results proved the thermo-responsive behavior of the prepared hydrogel-filled PET-supported PA TFC membrane and the ability to tune the membrane flux by changing the operating temperature was confirmed. Overall, this study provides a novel method to fabricate TFC membranes and helps to better understand the influence of the support layer on the separation performance of TFC membranes

Harnessing the power of metal-organic frameworks to develop microplastic fouling resistant forward osmosis membranes

With the gradual increase of microplastics (MPs) in water and wastewater streams, it is imperative to investigate their removal using tertiary treatment systems to minimize and preferably prevent their entrance into aquatic environments. Forward osmosis (FO) is a non-pressurized membrane process with potential applications in MPs removal from wastewater. However, efficient application of FO systems relies on developing high-performance FO membranes with low fouling tendency. MPs are proven as emerging foulants in membrane systems, diminishing their performance and lifetime and this highlights the need to consider MP fouling in developing sustainable membranes. The current study focuses on a novel modification of thin film composite (TFC) FO membranes by MIL-53(Fe) as a water-stable and hydrophilic metal-organic framework. Experimental results demonstrated that the optimized FO membrane (0.2 wt% MIL-53(Fe)) achieved a significantly higher water flux (90% increase) with a 23% less reverse salt flux. The modified membrane also had significantly less flux decline in fouling experiments and higher flux recovery after physical cleaning compared to the control membrane affirming its higher antifouling efficiency. MIL-53(Fe) integration in the FO substrate proved to be a practical method for developing high-performance TFC FO membranes with improved antifouling properties against MPs and organic foulants

Thermo-Responsive Hydrophilic Support for Polyamide Thin-Film Composite Membranes with Competitive Nanofiltration Performance

Poly(N-isopropylacrylamide) (PNIPAAm) was introduced into a polyethylene terephthalate (PET) nonwoven fabric to develop novel support for polyamide (PA) thin-film composite (TFC) membranes without using a microporous support layer. First, temperature-responsive PNIPAAm hydrogel was prepared by reactive pore-filling to adjust the pore size of non-woven fabric, creating hydrophilic support. The developed PET-based support was then used to fabricate PA TFC membranes via interfacial polymerization. SEM–EDX and AFM results confirmed the successful fabrication of hydrogel-integrated non-woven fabric and PA TFC membranes. The newly developed PA TFC membrane demonstrated an average water permeability of 1 L/m2 h bar, and an NaCl rejection of 47.0% at a low operating pressure of 1 bar. The thermo-responsive property of the prepared membrane was studied by measuring the water contact angle (WCA) below and above the lower critical solution temperature (LCST) of the PNIPAAm hydrogel. Results proved the thermo-responsive behavior of the prepared hydrogel-filled PET-supported PA TFC membrane and the ability to tune the membrane flux by changing the operating temperature was confirmed. Overall, this study provides a novel method to fabricate TFC membranes and helps to better understand the influence of the support layer on the separation performance of TFC membranes

Microplastics fouling and interaction with polymeric membranes: A review

The emergence and accumulation of microplastics (MPs) in various aquatic environments have recently raised significant concerns. Wastewater treatment plants (WWTPs) have been identified as one of the major sources of MPs discharge to the environment, implying a substantial need to improve advanced techniques for more efficient removal of MPs. Polymeric membranes have been proven effective in MPs removal. However, fouling is the main drawback of membrane processes and MPs can foul the membranes due to their small size and specific surface properties. Hence, it is important to investigate the impacts of MPs on membrane fouling to develop efficient membrane-based techniques for MPs removal. Although membrane technologies have a high potential for MPs removal, the interaction of MPs with membranes and their fouling effects have not been critically reviewed. The purpose of this paper is to provide a state-of-the-art review of MPs interaction with membranes and facilitate a better understanding of the relevant limitations and prospects of the membrane technologies. The first section of this paper is dedicated to a review of recent studies on MPs occurrence in WWTPs aiming to determine the most frequent MPs. This is followed by a summary of recent studies on MPs removal using membranes and discussions on the impact of MPs on membrane fouling and other probable issues (abrasion, concentration polarisation, biofouling, etc.). Finally, some recommendations for further research in this area are highlighted. This study serves as a valuable reference for future research on the development of anti-fouling membranes considering these new emerging contaminates