Influence of ultrasonic setting on compressive and diametral tensile strengths of glass ionomer cements

The aim of this study was to assess the influence of ultrasonic wave propagation on the compressive (CS) and diametral tensile (DTS) strengths of glass ionomer cements (GICs). Three variables were evaluated: conventional GICs, ultrasonic excitation and storage time (1 hour, 24 hours and 7 days). Bovine teeth molds were used for simulating a clinical ultrasonic excitation. The data were submitted to three-way ANOVA and Tukey tests (P < 0.05). All the tested conventional GICs presented an increase in strength from 1 hour to 7 days for CS and DTS. Ultrasonic excitation resulted in a statistically significant increase in the CS, but showed no statistically significant difference in the DTS. Regardless the GICs tested the increase in strength was maturation time-dependent for all groups

Resistência à compressão e à tração diametral de cimentos de ionômero de vidro

The aim of this study was to compare, in different periods of time, the compressive and diametral tensile strength of a traditional high viscous glass ionomer cement: Fuji IX (GC Corporation), with two new Brazilian GIC's: Vitro-Molar (DFL) and Bioglass R (Biodinamica), all indicated for the Atraumatic Restorative Treatment (ART) technique. Fifteen disk specimens (6.0mm diameter x 3.0mm height) for the diametral tensile strength (DTS) test and fifteen cylindrical specimens (6.0mm diameter x 12.0mm height) for the compressive strength (CS) test were made of each GIC. Specimens were stored in deionized water at 37&ordm; C and 100% of humidity in a stove until testing. Five specimens of each GIC were submitted to CS and DTS test in each period, namely 1 hour, 24 hours and 7 days. The specimens were tested in a testing machine (Emic) at a crosshead speed of 1.0mm/min for CS and 0.5mm/min for the DTS test until failure occurred. The data were submitted to two-way ANOVA and Tukey tests (alpha=0.05). The mean CS values ranged from 42.03 to 155.47MPa and means DTS from 5.54 to 13.72 MPa, with test periods from 1h to 7 days. The CS and DTS tests showed no statistically significant difference between Fuji IX and Vitro Molar, except for CS test at 1-hour period. Bioglass R had lowest mean value for CS of the cements tested. In DTS test Bioglass R presented no statistically significant differences when compared with all others tested GICs at 1-hour period and Bioglass R presented no difference at 24-hour and 7-day periods when compared to Vitro-Molar. Further studies to investigate other physical properties such as fracture toughness and wear resistance, as well as chemical composition and biocompatibility, are now needed to better understand the properties of these new Brazilian GIC's.Comparou-se a Resistência à Compressão (RC) e à Tração Diametral (TD) de um cimento de ionômero de vidro de alta viscosidade [Fuji IX (GC Corporation)] e de dois novos cimentos Brasileiros [Vitro Molar (DFL) e Bioglass R (Biodinamica)], recentemente lançados no mercado, ambos indicados para o Tratamento Restaurador Atraumático (ART), em diferentes períodos de tempo. Foram confeccionados quinze corpos-de-prova com 6,0 mm de diâmetro x 3,0 mm de altura para o teste de TD e quinze com 6,0 mm de diâmetro e 12,0 mm de altura para o teste de RC, para cada ionômero a ser testado. Os corpos-de-prova foram armazenados em recipientes plásticos, com água deionizada, e mantidos em estufa a 37&ordm;C e 100% de umidade, até a realização dos testes. Cinco corpos-de-prova de cada material foram submetidos aos testes de TD e RC em cada período de tempo: 1-hora, 24-horas e 7-dias, em uma máquina de testes universal (EMIC - DL 500) a uma velocidade de 1,0 mm/min para RC e 0,5mm/min para TD. Os dados obtidos foram submetidos aos testes ANOVA a dois critérios e Tukey (á=0,05). Os valores médios de RC e TD variaram de 42,03 a 155.47 MPa e de 5,54 a 13,72 MPa, respectivamente para os períodos analisados. O Fuji IX e o Vitro Molar não apresentaram diferenças em relação aos testes de RC e TD, exceto para RC no período de 1-hora. O Bioglass R apresentou os menores valores de RC dos cimentos testados. Na TD o Bioglass R não apresentou diferença em relação aos outros cimentos testados no período de 1-hora e não foi diferente do Vitro-Molar nos períodos de 24-horas e 7-dias. Mais estudos são necessários para avaliar outras propriedades mecânicas desses novos cimentos de ionômero de vidro brasileiros, tais como: tenacidade e desgaste, bem como composição química e biocompatibilidade

Comparasion of two minimally invasive methods on the longevity of glass ionomer cement restorations: short-term results of a pilot study

The purpose of this study was to evaluate the clinical performance of glass ionomer cement (GIC) restorations comparing two minimally invasive methods in permanent teeth after 12 months. Fifty pregnant women (second trimester of pregnancy), mean age 22 ± 5.30 years, were treated by two previously trained operators. The treatment approaches tested were: chemomechanical method (CarisolvTM; MediTeam) and atraumatic restorative treatment (ART). A split-mouth study design was used in which the two treatments were randomly placed in 50 matched pairs of permanent teeth. The chemomechanical method (CM) was the test group and the ART was the control group. The treatments were performed in Public Health Centers. The tested restorative material was a high-strength GIC (Ketac Molar; 3M/ESPE). The restorations were placed according to the ART guidelines. Two calibrated independent examiners evaluated the restorations in accordance with ART criteria. The inter-examiner kappa was 0.97. Data were analyzed using 95% confidence interval on the binomial distribution and Fisher's exact test at 5% significance level. In a 12-month follow-up, 86% of the restorations were evaluated. In the test group (CM), 100% (CI=93.3-100%) of the restorations were considered successful. In the control group (ART) 97.6% (CI=87.4-99.9%) of the restorations were considered successful and 2.4% unsuccessful (marginal defect >;0.5 mm). There was no statistically significant difference between the 12-mounth success rate for both groups (Fisher's exact test: P=0.49) and between the two operators (Fisher's exact test: P=1.00). Both minimally invasive methods, chemomechanical method and ART, showed a similar clinical performance after 12 months of follow up

Comparasion of two minimally invasive methods on the longevity of glass ionomer cement restorations: short-term results of a pilot study

The purpose of this study was to evaluate the clinical performance of glass ionomer cement (GIC) restorations comparing two minimally invasive methods in permanent teeth after 12 months. Fifty pregnant women (second trimester of pregnancy), mean age 22 ± 5.30 years, were treated by two previously trained operators. The treatment approaches tested were: chemomechanical method (CarisolvTM; MediTeam) and atraumatic restorative treatment (ART). A split-mouth study design was used in which the two treatments were randomly placed in 50 matched pairs of permanent teeth. The chemomechanical method (CM) was the test group and the ART was the control group. The treatments were performed in Public Health Centers. The tested restorative material was a high-strength GIC (Ketac Molar; 3M/ESPE). The restorations were placed according to the ART guidelines. Two calibrated independent examiners evaluated the restorations in accordance with ART criteria. The inter-examiner kappa was 0.97. Data were analyzed using 95% confidence interval on the binomial distribution and Fisher's exact test at 5% significance level. In a 12-month follow-up, 86% of the restorations were evaluated. In the test group (CM), 100% (CI=93.3-100%) of the restorations were considered successful. In the control group (ART) 97.6% (CI=87.4-99.9%) of the restorations were considered successful and 2.4% unsuccessful (marginal defect >0.5 mm). There was no statistically significant difference between the 12-mounth success rate for both groups (Fisher's exact test: P=0.49) and between the two operators (Fisher's exact test: P=1.00). Both minimally invasive methods, chemomechanical method and ART, showed a similar clinical performance after 12 months of follow up.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES

Diagnóstico, plan de tratamiento y restauración de un diente con el síndrome del diente fisurado: reporte de caso y seguimiento de siete años

Se describe y reporta el diagnóstico, tipo de tratamiento y seguimiento de un caso con el síndrome del diente fisurado. Una paciente de 26 años acusaba sensibilidad a los cambios térmicos y a la oclusión en el lado izquierdo de la mandíbula. Al examen clínico se observó dos grietas o fisuras pigmentadas en las superficies bucales y linguales de la pieza 36. La colocación de una restauración directa con resina compuesta resolvió los síntomas y alivió por completo el dolor. Dicha situación persistió incluso en el control realizado 7 años después. El diagnóstico y tratamiento para el caso descrito dio como resultado un completo alivio y mantenimiento de la situación alcanzada siete años después

Avaliação de seis meses de restaurações ART de classe I em uma comunidade de alta experiência de cárie no Brasil

The aim of this study to evaluate the success rate in one-surface ART restorations placed in permanent molars using a glass ionomer cement especially developed for ART in a community with high caries experience; to evaluate the operator influence on its success, post-operative sensitivity and technique acceptance by patients. Prior to placement of the restorations, the Gingival Bleeding Index, Visible Plaque Index, DMFT, dmft indices and treatment needed were assessed. One hundred and fifty five one-surface restorations were placed in permanent molars of school children, according to the WHO ART manual, 1997. After 6 months, the success rate was verified clinically and by slides. At baseline, the mean DMFT was 2.56 (&plusmn;1.08) and the mean dmft, 2.53 (&plusmn;2.33). Operators A and B have placed 102 and 53 ART restorations respectively. The mean time of placement was 16 minutes and 25 seconds to operator A and 14 minutes and 43 seconds to operator B. At 6-month follow up, 152 ART restorations were evaluated and 97.3% were assessed to be successful. Two restorations were excluded from the sample because the ART restorations were replaced by amalgam fillings. Only 4 restorations have failed, in which 2 due to caries, 1 due to fistula presence and the other because the restoration was lost. Four patients reported postoperative sensitivity. At this study period, ART treatment seems to be suitable for its purpose. Further evaluations are necessary to the new glass ionomer cements especially developed for ART technique provided good results at 6-month follow up in a community with high DMFT and dmft indices. The success rate for one-surface cavities in permanent molars was 97.3%, and the studied indices seemed to have no influence in this early evolution period.O objetivo deste estudo foi avaliar o índice de sucesso de restaurações de cavidade de classe I, realizadas em molares permanentes, utilizando-se a técnica do ART e um cimento de ionômero de vidro desenvolvido especialmente para a técnica, em uma comunidade de alto risco à cárie; avaliar a influência do operador no sucesso da técnica e avaliar a sensibilidade pós-operatória e a aceitação da técnica por parte dos pacientes. Antes da realização do tratamento verificou-se o índice de placa visível e o índice de sangramento gengival, CPOD, ceo-d e necessidade de tratamento. Um total de 155 restaurações de uma superfície foram realizadas em molares permanentes de escolares, de acordo com o manual de ART da OMS. Após 6 meses, realizou-se o acompanhamento clínico e por diapositivos. Inicialmente, o CPOD foi de 2,56 ( &plusmn;1,08) e o ceod de 2,53 ( &plusmn;2,33 ). Os operadores A e B realizaram 102 e 53 restaurações de ART respectivamente. O tempo médio para o tratamento foi de 16 minutos e 25 segundos para A e 14 minutos e 43 segundos para B. Aos seis meses. 152 restaurações foram avaliadas e 97,3% consideradas sucesso. Duas restaurações foram excluídas da amostra pois foram substituídas por amálgama. Somente 4 restaurações falharam, duas por recidiva de cárie, 1 por presença de fistula e a última por perda da restauração. Quatro pacientes relataram sensibilidade pós-operatória. O tratamento ART cumpriu seus objetivos no período analisado. Avaliações futuras são necessárias, especialmente para os cimentos de ionômero de vidro de alta viscosidade, devido aos bons resultados nesta comunidade de alto índice de cárie. O índice de sucesso foi de 97,3% e os índices de cárie parecem não influenciar no sucesso do tratamento

Cimento de ionômero de vidro: efeitos de diferentes períodos de tempo sobre a resistência à tração diametral

Objetivo: Avaliar a resistência à tração diametral (RTD) de um Cimento de Ionômero de Vidro (CIV) convencional em diferentes períodos de tempo de armazenamento. Métodos: Os corpos-de-prova para o teste de RTD foram confeccionados em matrizes de aço inoxidável (6,0±0,1 mm de diâmetro e 3,0±0,1 mm de altura), de acordo com a Especificação nº 9917 da ISO para CIV, utilizando o sistema de proporcionamento em volume do CIV pó-líquido (colher dosadora: gota). Em seguida, os corpos-de-prova foram armazenados em recipientes plásticos, contendo água destilada e mantidos em estufa a 37ºC e 100% de umidade, até a realização dos testes mecânicos após 1 hora, 24 horas e 7 dias, em uma máquina de testes universal (Instron Corp., EUA) a uma velocidade de 0,5 mm/min. Os dados obtidos foram submetidos aos testes estatísticos ANOVA a um critério, seguido pelo teste de múltipla comparação de médias Tukey, com nível de significância de 0,05 (P&lt;0,05). Resultados: A análise dos dados revelou um aumento da RTD em função do período de tempo de armazenamento 1 hora &lt; 24 horas &lt; 7 dias. Diferença estatisticamente significante foi observada apenas para o período de armazenamento de 1 hora e 7 dias (P=0,024). Conclusão: O aumento da RTD do CIV foi dependente do seu período de tempo de armazenamento

Avaliação das fontes de luz em uso nas clínicas odontológicas da FO/UFG: acompanhamento de 1 ano

Objetivo: Avaliar o estado de conservação e a densidade de potência das fontes de luz disponíveis para o atendimento clínico na Faculdade de Odontologia da Universidade Federal de Goiás (FO/UFG), em 2011-2012. Métodos: As seguintes informações e especificações técnicas das referidas fontes de luz foram coletadas: ambulatório (clínica odontológica) onde está alocada, tipo de fonte [aparelho de luz halógena e Diodo Emissores de Luz (LEDs)], marca, teste de paralelismo (exclusivamente para as fontes de luz halógena), estado de conservação da ponteira transmissora de luz, densidade de potência em mW/cm2 e data da aquisição. Os dados obtidos foram submetidos à análise estatística descritiva, teste t de Student, ANOVA a um critério e teste de Tukey para comparações múltiplas (P&lt;0,05). Resultados: No período de 2011-2012, a FO/UFG dispunha respectivamente de 20 e 22 fontes de luz para atendimento clínico. Quanto ao seu estado de conservação observou-se que em 2011, 90% das fontes de luz encontravam-se em inadequado estado de conservação, enquanto em 2012 este número foi de 54%. Em termos de densidade de potência 55% das fontes de luz apresentavam densidade menor que 300 mW/cm2 em 2011, enquanto em 2012 este resultado foi de 54,54%. Não foi observada diferença estatística significante quanto à densidade de potência das fontes de luz halógena (P=0,81) e LED (P=0,41) testadas no período avaliado. Conclusões: As fontes de luz no período de acompanhamento de um ano apresentaram uma melhoria no seu estado de conservação, enquanto a densidade de potência permaneceu similar

Avaliação de selantes ionoméricos realizados pela técnica do ART em comunidade com alta experiência de cárie: 1 ano de acompanhamento

The aim of this study was to investigate the retention rates and effect on occlusal caries incidence of two glass ionomers used as sealants, placed according to the Atraumatic Restorative Treatment (ART) approach, in a high caries-risk community. A total of 150 newly erupted first molars of 42 schoolchildren, between 6-8 years of age were selected. The teeth were divided into two groups: experimental and control groups. In the experimental group, 76 teeth were sealed using Vidrion R-SS White (conventional GIC) and in the control group, 74 teeth were sealed using ChemFlex-Dentsply (high-viscosity conventional GIC). The sealants were applied by one operator following the "press finger technique", described in the ART-WHO manual. Two calibrated independent examiners carried out the evaluation according to the ART criteria. The intra and inter-examiner agreements were 0.84 and 0.81, respectively. Data were submitted to Mann-Whitney and Chi-square tests (pO objetivo deste trabalho foi avaliar o índice de retenção e o efeito na incidência de cárie oclusal de dois selantes ionoméricos realizados pela técnica do Tratamento Restaurador Atraumático (ART) em comunidades com alto índice de cárie. Foram selecionados 150 primeiros molares recém-erupcionados de 42 escolares, entre 6-8 anos de idade. Os dentes foram divididos em dois grupos: experimental e controle. No grupo experimental 76 dentes foram selados com Vidrion R-SSWhite (CIV-convencional) e no grupo controle, 74 dentes foram selados com ChemFlex-Dentsply (CIV-alta viscosidade). Os selantes foram realizados por apenas um operador pela técnica da "pressão digital", descrita no manual de ART da OMS. Dois avaliadores independentes e calibrados segundo os critérios do ART realizaram a avaliação. A concordância intra e inter-examinadores foi de 0,84 e 0,81, respectivamente. Os resultados foram submetidos aos testes Mann-Whitney e Q-quadrado (

Fuentes de luz de uso clínico en el pre grado: 7 años de seguimento

Objetive: To monitor the light curing units available at undergraduate dental clinics of a Brazilian Public Higher Education Institution for seven uninterrupted years. Materials and methods: In the period between 2011-2017, the quality control of light curing units at the Faculty of Dentistry, Federal University of Goiás, was evaluated by analyzing their state of conservation and power density (mW/cm2). Data obtained were subjected to descriptive statistical analysis and Levene, Shapiro-Wilk, Kruskal-Wallis, Dunn and Chi-square tests (P &lt;0.05). Results: Regarding the conservation status of the light curing units, comparatively, there was no statistically significant difference between the years 2012, 2016 and 2017 (p&gt; 0.05). Statistically significant differences were found for power density values between years (p &lt;0.0001). In pairwise comparisons, the power density values for the years 2011 (p &lt;0.01) and 2012 (p &lt;0.05) were statistically different from the years 2015, 2016 and 2017. Conclusions: A significant improvement in the state of conservation of light curing units was observed in the initial four years of evaluations, with a decline in the fifth year and stabilization in the last two years. Regarding the power density of the light curing units, a gradual increase was observed in the seven years of study, with stabilization of the results after the fifth year of quality control.Objetivo: Realizar, durante siete años ininterrumpidos, un control y seguimiento de las fuentes de luz disponibles en las clínicas odontológicas de pre graado de una Institución de Enseñanza Superior Pública Brasileña. Material y métodos: Durante el período comprendido entre 2011-2017 se evaluó el control de calidad de las fuentes de luz de la Facultad de Odontología de la Universidad Federal de Goiás a través del análisis de su estado de conservación y de su densidad de potencia (mW/cm2). Los datos obtenidos se sometieron a un análisis estadístico descritpivo y a las pruebas de Levene, Shapiro-Wilk, Kruskal-Wallis, Dunn y Chi-cuadrado (P&lt;0,05). Resultados: No se observaron diferencias estadísticas significativas del estado de conservación de las fuentes de luz entre los años 2012, 2016 y 2017 (p&gt;0,05). Sí se observaron diferencias estadísticas significativas entre los valores de densidad de potência entre dichos años (p&lt;0,0001). En las comparaciones por pares, los valores de densidad de potencia para los años 2011 (p&lt;0,01) y 2012 (p&lt;0,05) fueron estadísticamente diferentes de los años 2015, 2016 y 2017. Conclusiones: Comparativamente se observó una mejora sustancial del estado de conservación de las fuentes de luz en los cuatro años iniciales de evaluaciones, con una disminución en el quinto año y una estabilización en los dos últimos años. Durante los siete años de estudio de la densidad de potencia de las fuentes de luz se observó en un aumento gradual de la misma con una estabilización de los resultados a partir del quinto año de control de calidad