Deformation and damage mechanisms in an alpha/beta 6242 Ti alloy in fatigue, dwell-fatigue and creep at room temperature. Influence of internal hydrogen

International audienceIn beta-forged Ti6242, dwell periods during ambient stress-controlled fatigue substantially reduce the lifetime. Cracks initiate due to the coalescence of shear-induced cavities nucleated at alpha/beta interfaces. This damage is most often due to pyramidal slip and enhanced by dwell periods. The influence of the hydrogen content on the tensile, creep and fatigue behaviour, damage mechanisms, and crack growth was investigated. Hydrogen reduced the proportional limit and the serrations on the tensile curves but increased the conventional yield stress at high strain rate, so that it either slowed down or enhanced room temperature creep, depending on the applied stress. When a H-induced reduction in creep occurred, H had a beneficial influence on the fatigue and dwell-fatigue lives, in spite of an acceleration of fatigue crack growth. Observations of the H distribution, using the microprint technique show that even though most of it resides in the beta phase, some is transported into the alpha phase, especially in heavily deformed alpha laths

NUCLEATION OF CRACKS FROM SHEAR-INDUCED CAVITIES IN AN a/b TITANIUM ALLOY IN FATIGUE, ROOM-TEMPERATURE CREEP AND DWELL-FATIGUE

International audienceIn titanium alloys, dwell periods during room-temperature stress-controlled fatigue tests are responsible for substantial reductions in lifetime compared to pure fatigue loading. The mechanisms of such a creep-fatigue interaction have been investigated for alloy Ti6242. SEM and TEM observations revealed crack initiation by coalescence of shear-induced cavities nucleated at a/b interfaces in large colonies of a laths nearly parallel to the loading axis. The density and average size of cavities were larger in dwell-fatigue and creep than in fatigue. A qualitative micromechanical model of cavity nucleation based on discrete dislocation dynamics was developed. The number of cycles for cavity nucleation was computed as a function of the applied stress range. A finite threshold, dependent on the size of a laths colonies with similar orientation, was found. The simulations predict earlier cavity nucleation in creep or dwell-fatigue than in pure fatigue, which is consistent with the performed experiments

Multi-partner benchmark experiment of fatigue crack growth measurements

International audienceThe design of reliable structures and the estimation of the residual fatigue life of industrial parts containing flaws or cracks rely on our ability to predict the propagation of fatigue cracks. Whereas in industrial component cracks might have a complex path due to geometry and loading, lab experiments used for identifying crack propagation law are often in pure mode I. The paper presents a synthesis of an experimental benchmark performed in the context of a French national research network. A sample has been designed to produce mixed-mode crack propagation and variation of small scale yielding conditions. Two geometries and two maximum load levels are defined for the two tested materials: a stainless steel and an aluminum alloy. Around ten participants performed experiments using their usual instrumentation. Among the eight possible parameter sets, three are selected for which detailed results are presented. A satisfying overall agreement is obtained. But, some discrepancies are evidenced due either to limitations of the instrumentation or simply because from one lab to the other the applied load is not exactly the same. It is thus concluded that one of the most important issue is boundary conditions, which is confirmed by numerical simulations

L'auteur

Parce qu’il en va du sens même de l’enseignement de la littérature et probablement de son avenir, il est temps de récuser à la fois l’annexion de l’Auteur par « l’histoire littéraire » et sa mise à l’écart au seul bénéfice de « l’analyse textuelle » et de ses dérivés méthodologiques. La question de « l’auteur » - c’est-à-dire de la singularité d’une vie immergée dans le langage - est en effet au cœur de l’expérience nourricière de la lecture, ou devrait l’être. Il n’y a donc pas lieu de s’étonner si, à l’invitation du Centre de Recherches sur les Modernités Littéraires de l’Université Michel de Montaigne (Bordeaux 3) et de l’IUFM d’Aquitaine, des écrivains, des biographes, des théoriciens du littéraire et des spécialistes de l’enseignement du français ont accepté de prendre au sérieux cette question controversée de « l’auteur », en la considérant comme une variable majeure de la réalité du texte et de la relation que l’on entretient avec lui. De fait, ce volume présente un éventail d’approches et de perspectives nouvelles, à la lumière de recherches en cours. Il se propose ainsi d’offrir au lecteur ordinaire comme au chercheur, matière à frayer les voies d’une critique inventive. Les quatre volets qui organisent cet ouvrage - « Ouvertures », « Les Discours de légitimation », « Lieux et territoires », « Les enjeux d’une relation », loin, d’ailleurs, de prétendre clore la discussion, en suggèrent au contraire la dynamique. Pourvus d’un « visage », d’un « corps » et d’une « vie » irréductibles à ceux de l’état civil, les auteurs sont d’abord l’incarnation de leurs œuvres telles qu’elles sont reçues et perçues par une époque, une génération, mais aussi par une mémoire et des institutions. Il fallait donc tenter de démêler la trame de cette fable en cessant d’opposer « biographie » et « mythographie », histoire et légende, portrait et icône, pour tenter de reconnaître ce qui, à travers le temps, nous relie de multiples façons à cet étranger si familier, que l’on désigne sous le nom d’« auteur » - notion que la littérature n’a cessé, sous toutes les latitudes, de réinventer. A charge pour les enseignants d’en témoigner, moins en qualité de techniciens du texte que de passeurs, toujours sur le qui-vive