Interface characteristics in an {\alpha}+{\beta} titanium alloy
The alpha/beta interface in Ti-6Al-2Sn-4Zr-6Mo (Ti-6246) is investigated via
centre of symmetry analysis, both as-grown and after 10% cold work.
Semi-coherent interface steps are observed at a spacing of 4.5 +/-1.13 atoms in
the as-grown condition, in good agreement with theory prediction (4.37 atoms).
Lattice accommodation is observed, with elongation along [-1 2 -1 0]alpha and
contraction along [1 0 -1 0]alpha . Deformed alpha exhibited larger, less
coherent steps with slip bands lying in {110}beta. This indicates dislocation
pile-up at the grain boundary, a precursor to globularisation, offering insight
into the effect of deformation processing on the interface, which is important
for titanium alloy processing route design.Comment: Revised after revie
Vulnerability amongst Low-Income Households in the Private Rented Sector in England
Analysis of problems experienced by vulnerable, low income households living in the private rented sector in Englan
The Evolving Private Rented Sector: Its Contribution and Potential
Review of the private rented sector in Englan
Dissociating recollection from familiarity: electrophysiological evidence that familiarity for faces is associated with a posterior old/new effect
In recognition memory research, a tension exists between dual-process and single-process models of episodic retrieval. Dual-process models propose that ‘familiarity’ assessment and the ‘recollection’ of contextual information are independent processes, while single process models claim that one common process supports retrieval. Event-related potentials (ERPs) have been used to show dissociations between the mid frontal and the left parietal ERP old/new effects, which have been associated with familiarity and recollection, respectively. While much ERP evidence favours dual-process theory, Yovel and Paller (2004) used faces as retrieval cues to demonstrate that posterior old/new effects index both familiarity and recollection, a finding consistent with single process models. Here we present evidence supporting Yovel and Paller’s claim that a posterior old/new effect indexes familiarity for faces, along with a novel finding that recollection is associated with an anterior old/new effect. Importantly, and in contrast to Yovel and Paller, the old/new effects associated with familiarity and recollection were topographically dissociable, consistent with a dual process view of recognition memory. The neural correlates of familiarity and recollection identified here for faces appear to be different from those typically observed, suggesting that the ERP old/new effects associated with episodic recognition are not the same under all circumstances
Recommended from our members
Cell-Surface Proteomics Identifies Differences in Signaling and Adhesion Protein Expression between Naive and Primed Human Pluripotent Stem Cells.
Naive and primed human pluripotent stem cells (hPSC) provide valuable models to study cellular and molecular developmental processes. The lack of detailed information about cell-surface protein expression in these two pluripotent cell types prevents an understanding of how the cells communicate and interact with their microenvironments. Here, we used plasma membrane profiling to directly measure cell-surface protein expression in naive and primed hPSC. This unbiased approach quantified over 1,700 plasma membrane proteins, including those involved in cell adhesion, signaling, and cell interactions. Notably, multiple cytokine receptors upstream of JAK-STAT signaling were more abundant in naive hPSC. In addition, functional experiments showed that FOLR1 and SUSD2 proteins are highly expressed at the cell surface in naive hPSC but are not required to establish human naive pluripotency. This study provides a comprehensive stem cell proteomic resource that uncovers differences in signaling pathway activity and has identified new markers to define human pluripotent states
Interface characteristics in an α+β titanium alloy
The α/β interface in Ti-6Al-2Sn-4Zr-6Mo (Ti-6246) was investigated via center of symmetry analysis, both as-grown and after 10% cold work. Semicoherent interface steps are observed at a spacing of 4.5±1.13 atoms in the as-grown condition, in good agreement with theory. Lattice accommodation is observed, with elongation along [1210]α and contraction along [1010]α. Deformed α exhibited larger, less coherent steps with slip bands lying in {110}β. This indicates dislocation pile-up at the grain boundary, a precursor to globularization during heat treatment. Atom probe tomography measurements of secondary α plates in the fully heat-treated condition showed a Zr excess at the interface, which was localized into regular structures indicative of Zr association with interface defects, such as dislocations. Such chemo-mechanical stabilization of the interface defects would both inhibit plate growth during elevated temperature service and the interaction of interface defects with gliding dislocations during deformation
The Kinetics of Primary Alpha Plate Growth in Titanium Alloys
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the
beta are examined, comparing model to experiment. The plate growth velocity
depends sensitively both on the diffusivity D(T) of the rate-limiting species
and on the supersaturation around the growing plate. These result in a maxima
in growth velocity around 40 K below the transus, once sufficient
supersaturation is available to drive plate growth. In Ti-6246, the plate
growth velocity was found to be around 0.32 um min-1 at 850 oC, which was in
good agreement with the model prediction of 0.36 um min-1 . The solute field
around the growing plates, and the plate thickness, was found to be quite
variable, due to the intergrowth of plates and soft impingement. This solute
field was found to extend to up to 30 nm, and the interface concentration in
the beta was found to be around 6.4 at.% Mo. It was found that increasing O
content will have minimal effect on the plate lengths expected during
continuous cooling; in contrast, Mo approximately doubles the plate lengths
obtained for every 2 wt.% Mo reduction. Alloys using V as the beta stabiliser
instead of Mo are expected to have much faster plate growth kinetics at
nominally equivalent V contents. These findings will provide a useful tool for
the integrated design of alloys and process routes to achieve tailored
microstructures.Comment: Revised version resubmitted to journa
Sensitivity of material failure to surface roughness: a study on titanium alloys Ti64 and Ti407
The relationship between material failure and surface roughness has been investigated using two titanium alloys: Ti64 and the more ductile Ti407. Three surface types were created (polished, sandblasted and scratched) with instances spanning a wide range of average roughness. The surfaces were tested in three-point bending with the imparted roughness on the tensile under-surface of a rectangular beam specimen. Results showed failure of Ti64 to be highly sensitive to both magnitude and orientation of roughness. High roughness in the maximum tensile stress direction (and scratch like features perpendicular to this direction) were most detrimental. Thus, strain-to-failure (and work-to-failure) in Ti64 dropped off significantly with increasing surface roughness in the tensile direction. Finite element modelling of the test indicated that cracks initiate at zones of high plastic strain at the tips of roughness valleys due to high local surface curvature. Thus, roughness can be considered as a series of blunt crack-like features where larger crack tip curvature induces greater likelihood of crack propagation. Contrastingly, the mechanical response of Ti407 was insensitive to surface roughness owing to its significantly greater ductility. Thus, designers need to be aware of the sensitivity of failure of particular materials to surface roughness. The insensitivity of Ti407 is advantageous, but the sensitivity of failure to surface roughness in a material like Ti64 is potentially serious if not properly accounted for
Investigating the functional interaction between semantic and episodic memory: Convergent behavioral and electrophysiological evidence for the role of familiarity
Throughout our lives we acquire general knowledge about the world (semantic memory) while also retaining memories of specific events (episodic memory). Although these two forms of memory have been dissociated on the basis of neuropsychological data, it is clear that they typically function together during normal cognition. The goal of the present study was to investigate this interaction. One influence of semantic memory on episodic retrieval is ‘Levels Of Processing’; recognition is enhanced when stimuli are processed in a semantically meaningful way. Studies examining this semantic processing advantage have largely concluded that semantic memory augments episodic retrieval primarily by enhancing recollection. The present study provides strong evidence for an alternative relationship between semantic and episodic memory. We employed a manipulation of the semantic coherence of to-be-remembered information (semantically related vs. unrelated word pairs) during an associative recognition memory test. Results revealed that associative recognition is significantly enhanced for semantically coherent material, and behavioral estimates (using the process dissociation procedure) demonstrated concomitant changes in the contribution of familiarity to retrieval. Neuroimaging data (event-related potentials recorded at test) also revealed a significant increase in familiarity based retrieval. The electrophysiological correlate of familiarity (the mid-frontal ERP old/new effect) was larger for semantically related compared to unrelated word pairs, but no difference was present in the electrophysiological correlate of recollection (the left parietal old/new effect). We conclude that semantic memory and episodic memory do indeed interact in normal functioning, and not only by modulating recollection, but also by enhancing familiarity
- …