A importância relativa da densidade da madeira e do teor de carboidratos no rendimento de polpa e na qualidade do produto.

The purpose of this study was to evaluate basic density, chemical composition and fiber dimensions of ten Eucalyptus sp wood samples and to verify the impact of this set of parameters and their combination on the Kraft pulping process yield and on bleached pulp quality. Ten eucalypt woods of different species, with basic densities varying from 365 to 544 kg/m³ and total wood carbohydrate contents varying from 70.0 to 74.5%, were transformed into kraft pulp of kappa number 15,5-16,7 and bleached to 90% ISO brightness by the sequence OD(PO)D. Wood basic density showed stronger correlations with fiber dimensions and pulp quality than did chemical composition. However, pulping yield was strongly affected by chemical composition. Lighter woods resulted in higher pulping yields. However, wood specific consumption was lower for denser woods, even though these demanded more drastic pulping conditions to achieve a given kappa number. The pulp quality results suggest that lower density woods should be directed towards fabrication of refined paper (printing and writing grades) while the denser woods should be directed to the sanitary papers segment (tissue grades).O objetivo deste estudo foi avaliar a densidade básica, a composição química e as dimensões de fibras de dez amostras de madeira de Eucalyptus spp. e, verificar o impacto desse conjunto de parâmetros e sua combinação no rendimento do processo de polpação kraft e na qualidade da polpa branqueada. A madeira de dez espécies de eucalipto, com densidade básica variando entre 365 a 544 kg/m3 e teores de carboidratos totais variando entre 70,0 a 74,5% foi transformada em polpa Kraft, com número kappa 15,5-16,7 e branqueada a 90% ISO por uma seqüência de quatro estágios (OD(PO)D) composta de deslignificação com oxigênio (O), deslignificação com dióxido de cloro (D),  extração alcalina com peróxido pressurizado (PO) e branqueamento com dióxido de cloro (D). A densidade básica da madeira mostrou melhor correlação com as dimensões da fibra e qualidade da polpa que a sua composição química. Porém o rendimento depurado foi mais influenciado pela composição química da madeira do que pela densidade básica. Madeiras de menor densidade apresentaram maiores rendimentos de polpação, mas o consumo específico de madeira foi mais baixo para as madeiras mais densas. Os resultados de qualidade de polpa sugerem que madeiras com densidade mais baixa devam ser direcionadas à fabricação de papel refinado (impressão e de escrita), enquanto que as mais densas sejam destinadas ao segmento de papéis sanitários (tissue)

Relative importance of wood density and carbohydrate content on pulping yield and product quality

O objetivo deste estudo foi avaliar a densidade básica, a composição química e as dimensões de fibras de dez amostras de madeira de Eucalyptus spp. e, verificar o impacto desse conjunto de parâmetros e sua combinação no rendimento do processo de polpação kraft e na qualidade da polpa branqueada. A madeira de dez espécies de eucalipto, com densidade básica variando entre 365 a 544 kg/m3 e teores de carboidratos totais variando entre 70,0 a 74,5% foi transformada em polpa Kraft, com número kappa 15,5- 16,7 e branqueada a 90% ISO por uma seqüência de quatro estágios (OD(PO)D) composta de deslignificação com oxigênio (O), deslignificação com dióxido de cloro (D), extração alcalina com peróxido pressurizado (PO) e branqueamento com dióxido de cloro (D). A densidade básica da madeira mostrou melhor correlação com as dimensões da fibra e qualidade da polpa que a sua composição química. Porém o rendimento depurado foi mais influenciado pela composição química da madeira do que pela densidade básica. Madeiras de menor densidade apresentaram maiores rendimentos de polpação, mas o consumo específico de madeira foi mais baixo para as madeiras mais densas. Os resultados de qualidade de polpa sugerem que madeiras com densidade mais baixa devam ser direcionadas à fabricação de papel refinado (impressão e de escrita), enquanto que as mais densas sejam destinadas ao segmento de papéis sanitários (tissue).The purpose of this study was to evaluate basic density, chemical composition and fiber dimensions of ten Eucalyptus sp wood samples and to verify the impact of this set of parameters and their combination on the Kraft pulping process yield and on bleached pulp quality. Ten eucalypt woods of different species, with basic densities varying from 365 to 544 kg/m³ and total wood carbohydrate contents varying from 70.0 to 74.5%, were transformed into kraft pulp of kappa number 15,5-16,7 and bleached to 90% ISO brightness by the sequence OD(PO)D. Wood basic density showed stronger correlations with fiber dimensions and pulp quality than did chemical composition. However, pulping yield was strongly affected by chemical composition. Lighter woods resulted in higher pulping yields. However, wood specific consumption was lower for denser woods, even though these demanded more drastic pulping conditions to achieve a given kappa number. The pulp quality results suggest that lower density woods should be directed towards fabrication of refined paper (printing and writing grades) while the denser woods should be directed to the sanitary papers segment (tissue grades)

Propriedades de chapas de aglomerado fabricadas com adesivo tânico de angico-vermelho (Anadenanthera peregrina) e uréia-formadeído

O principal objetivo deste trabalho foi produzir chapas de aglomerado substituindo-se parcial ou totalmente os adesivos à base de uréia-formaldeído por adesivos de taninos extraídos da casca de angico-vermelho (Anadenanthera peregrina) e hidrolisados. As chapas de aglomerado foram fabricadas com partículas de Pinus elliottii e dimensões aproximadas de 40 x 40 x 1 cm, contendo 8% de sólidos de adesivo em relação à massa seca de partículas, sendo 100% de adesivo de uréia-formaldeído puro ou contendo 12,5, 25 e 37,5% de adesivo tânico. Foram produzidas, também, chapas com adesivos tânicos puros, constituindo um total de cinco tratamentos, com três repetições. As chapas foram fabricadas com densidade média de 0,7 g/cm³. As propriedades físicas e mecânicas das chapas foram determinadas em conformidade com a norma ASTM D-1037 (1993). Os resultados dos testes mecânicos foram comparados com os valores mínimos estabelecidos na norma ANSI/A 208.1-1993 (Wood Particleboard), enquanto os resultados dos testes de absorção de água e inchamento em espessura, comparados com os valores máximos estabelecidos na norma DIN 68m761 (1)-1961. A resistência mecânica das chapas de aglomerado produzidas com adesivos contendo taninos de angico-vermelho, com exceção do módulo de elasticidade, ultrapassou os valores mínimos requeridos na norma ANSI/A1-280/93. A absorção de água e o inchamento em espessura, após 2 e 24 h de imersão, de todas as chapas excederam o valor máximo estabelecido. Conclui-se que os adesivos de taninos de angico-vermelho podem substituir parcial ou totalmente o adesivo comercial de uréia-formaldeído, e as suas misturas são indicadas para uso interior, em que a resistência à umidade não é requerida