15 research outputs found
A photoluminescence study of excitonic grade CuInSe2 single crystals irradiated with 6 Mev electrons
High-quality single crystals of CuInSe2 with near-stoichiometric elemental compositions were irradiated with 6 MeV electrons, at doses from 1015 to 3 × 1018 cm−2, and studied using photoluminescence (PL) at temperatures from 4.2 to 300 K. Before irradiation, the photoluminescence spectra reveal a number of sharp and well resolved lines associated with free- and bound-excitons. The spectra also show broader bands relating to free-to-bound transitions and their phonon replicas in the lower energy region below 1.0 eV. The irradiation with 6 MeV electrons reduces the intensity of the free- and the majority of the bound-exciton peaks. Such a reduction can be seen for doses above 1016 cm−2. The irradiation induces new PL lines at 1.0215 eV and 0.9909 eV and also enhances the intensity of the lines at 1.0325 and 1.0102 eV present in the photoluminescence spectra before the irradiation. Two broad bands at 0.902 and 0.972 eV, respectively, are tentatively associated with two acceptor-type defects: namely, interstitial selenium (Sei) and copper on indium site (Cu In). After irradiation, these become more intense suggesting an increase in the concentration of these defects due to irradiation
Effects of selenisation temperature on photoluminescence and photoluminescence excitation spectra of ZnO/CdS/Cu2ZnSnSe4/Mo/glass
The effect of solar cell processing (including etching in KCN along with deposition of CdS and ZnO) on photoluminescence (PL) spectra and bandgap Eg (measured at 4.2 K by photoluminescence excitation) of Cu2ZnSnSe4 films, produced by selenising metallic precursors at 450 °C, 500 °C and 550 °C, was studied. Temperature and excitation intensity analysis of the P1 dominant band in the PL spectra of solar cells suggests that after processing this band still can be assigned to the free-to-bound recombination of free electrons with holes bound at deep acceptor levels influenced by valence band-tails. However processing increased the intensity of P1 and blue shifted it. The strongest effect was observed for the film selenised at 500 °C. For the film selenised at 450 °C the blue shift and increase in the intensity were smaller and only a slight intensity rise was found for the film selenised at 550 °C. The intensity increase we assign to a reduction in the concentration of non-radiative recombination centers on the surface because of the etching and changes in doping due to inter-diffusion of Cd, S, Se and Zn after the deposition of CdS. Such an inter-diffusion depends on the elemental composition of the films defining the chemistry of defects and influencing Eg which increased in the film selenised at 500 °C but decreased in the other films. Processing increased the P1 shift rate (j-shift) with excitation power change in all the films demonstrating a higher compensation degree in the solar cells which is consistent with the formation of an interface layer containing new donors CdCu
A luminescence study of Cu2ZnSnSe4/Mo/glass films and solar cells with near stoichiometric copper content
Cu2ZnSnSe4 (CZTSe) is one of the leading candidates for the absorber layer in sustainable solar cells. Thin films of CZTSe with a near stoichiometric [Cu]/[Zn + Sn] were used to produce solar cells with conversion efficiency η = 6.4% by a standard solar cell processing including KCN etching and the deposition of CdS and ZnO. Both CZTSe films and solar cells were examined using photoluminescence (PL) to analyse the nature of radiative recombination and photoluminescence excitation (PLE) at 4.2 K to determine the bandgap (E g ). Low temperature PL spectra of the films reveal an intense band P1 at 0.81 eV and a low intensity band P2 at 0.93 eV. Their temperature and excitation intensity dependencies suggest that they both involve recombinations of free electrons with holes localised at acceptors with the energy level influenced by potential fluctuations in the valence band. We associate P1 and P2 with different fractions of CZTSe: with a lower and higher degree of order of Cu and Zn on the cation sub-lattice, respectively. Device processing reduced the intensity of P1 by 2.5 whereas the intensity of P2 increased by a 1.5. We assign this to a low temperature annealing due to CdS and ZnO deposition which increased the fraction of CZTSe with high degree of Cu/Zn order and decreased the fraction with low degree of Cu/Zn order. Device processing increased E g , blue shifted P1, decreased its width, j-shift and the mean depth of potential fluctuations. These can also be related to the annealing and/or KCN etching and the chemical effect of Cd, due to CdS replacing copper at the CdS-CZTSe interface layer. Processing induced a new broad band P3 at 1.3 eV (quenching with E a = 200 meV) which we attributed to defects in the CdS layer
Impact of the selenisation temperature on the structural and optical properties of CZTSe absorbers
We present structural and optical spectroscopy studies of thin films of Cu2ZnSnSe4 (CZTSe) with strong copper deficiency deposited on Mo/Glass substrates and selenised at 450, 500 or 550 °C. Solar cells fabricated from these films demonstrated efficiencies up to 7.4% for selenisation at 500 °C. Structural analysis based on X-ray diffraction and Raman spectroscopy revealed the presence of SnSe2 in the film selenised at 450 °C but not detected in the films selenised at higher temperatures. A progressive decrease of the Sn and Se content was observed as the selenisation temperature increased. Photoluminescence excitation was used to determine the bandgaps at 4.2 K. Detailed measurements of the temperature and excitation intensity dependencies of the photoluminescence spectra allow the recombination mechanisms of the observed emission bands to be identified as band-to-impurity and band-to-band transitions, and their evolution with selenisation temperature changes to be analysed. The strongest band-to-band transition is recorded in the PL spectra of the film selenised at 500 °C and can be observed from 6 K to room temperature. The compositional and structural changes in the films and their influence on the optoelectronic properties of CZTSe and solar cells are discussed
Stimulated emission and optical properties of solid solutions of Cu(In,Ga)Se2 direct band gap semiconductors
Stimulated emission, optical properties, and structural characteristics of non-irradiated and proton-irradiated Cu(In,Ga)Se2 thin films deposited on soda lime glass substrates using co-evaporation of elements in a multistage process were investigated. X-ray diffraction analysis, scanning electron microscopy, X-ray spectral analysis with energy dispersion, low-temperature photoluminescence, optical transmittance and reflectance were used to study the films. Stimulated emission at low temperatures of ~20 K was found in non-irradiated and proton-irradiated Cu(In,Ga)Se2 thin films upon excitation by laser pulses of nanosecond duration with a threshold power density of ~20 kW/cm2. It was shown that the appearance and parameters of the stimulated emission depend strongly on the concentration of ion-induced defects in Cu(In,Ga)Se2 thin films
Photoluminescence, Stimulated and Laser Emission in CuInSe2crystals
Excitonic quality CuInSe2 crystals were studied using low-temperature (10 K) photoluminescence (PL) excited by continuous wave and nanosecond pulsed lasers at power densities from 0.01 to 76 kW/cm2. Increasing the excitation power density level to 26 kW/cm2 resulted in the appearance of a stimulated emission SE-band in the PL spectra at 1.035 eV. Further increase in the excitation level to 39 kW/cm2 generated on the top of the SE band, a structure of equidistant sharp lines attributed to laser emission. © 2021 Author(s).This work was supported by State Program of Scientific Research of the Republic of Belarus “Physical Material Science, New Materials and Technologies” (Project No. 1.4.4) and Belarusian Republican Foundation of Basic Research (Grant No. F20M-058). The research was carried out within the state assignment of Ministry of Science and Higher Education of the Russian Federation (“Spin” No. AAAA-A18-118020290104-2)
Influence of the copper content on the optical properties of CZTSe thin films
We present an optical spectroscopy study of Cu2ZnSnSe4 (CZTSe) thin films deposited on Mo/glass substrates. The [Cu]/[Zn+Sn] ratio in these films varies from nearly stoichiometric to strongly Cu deficient and Zn rich. Increasing Cu deficiency and Zn excess widens the bandgap Eg, determined using photoluminescence excitation (PLE) at 4.2 K, from 0.99 eV to 1.03 eV and blue shifts the dominant band in the photoluminescence (PL) spectra from 0.83 eV to 0.95 eV. The PL spectra of the near stoichiometric film reveal two bands: a dominant band centred at 0.83 eV and a lower intensity one at 0.93 eV. The temperature and excitation intensity dependence of the PL spectra help to identify the recombination mechanisms of the observed emission bands as free-to-bound: recombination of free electrons with holes localised at acceptors affected by randomly distributed potential fluctuations. Both the mean depth of such fluctuations, determined by analysing the shape of the dominant bands, and the broadening energy, estimated from the PLE spectra, become smaller with increasing Cu deficiency and Zn excess which also widens Eg due to an improved ordering of the Cu/Zn atoms. These changes in the elemental composition induce a significant blue shift of the PL bands exceeding the Eg widening. This is attributed to a change of the dominant acceptor for a shallow one, and is beneficial for the solar cell performance. Film regions with a higher degree of Cu/Zn ordering are present in the near stoichiometric film generating the second PL band at 0.93 eV
Спонтанное, стимулированное излучение и лазерная генерация в кристаллах и тонких пленках CuInSe2
Представлены результаты исследования спектров излучения кристаллов и тонких пленок CuInSe2 при непрерывном (2 Вт/см2) и наносекундном импульсном лазерном возбуждении в диапазоне плотности мощности возбуждения ~1–100 кВт/см2 и температурах 10–160 К. Обнаружено, что в кристаллах CuInSe2 стимулированное излучение возникает в спектральной области 1,033 эВ с минимальным уровнем пороговой накачки 9,8 кВт/см2, а при уровнях накачки 36–76 кВт/см2 наблюдается лазерное излучение. Установлено, что для тонких пленок CuInSe2, сформированных на стеклянных подложках с предварительно осажденным на стекло слоем молибдена (структура CuInSe2/Mo/стекло), характерно появление только стимулированного излучения в области энергий 1,014–1,097 эВ с минимальным уровнем пороговой накачки 30 кВт/см2 при температуре 10 К. Обсуждаются механизмы возникновения стимулированного и лазерного излучения в соединении CuInSe2.Представлены результаты исследования спектров излучения кристаллов и тонких пленок CuInSe2 при непрерывном (2 Вт/см2) и наносекундном импульсном лазерном возбуждении в диапазоне плотности мощности возбуждения ~1–100 кВт/см2 и температурах 10–160 К. Обнаружено, что в кристаллах CuInSe2 стимулированное излучение возникает в спектральной области 1,033 эВ с минимальным уровнем пороговой накачки 9,8 кВт/см2, а при уровнях накачки 36–76 кВт/см2 наблюдается лазерное излучение. Установлено, что для тонких пленок CuInSe2, сформированных на стеклянных подложках с предварительно осажденным на стекло слоем молибдена (структура CuInSe2/Mo/стекло), характерно появление только стимулированного излучения в области энергий 1,014–1,097 эВ с минимальным уровнем пороговой накачки 30 кВт/см2 при температуре 10 К. Обсуждаются механизмы возникновения стимулированного и лазерного излучения в соединении CuInSe2
Photoluminescence, stimulated and laser emission in CuInSe2 crystals
Excitonic quality CuInSe2 crystals were studied using low-temperature (10 K) photoluminescence (PL) excited by continuous wave and nanosecond pulsed lasers at power densities from 0.01 kW/cm2 to 76 kW/cm2 . Increasing the excitation power density level to 26 kW/cm2 resulted in the appearance of a stimulated emission SE-band in the PL spectra at 1.035 eV. Further increase in the excitation level to 39 kW/cm2 generated on the top of the SE band a structure of equidistant sharp lines attributed to laser emission. at 1.035 eV. Further increase in the excitation level to 39 kW/cm2 generated a structure of equidistant sharp lines attributed to laser emission on the top of the SE band. The lasing regime suggests the presence of volumes with parallel faces (microcracks or grain boundaries), which act as laser mirrors within the CuInSe2 crystals