Effect of ZnO on Cu/ZnO/Al_2O_3 catalysts for methanol synthesis

[中文文摘]用高速碰撞共沉淀法制备m(CuO) /m(ZnO) /m(Al2 O3 )比分别为 60 /3 0 /1 0和 3 0 /60 /1 0的 1 #和 2 #催化剂 ,结果表明高ZnO的 2 #催化剂活性较好 ,分散度较大。XPS测试表明 2 #催化剂表面ZnO吸附的中间体 (CHx 或CHxO)较多且表面的Cu+1浓度较高 ,从而促进CO加氢合成甲醇的活性。[英文文摘]Cu/ZnO/Al_2O_3 catalysts with ratios of 60/30/10 and 30/60/10 have been prepared by high speed collision coprecipitation method. The performance of the catalyst with the higher ZnO content shows the higher activity in methanol synthesis. The characterization results indicated that the catalyst with the higher ZnO content has higher dispersion. On the surface of the higher ZnO content catalyst, there was more Cu+1 and more intermediate (CH_x and CH_xO) adsorpted. It is beneficial for the CO hydrogenating to produce methanol

高速碰撞共沉淀法铜基甲醇合成催化剂的研制

开发出高速碰撞共沉淀制备铜基甲醇催化剂的新方法。用此法一步共沉淀制得的ｂ 催化剂，其分散度和催化剂表面单位Ｃｕ 原子的ＣＯ 转化数比ｅ 催化剂分别增加２０％ 和１４ ％ 。在催化剂Ｃｕ 质量分数减少３７％ 的情况下，其催化剂活性仍相当高，因此这是一种值得推广应用的催化剂制备新方法

令和6年度 心理学系卒業論文概要

校則に基づく髪色・髪型の対人印象(荒木美空), 日常生活における服装が印象形成に及ぼす影響 : 男性服の服装特徴という観点から(油谷健心), 大学生における過剰適応と共感性，抑うつとの関連(小池奈々), 制御適合における適切感は課題遂行パフォーマンスを調整するか(小林拓翔), 音楽イベント参加と主観的幸福感の関係 : 音楽イベント参加の社会的要素に着目して(酒井菜月音), 採用面接での複数観衆問題における自己呈示(柴田実怜), 後悔感情と認知的感情制御方略および準備機能との関連 : 後悔感情の強度に着目して(高沢穂), 懸念的被透視感の喚起が非言語的反応・言語内容・印象に与える影響 : 対面状況とビデオ会議システム場面の比較検討(橋本采奈), 関係性の違いが自己動機付けに与える影響 : 自尊感情の観点から(前澤享一), 職場いじめの加害傾向に関連する要因の検討(西川櫻), オンラインゲームの利用が社会的スキルに及ぼす影響 : ゲームの種類・利用動機に着目して(尾畑朋香), 反すうとコーピングの関連 : 大学受験直前場面に着目した検討(川角茉凜), 青年のInstagram 依存傾向と心理的問題の関連 : 利用動機の媒介効果(小池日向子), 自己認知が対人認知を介して新入成員の組織コミットメントに及ぼす効果 : 椅子の柔らかさ・硬さが認知に与える影響を考慮する(高柳陽), 大学生の友人グループにおける攻撃的ユーモアが関係満足度を介してグループのコミットメントに与える影響 : 内集団・外集団に着目して(石川晴己), 方言の使用と聴者の出身地が共感喚起に及ぼす影響 : 熊本方言に着目した検討(上村彩紀), 防衛的悲観主義と抑うつの関連 : 曖昧さへの耐性の影響を踏まえて(後藤祐奏), 自己奉仕的な自己卑下呈示と過敏型自己愛および自己不全感の関連(鈴木梨音), 大学生の抑うつとソーシャルスキル・親友に対する居場所感の関連(高木美和), 悩み体験と大学生の援助要請スタイルの関連(建部史香), 作り笑いが送り手の感情や関係性の捉え方に与える影響(鳥羽凜々子), 親への愛着と援助要請行動の利益・コスト予測の関連 : 恋人の応答性認知の調整効果に着目して(中川寛子), 自己開示レベル : 自己開示欲求レベル間のずれと友人関係満足度の関連(林香穂), 青年期における夫婦間葛藤の認知と抑うつの関連に対する情緒的自律性の調整効果(平井里実), 大学生の社会的迷惑行為と親と友人への愛着スタイルとの関連性の検討 : 社会的絆理論の愛着に着目して(廣部よしの), 青年期における家庭での食事状況と両親に対する愛着の関連(松下睦), 単純接触効果の般化によるボーカルメロディの印象評価の検討(松永大毅), 高校3 年生における親からの期待認知と抑うつおよび完全主義の関連 : 進学・学業期待に着目して(宮田菜月), 認知的再解釈はミスを過度に気にする傾向が適応に与える影響を緩和するか : 主観的・心理学的幸福感と抑うつ傾向に着目して(山腰香奈), 職場いじめの被害者が加害者化するとは : 自尊感情と仮想的有能感に着目して(神村純香), 高校時代の進路決定自己効力感と大学生活の自立および適応との関連(原田笑花), 中学生の友人関係における機能的アサーションと学校適応感の関連について : 学級風土の影響に着目して(蒔田ゆり)departmental bulletin pape

Synthesis of 1-(4-(n-heptoxy) butyl) hexahydro-2H-azepin-2-one

1-（4-正庚氧基）丁基己内酰胺1可由正庚醇与1，4-二卤代丁烷反应后，再与己内酰胺反应制得。每步均在混合无机碱kOH/k2CO3（作为碱性试剂）和季铵盐（作为固-液相转移催化剂）存在下进行反应。This paper reports the sequential reactions of nheptyl alcohol with 1,4-dihalobutane, and then with 4-caprolactam in two steps of solid-liquid phase transFer catalytic reaction to the title compound 1

Promoting EFFect of Mn in the Cu Mn/Al 2O 3 Catalysts For Synthesis of Methanol

甲醇合成催化剂Cu-Mn/Al2O3中锰的助催化作用李基涛张伟德高利珍（厦门大学化学系物理化学研究所厦门361005）林建毅陈华毅k.l.TAn（国立新加坡大学物理系0511）关键词甲醇合成Mn的助催化作用活性表面态铜催化剂分类号O643.32甲醇是...Cu Mn/Al 2O 3 impregnation catalysts were studied with respect to their catalytic activity in the synthesis of methanol.Moreover, TPR, XPS and N 2O decomposition were used For the characterization of catalysts.The experimental results indicated that copper not only was present on the support but also interacted with MnO.Cu(Ⅰ)was Found on the surFace of the catalysts aFter reduction and reaction.The valence of Mn was increased aFter reaction.ThereFore, partial positive charge was obtained by surFace copper through oxygen bridge of Cu…O-Mn.So the capacity of adsorbing CO and H 2 was enhanced on the catalysts.The synthesis of methanol was promoted as a result.福建省自然科学基金;固体表面物理化学国家重点实验室资

A Study of Cu-Mn/SiO_2 Catalysts For Methanol Synthesis

对浸渍法制备的Cu-Mn/SIO2催化剂进行了甲醇合成的活性评价，同时用XPS、AuSEr、n2O分解，TPr等技术对催化剂进行了表征.结果表明，在双组份催化剂中，工作态催化剂表面主要存在Cu（O）.催化反应可能通过Cu…O-Mn氧桥的长程诱导交换作用，使Cu带部分正电荷，这有利于CO与H2的吸附和活化，从而提高甲醇合成的收率.Cu-Mn/SiO, impregnation catalysts were studied with respect to their catalytic activity in the synthesis of methanol.Moreover, the means of XPS, Auger, TPR and decomposition of N2O were also used to characterize the catalysts.The experimental results show that Cu (O) mostly existed on the working surFace of the catalysts.The catalytic reaction was promoted by Cu with part of positive charges which was Formed by means of long path exchange Function between Cu...O-Mn.ThereFore, this was Favourable For adsorbing and activating CO and H2 on the surFace of catalysts and For promoting methanol synthesis.福建省自然科学基金;固体表面物理化学国家重点实验室资

液體加熱裝置

M525349TWN2B67C-003/26(2006.01)105203905[[abstract]]本創作係提供一種液體加熱裝置。包括半球形的盛水杯，盛水杯裡面設有螺旋形加熱管道，加熱管道的上端開口在盛水杯的上方，加熱管道的底端穿過盛水杯的底部，加熱管道的開口設置有漏斗，加熱管道底端設有閥門。本裝置的加熱管道導熱性能很好，能快速將熱水的熱量傳向待加熱液體，加熱時間短，加熱效率非常高。[[notice]]補正完

胶原涂层对3D打印种植体表面生物相容性的影响

背景:金属等惰性生物材料存在生物相容性差、组织结合力弱等问题,从而导致种植牙或骨植入物的使用效果较差。因此,如何增强惰性生物材料的生物相容性成为了近几年的研究热点。目的:对钛合金材料进行胶原覆层并评价其生物相容性。方法:以钛合金片(Ti6Al4V)为基质,Ⅰ型胶原和Ⅱ型胶原为覆层材料,3-氨基丙基三乙氧基硅烷(KH550)为偶联剂,对基于3D打印的钛合金片进行胶原覆层。将覆层材料用于小鼠前成骨细胞(MC-3T3-E1)培养,通过细胞培养效果评价其生物相容性,并通过细胞蛋白差异性识别比较不同类型胶原对细胞分化的影响。结果与结论:(1)当钛合金片(&Phi;10 cm)表面含氮量为8.41%时,Ⅰ型胶原覆层量为0.81 mg,Ⅱ型胶原覆层量为0.77 mg;(2)与空白钛合金片相比,经胶原覆层后的钛合金片细胞贴附状态更好,铺展面积更大,且细胞增殖速率更快,活性更强;(3)Ⅰ型胶原覆层材料培养的细胞多表达与基质合成有关的蛋白,而Ⅱ型胶原覆层材料培养的细胞多表达与矿化及钙盐沉积有关的蛋白;(4)结果表明,胶原覆层可提高钛合金材料的生物相容性,且不同胶原类型可影响细胞表达不同功能性蛋白。</p