Combining 2D organic and 1D inorganic nanoblocks to develop free-standing hybrid nanomembranes for conformable biosensors

We report a simple approach to fabricate free-standing perforated 2D nanomembranes hosting well-ordered 1D metallic nanostructures to obtain hybrid materials with nanostructured surfaces for flexible electronics. Nanomembranes are formed by alternatively depositing perforated poly(lactic acid) (PLA) and poly(3,4-ethylenedioxythiophene) layers. Copper metallic nanowires (NWs) were incorporated into the nanoperforations of the top PLA layer by electrodeposition and further coated with silver via a transmetallation reaction. The combination of 2D polymeric nanomembranes and aligned 1D metallic NWs allows merging the flexibility and conformability of the ultrathin soft polymeric nanomembranes with the good electrical properties of metals for biointegrated electronic devices. Thus, we were able to tailor the nanomembrane surface chemistry as it was corroborated by SEM, EDX, XPS, CV, EIS and contact angle. The obtained hybrid nanomembranes were flexible and conformable showing sensing capacity towards H2O2 with good linear concentration range (0.35–10 mM), sensitivity (120 µA cm?2 mM?1) and limit of detection (7 ?m). Moreover, the membranes showed good stability, reproducibility and selectivity towards H2O2

Over 10% efficient wide bandgap CIGSe solar cells on transparent substrate with Na predeposition treatment

With the recent rise of new photovoltaic applications, it has become necessary to develop specific optoelectronic properties for thin‐film technologies such as Cu(In,Ga)Se2 and to take advantage of their high degree of tunability. The feasibility of efficient wide bandgap absorbers on transparent conductive oxide substrates is, in that context, of critical importance. Using an original approach based on a predeposition sodium treatment, Cu(In,Ga)Se2 absorbers fabricated by sputtering and reactive annealing with a Ga to (Ga + In) content over 0.7 and an optical bandgap above 1.4 eV are deposited on transparent fluorine‐doped tin oxide films, with the insertion of an ultrathin MoSe2 layer preserving the contact's ohmicity. Different material characterizations are carried out, and a thorough Raman analysis of the absorber reveals that the sodium pretreatment significantly enhances the Ga incorporation into the chalcopyrite matrix, along with markedly improving the film's morphology and crystalline quality. This translates to a spectacular boost of the photovoltaic performance for the resulting solar cell as compared with a reference device without Na, specifically in the voltage and fill factor. Eventually, an efficiency exceeding 10% is obtained without antireflection coating, a record value bridging the gap with the state of the art on nontransparent substrates

Electrodéposition d'alliages zinc-manganèse en milieu alcalin

LA ROCHELLE-BU (173002101) / SudocSudocFranceF

Transition-Metal Oxides for Kesterite Solar Cells Developed on Transparent Substrates

This document is the unedited Author’s version of a Submitted Work that was subsequently accepted for publication in Transition-Metal Oxides for Kesterite Solar Cells Developed on Transparent Substrates, copyright © American Chemical Society after peer review. To access the final edited and published work see https://pubs.acs.org/doi/10.1021/acsami.0c06992Fabrication on transparent soda-lime glass/fluorine-doped tin oxide (FTO) substrates opens the way to advanced applications for kesterite solar cells such as semitransparent, bifacial, and tandem devices, which are key to the future of the PV market. However, the complex behavior of the p-kesterite/n-FTO back-interface potentially limits the power conversion efficiency of such devices. Overcoming this issue requires careful interface engineering. This work empirically explores the use of transition-metal oxides (TMOs) and Mo-based nanolayers to improve the back-interface of Cu2ZnSnSe4, Cu2ZnSnS4, and Cu2ZnSn(S,Se)4 solar cells fabricated on transparent glass/FTO substrates. Although the use of TMOs alone is found to be highly detrimental to the devices inducing complex current-blocking behaviors, the use of Mo:Na nanolayers and their combination with n-type TMOs TiO2 and V2O5 are shown to be a very promising strategy to improve the limited performance of kesterite devices fabricated on transparent substrates. The optoelectronic, morphological, structural, and in-depth compositional characterization performed on the devices suggests that the improvements observed are related to a combination of shunt insulation and recombination reduction. This way, record efficiencies of 6.1, 6.2, and 7.9% are obtained for Cu2ZnSnSe4, Cu2ZnSnS4, and Cu2ZnSn(S,Se)4 devices, respectively, giving proof of the potential of TMOs for the development of kesterite solar cells on transparent substrates.This research was supported by the H2020 Programme under the project INFINITE-CELL (H2020-MSCA-RISE-2017-777968), by the Ministry of Science and Innovation of Spain under IGNITE project (ENE2017-87671-C3-1-R), by the European Regional Development Funds (ERDF, FEDER Programa Competitivitat de Catalunya 2007–2013) and CERCA Programme / Generalitat de Catalunya. Authors from IREC belong to the SEMS (Solar Energy Materials and Systems) Consolidated Research Group of the “Generalitat de Catalunya” (Ref. 2017 SGR 862)Peer ReviewedPostprint (author's final draft