Prediction of thermal cycling induced matrix cracking

Thermal fatigue has been observed to cause matrix cracking in laminated composite materials. A method is presented to predict transverse matrix cracks in composite laminates subjected to cyclic thermal load. Shear lag stress approximations and a simple energy-based fracture criteria are used to predict crack densities as a function of temperature. Prediction of crack densities as a function of thermal cycling is accomplished by assuming that fatigue degrades the material's inherent resistance to cracking. The method is implemented as a computer program. A simple experiment provides data on progressive cracking of a laminate with decreasing temperature. Existing data on thermal fatigue is also used. Correlations of the analytical predictions to the data are very good. A parametric study using the analytical method is presented which provides insight into material behavior under cyclical thermal loads

Introduction to MATE-CON

Presentation on MATE-CO

Value Stream Analysis and Mapping for Product Development

This paper explores the concept of Value Stream Analysis and Mapping (VSA/M) as applied to Product Development (PD) efforts. Value Stream Analysis and Mapping is a method of business process improvement. The application of VSA/M began in the manufacturing community. PD efforts provide a different setting for the use of VSA/M. Site visits were made to nine major U.S. aerospace organizations. Interviews, discussions, and participatory events were used to gather data on (1) the sophistication of the tools used in PD process improvement efforts, (2) the lean context of the use of the tools, and (3) success of the efforts. It was found that all three factors were strongly correlated, suggesting success depends on both good tools and lean context. Finally, a general VSA/M method for PD activities is proposed. The method uses modified process mapping tools to analyze and improve process

Output from the 1998 Product Development Value Stream Workshop: A Framework for Understanding Information Flow in the Product Development Process

The descriptions below and the attached diagrams are outputs of the 1998 LAI Product Development Focus Team workshop on the Value Chain in Product Development. A working group at that workshop was asked to model the product development process: in terms of the phases of product development and their interfaces, boundaries and outputs. Their work has proven to be generally useful to LAI researchers and industry members, and so is formalized here

Value Stream Analysis and Mapping for Product Development

This paper explores the concept of Value Stream Analysis and Mapping (VSA/M) as applied to Product Development (PD) efforts. Value Stream Analysis and Mapping is a method of business process improvement. The application of VSA/M began in the manufacturing community. PD efforts provide a different setting for the use of VSA/M. Site visits were made to nine major U.S. aerospace organizations. Interviews, discussions, and participatory events were used to gather data on (1) the sophistication of the tools used in PD process improvement efforts, (2) the lean context of the use of the tools, and (3) success of the efforts. It was found that all three factors were strongly correlated, suggesting success depends on both good tools and lean context. Finally, a general VSA/M method for PD activities is proposed. The method uses modified process mapping tools to analyze and improve process

Lean Enterprise Product Development (LEPD) Simulation

LEPD Simulation slid

Prediction of thermal cycling induced cracking in polymer matrix composites

This report summarizes the work done in the period February 1993 through July 1993 on the 'Prediction of Thermal Cycling Induced Cracking In Polymer Matrix Composites' program. An oral presentation of this work was given to Langley personnel in September of 1993. This document was prepared for archival purposes. Progress studies have been performed on the effects of spatial variations in material strength. Qualitative agreement was found with observed patterns of crack distribution. These results were presented to NASA Langley personnel in November 1992. The analytical methodology developed by Prof. McManus in the summer of 1992 (under an ASEE fellowship) has been generalized. A method for predicting matrix cracking due to decreasing temperatures and/or thermal cycling in all plies of an arbitrary laminate has been implemented as a computer code. The code also predicts changes in properties due to the cracking. Experimental progressive cracking studies on a variety of laminates were carried out at Langley Research Center. Results were correlated to predictions using the new methods. Results were initially mixed. This motivated an exploration of the configuration of cracks within laminates. A crack configuration study was carried out by cutting and/or sanding specimens in order to examine the distribution of cracks within the specimens. These investigations were supplemented by dye-penetrant enhanced X-ray photographs. The behavior of thin plies was found to be different from the behavior of thicker plies (or ply groups) on which existing theories are based. Significant edge effects were also noted, which caused the traditional metric of microcracking (count of cracks on a polished edge) to be very inaccurate in some cases. With edge and configuration taken into account, rough agreement with predictions was achieved. All results to date were reviewed with NASA Langley personnel in September 1993

Modeling of outgassing and matrix decomposition in carbon-phenolic composites

A new release rate equation to model the phase change of water to steam in composite materials was derived from the theory of molecular diffusion and equilibrium moisture concentration. The new model is dependent on internal pressure, the microstructure of the voids and channels in the composite materials, and the diffusion properties of the matrix material. Hence, it is more fundamental and accurate than the empirical Arrhenius rate equation currently in use. The model was mathematically formalized and integrated into the thermostructural analysis code CHAR. Parametric studies on variation of several parameters have been done. Comparisons to Arrhenius and straight-line models show that the new model produces physically realistic results under all conditions

Modeling of outgassing and matrix decomposition in carbon-phenolic composites

Work done in the period Jan. - June 1994 is summarized. Two threads of research have been followed. First, the thermodynamics approach was used to model the chemical and mechanical responses of composites exposed to high temperatures. The thermodynamics approach lends itself easily to the usage of variational principles. This thermodynamic-variational approach has been applied to the transpiration cooling problem. The second thread is the development of a better algorithm to solve the governing equations resulting from the modeling. Explicit finite difference method is explored for solving the governing nonlinear, partial differential equations. The method allows detailed material models to be included and solution on massively parallel supercomputers. To demonstrate the feasibility of the explicit scheme in solving nonlinear partial differential equations, a transpiration cooling problem was solved. Some interesting transient behaviors were captured such as stress waves and small spatial oscillations of transient pressure distribution