Fundamental studies on dynamic wear behavior of SBR rubber compounds modified by SBR rubber powder

The aim of this study is focused on the experimental investigation of dynamic wear behavior of carbon black filled rubber compounds comprising pristine styrene butadiene rubber (SBR) together with incorporated SBR ground rubber (rubber powder). We also analyzed and described quantitatively the service conditions of some dynamically loaded rubber products, which are liable to wear (e.g. conveyor belts, tires). Beside the well-known standard test method to characterize wear resistance at steady-state conditions, we used an own developed testing equipment based on gravimetric determination of mass loss of rubber test specimen to investigate the influence of rubber powder content on dynamic wear depending on varying impact energy levels. Incorporation of SBR rubber powder in SBR rubber compounds increases wear. With increasing rubber powder content the wear at steady-state conditions progressively increases. However, the level of wear at dynamic loading conditions increases only once, but stays constant subsequently even with contents of incorporated rubber powder

Charakterisierung des Deformations- und Versagensverhaltens von Elastomeren unter querdehnungsbehinderter Zugbelastung

Das Deformations- und Versagensverhalten von Elastomeren wird maßgeblich von der rezepturspezifischen Zusammensetzung und den wirkenden Belastungsbedingungen beeinflusst. Untersuchungen zum Einfluss spezifischer Belastungsparameter, wie Deformationsgeschwindigkeit oder Belastungsszenario (statisch oder zyklisch, Zug oder Druck sowie Schub), auf das mechanische Verhalten von Elastomeren sind grundlegend für die technische Auslegung von Elastomerprodukten. Zur Beschreibung des Versagensverhaltens von Elastomeren unter zyklischer oder dynamischer Belastung sind bruchmechanische Konzepte in Industrie und Forschung bereits etabliert. Dabei basiert die Analyse des bruchmechanischen Verhaltens von Elastomeren meist auf makroskopischen Eigenschaften, obwohl (sub-) mikrostrukturelle Änderungen und Schädigungen erheblichen Einfluss haben wer-den. Ein spezifisches Phänomen mikrostruktureller Schädigung ist die Kavitation unter querdehnungsbehinderter Zugbelastung. Infolge geometrischer Zwangsbedingungen und einer dadurch eingeschränkten Kontrahierbarkeit, kann sich bei Zugbelastung ein mehrachsiger Spannungszustand einstellen. Infolge dessen können sich Defekte, sogenannte Kavitäten, bilden. Diese Kavitäten wachsen bei zunehmender äußerer Belastung und bauen dadurch die Zwangsbedingungen sowie die inneren Spannungen ab. Das Wissen über den Kavitationsprozess bei Elastomeren ist grundlegend für das Verständnis des makroskopischen Versagensverhaltens, doch bislang nur eingeschränkt vorhanden. In dieser Arbeit wurden Methoden für in situ Experimente, wie Dilatometrie und Mikrotomographie, entwickelt und optimiert. Dadurch konnte die Kavitation in Elastomeren umfassend untersucht und der Schädigungsverlauf mit aussagekräftigen Kennwerten beschrieben werden. Verschiedene Einflussfaktoren, wie Netzwerkeigenschaften und Füllstoffverstärkung, wurden ebenso beleuchtet wie der Einfluss von geometrischen Zwangsbedingungen. Für die Experimente wurden spezielle Prüfkörper verwendet, die durch ein ausgeprägtes Geometrieverhältnis gekennzeichnet sind. Sogenannte Pancake-Prüfkörper sind dünne scheibenförmige Zylinderproben, die zwischen steifen Probenhaltern verklebt werden. Sowohl an ungefüllten als auch rußverstärkten Elastomeren auf Basis von Styrol-Butadien-Kautschuk (SBR) konnte die Charakterisierung des Beginns der Kavitation, insbesondere dank hochauflösender Messtechnik, gelingen. Neben einem spannungsbasierten konnte auch ein energiebasiertes Kavitationskriterium definiert werden. In jedem Fall zeigten die Ergebnisse, dass die traditionellen Vorhersagen den werkstoffimmanenten Widerstand gegen Kavitation deutlich überschätzen. Entgegen der oft getroffenen Annahme, dass Kavitation ausschließlich infolge eines Grenzflächenversagens zwischen weicher Elastomermatrix und steifen Füllstoffpartikeln auftritt, konnte gezeigt werden, dass dieses Schädigungsphänomen auch bei ungefüllten Elastomeren auftreten kann. Des Weiteren wurde das Phänomen Kavitation mittels Kleinwinkel-Röntgenstreuung auch an gekerbten Flach-Prüfkörpern untersucht. Dabei konnten Kavitäten entlang der Rissfronten nachgewiesen werden. Im Zusammenhang von Kavitation und bruchmechanischem Verhalten konnte auch eine Korrelation zwischen Beginn der Kavitation und makroskopischer Rissinitiierung gefunden werden. Dies deutet zum einen darauf hin, dass die Kavitation durch bruchmechanische Vorgänge, wie Kettenbruch, bestimmt wird und zum anderen, dass die Kavitation das makroskopische Versagensverhalten beeinflusst. Weiterhin konnte sowohl mittels numerischer Berechnungen als auch anhand experimenteller Daten gezeigt werden, dass infolge geometrischer oder struktureller Zwangsbedingungen, entgegen der allgemeinen Annahme, für Elastomere nicht ausschließlich von inkompressiblem Deformationsverhalten ausgegangen werden sollte. Die vorgestellten experimentellen Methoden zur Charakterisierung der Kavitation in Elastomeren sind geeignet, um in weiteren Studien die Bestimmung z.B. von dynamisch-bruchmechanischen Eigenschaften unter Berücksichtigung mikrostruktureller Schädigung für verschiedene Elastomere zu untersuchen.:1 EINLEITUNG UND ZIELSTELLUNG 2 STAND DER FORSCHUNG ZUM DEFORMATIONS- UND VERSAGENSVERHALTEN VON ELASTOMEREN 2.1 GRUNDLAGEN ZUR KAUTSCHUKMISCHUNGSHERSTELLUNG UND -VERARBEITUNG 2.2 TYPISCHE MERKMALE DES PHYSIKALISCH-MECHANISCHEN EIGENSCHAFTSPROFILS VON ELASTOMEREN 2.3 CHARAKTERISIERUNG DES MECHANISCHEN UND BRUCHMECHANISCHEN VERHALTENS VON ELASTOMEREN 2.4 ANALYSE DES VERSAGENSVERHALTENS VON ELASTOMEREN INFOLGE QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 2.5 ABLEITUNG VON UNTERSUCHUNGSANSÄTZEN ZUR CHARAKTERISIERUNG UND BESCHREIBUNG DER KAVITATION IN ELASTOMEREN 3 VORBETRACHTUNGEN ZUM DEFORMATIONSVERHALTEN VON ELASTOMEREN 3.1 ALLGEMEINE GRUNDLAGEN 3.2 DEFORMATIONSVERHALTEN VON ELASTOMEREN UNTER KOMPLEXEN BELASTUNGSZUSTÄNDEN 3.3 FE-ANALYSE ZUR CHARAKTERISIERUNG DES DEFORMATIONSVERHALTENS VON PANCAKE-PRÜFKÖRPERN 4 EXPERIMENTELLES 4.1 WERKSTOFFE 4.2 PRÜFKÖRPER 4.3 KONVENTIONELLE CHARAKTERISIERUNG DER ELASTOMERE 4.4 OBERFLÄCHENANALYSE 4.5 IN SITU DILATOMETRIE AN PANCAKE-PRÜFKÖRPERN 4.6 IN SITU RÖNTGEN-MIKROTOMOGRAPHIE AN PANCAKE-PRÜFKÖRPERN 4.7 IN SITU KLEINWINKEL-RÖNTGENSTREUUNG AN GEKERBTEN FLACH-PRÜFKÖRPERN 4.8 ERMITTLUNG DES WERKSTOFFIMMANENTEN MAKROSKOPISCHEN WIDERSTANDS GEGEN RISSINITIIERUNG AN FLACH-PRÜFKÖRPERN 5 ERGEBNISSE UND DISKUSSION 5.1 PHYSIKALISCH-MECHANISCHE EIGENSCHAFTEN 5.2 DEFORMATIONS- UND VERSAGENSVERLAUF VON UNGEFÜLLTEN ELASTOMEREN UNTER QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 5.2.1 Typische Verlaufsform der Kavitation und grundlegende Erkenntnisse 5.2.2 Beginn der Kavitation – Besonderheiten bei kleinen Dehnungen 5.2.3 Ursprung der Kavitation – Nukleierung und Bildung von Kavitäten 5.2.4 Fortschreitende Kavitation – Besonderheiten bei hohen Dehnungen 5.3 EINFLUSS TYPISCHER MISCHUNGSBESTANDTEILE AUF DEN DEFORMATIONS- UND VERSAGENSVERLAUF UNTER QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 5.3.1 Unterschiedliche Netzwerkeigenschaften durch Variation von Schwefel- und ZnO-Anteilen 5.3.2 Einfluss des Verstärkungseffekts durch Variation des Rußanteils 5.4 EINFLUSS GEOMETRISCHER ZWANGSBEDINGUNGEN AUF DEN DEFORMATIONS- UND VERSAGENSVERLAUF UNTER QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 5.4.1 Variation des Geometriefaktors von Pancake-Prüfkörpern ungefüllter Elastomere 5.4.2 Ermittlung einer effektiven Querkontraktionszahl als Maß der Kompressibilität des Deformationsverhaltens 5.4.3 Kavitation in der Rissprozesszone gekerbter Flach-Prüfkörper 5.5 BEWERTUNG DER KRITERIEN ZUR CHARAKTERISIERUNG DES BEGINNS DER KAVITATION 5.5.1 Diskussion zur Bestimmung eines spannungsbasierten sowie eines energiebasierten Kavitationskriteriums 5.5.2 Vergleich des energiebasierten Kavitationskriteriums mit dem werkstoffimmanenten Widerstands gegen Rissinitiierung 6 ZUSAMMENFASSUNG 6.1 ÜBERBLICK ZU GEWONNENEN ERKENNTNISSEN 6.2 AUSBLICK 6.3 PRAKTISCHE RELEVANZ LITERATURVERZEICHNIS BILDVERZEICHNIS TABELLENVERZEICHNIS ANHANG PUBLIKATIONSLISTEThe deformation and failure behavior of rubbers is significantly influenced by the chemical composition and loading conditions. Investigations on how loading parameters, such as strain rate or type of loading, e.g. quasi-static vs. cyclic or tension vs. compression, affect the mechanical behavior of rubbers are elementary for designing elastomeric products. Some fracture mechanical concepts describing the failure behavior of rubbers are widely accepted in industrial and academic research Although structural changes on the network scale may affect the mechanical properties of rubbers, the most common failure analyses are based on macroscopic approaches not considering microscopic damage. A specific phenomenon in (micro-) structural failure is cavitation due to strain constraints. Under geometrical constraints, the lateral contraction is suppressed. As a result, stress triaxiality causes inhomogeneous, nonaffine deformation and internal defects, so-called cavities, appear. The formation and growth of cavities release stress and reduce the degree of constraints. Although cavitation in rubber has been studied for several decades, the knowledge about the fundamental mechanisms triggering the cavitation process is still very limited. This study aimed to characterize and describe the cavitation process comprehensively using convincing material parameters. Therefore several influencing factors, such as network properties and filler reinforcement, have been considered. Hence, advanced experimental methods, such as dilatometry and microtomography have been used for in situ investigations. Thin disk-shaped rubber samples have been used to prepare pancake specimens, which are characterized by a high aspect ratio. As a result, the degree of stress triaxiality is high and the dominating hydrostatic tensile stress causes the initiation of cavitation. For unfilled and carbon black reinforced styrene-butadiene-rubbers the onset of cavitation was determined precisely by highly sensitive data acquisition. Both, a stress-related and an energy-based cavitation criterion were found indicating that traditional approaches predicting internal failure indeed overestimate the material resistance against cavitation. Of special interest was the often suspected cavitation in unfilled rubbers, because, cavitation in rubbers is mainly attributed to interfacial failure between soft rubber matrix and rigid filler particles. Furthermore, cavitation in the process zone of notched planar specimens could be monitored by in situ X-ray scattering experiments. As a result, cavities appear in a region along the crack front. To understand the correlation between cavitation and macroscopic crack initiation additional tests were realized, i.e. intrinsic strength analysis. The results have shown that the macro failure is affected by microfracture, e.g. growth of cavities, controlled by the breakage of polymer chains. Both, numerical and experimental data indicate that under strain constraints rubbers do not exhibit incompressible deformation behavior. The presented experimental methods to characterize cavitation are suitable for future studies to investigate further aspects of cavitation, e.g. the behavior under dynamic loading, in rubbers or other rubber-like materials.:1 EINLEITUNG UND ZIELSTELLUNG 2 STAND DER FORSCHUNG ZUM DEFORMATIONS- UND VERSAGENSVERHALTEN VON ELASTOMEREN 2.1 GRUNDLAGEN ZUR KAUTSCHUKMISCHUNGSHERSTELLUNG UND -VERARBEITUNG 2.2 TYPISCHE MERKMALE DES PHYSIKALISCH-MECHANISCHEN EIGENSCHAFTSPROFILS VON ELASTOMEREN 2.3 CHARAKTERISIERUNG DES MECHANISCHEN UND BRUCHMECHANISCHEN VERHALTENS VON ELASTOMEREN 2.4 ANALYSE DES VERSAGENSVERHALTENS VON ELASTOMEREN INFOLGE QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 2.5 ABLEITUNG VON UNTERSUCHUNGSANSÄTZEN ZUR CHARAKTERISIERUNG UND BESCHREIBUNG DER KAVITATION IN ELASTOMEREN 3 VORBETRACHTUNGEN ZUM DEFORMATIONSVERHALTEN VON ELASTOMEREN 3.1 ALLGEMEINE GRUNDLAGEN 3.2 DEFORMATIONSVERHALTEN VON ELASTOMEREN UNTER KOMPLEXEN BELASTUNGSZUSTÄNDEN 3.3 FE-ANALYSE ZUR CHARAKTERISIERUNG DES DEFORMATIONSVERHALTENS VON PANCAKE-PRÜFKÖRPERN 4 EXPERIMENTELLES 4.1 WERKSTOFFE 4.2 PRÜFKÖRPER 4.3 KONVENTIONELLE CHARAKTERISIERUNG DER ELASTOMERE 4.4 OBERFLÄCHENANALYSE 4.5 IN SITU DILATOMETRIE AN PANCAKE-PRÜFKÖRPERN 4.6 IN SITU RÖNTGEN-MIKROTOMOGRAPHIE AN PANCAKE-PRÜFKÖRPERN 4.7 IN SITU KLEINWINKEL-RÖNTGENSTREUUNG AN GEKERBTEN FLACH-PRÜFKÖRPERN 4.8 ERMITTLUNG DES WERKSTOFFIMMANENTEN MAKROSKOPISCHEN WIDERSTANDS GEGEN RISSINITIIERUNG AN FLACH-PRÜFKÖRPERN 5 ERGEBNISSE UND DISKUSSION 5.1 PHYSIKALISCH-MECHANISCHE EIGENSCHAFTEN 5.2 DEFORMATIONS- UND VERSAGENSVERLAUF VON UNGEFÜLLTEN ELASTOMEREN UNTER QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 5.2.1 Typische Verlaufsform der Kavitation und grundlegende Erkenntnisse 5.2.2 Beginn der Kavitation – Besonderheiten bei kleinen Dehnungen 5.2.3 Ursprung der Kavitation – Nukleierung und Bildung von Kavitäten 5.2.4 Fortschreitende Kavitation – Besonderheiten bei hohen Dehnungen 5.3 EINFLUSS TYPISCHER MISCHUNGSBESTANDTEILE AUF DEN DEFORMATIONS- UND VERSAGENSVERLAUF UNTER QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 5.3.1 Unterschiedliche Netzwerkeigenschaften durch Variation von Schwefel- und ZnO-Anteilen 5.3.2 Einfluss des Verstärkungseffekts durch Variation des Rußanteils 5.4 EINFLUSS GEOMETRISCHER ZWANGSBEDINGUNGEN AUF DEN DEFORMATIONS- UND VERSAGENSVERLAUF UNTER QUERDEHNUNGSBEHINDERTER ZUGBELASTUNG 5.4.1 Variation des Geometriefaktors von Pancake-Prüfkörpern ungefüllter Elastomere 5.4.2 Ermittlung einer effektiven Querkontraktionszahl als Maß der Kompressibilität des Deformationsverhaltens 5.4.3 Kavitation in der Rissprozesszone gekerbter Flach-Prüfkörper 5.5 BEWERTUNG DER KRITERIEN ZUR CHARAKTERISIERUNG DES BEGINNS DER KAVITATION 5.5.1 Diskussion zur Bestimmung eines spannungsbasierten sowie eines energiebasierten Kavitationskriteriums 5.5.2 Vergleich des energiebasierten Kavitationskriteriums mit dem werkstoffimmanenten Widerstands gegen Rissinitiierung 6 ZUSAMMENFASSUNG 6.1 ÜBERBLICK ZU GEWONNENEN ERKENNTNISSEN 6.2 AUSBLICK 6.3 PRAKTISCHE RELEVANZ LITERATURVERZEICHNIS BILDVERZEICHNIS TABELLENVERZEICHNIS ANHANG PUBLIKATIONSLIST

Charakterisierung des Deformations- und Versagensverhaltens von Elastomerenunter querdehnungsbehinderter Zugbelastung

The deformation and failure behavior of rubbers is significantly influenced by the chemical composition and loading conditions. Investigations on how loading parameters, such as strain rate or type of loading, e.g. quasi-static vs. cyclic or tension vs. compression, affect the mechanical behavior of rubbers are elementary for designing elastomeric products. Some fracture mechanical concepts describing the failure behavior of rubbers are widely accepted in industrial and academic research. Although structural changes on the network scale may affect the mechanical properties of rubbers, the most common failure analyses are based on macroscopic approaches not considering microscopic damage. A specific phenomenon in (micro-) structural failure is cavitation due to strain constraints. Under geometrical constraints, the lateral contraction is suppressed. As a result, stress triaxiality causes inhomoge-neous, nonaffine deformation and internal defects, so-called cavities, appear. The formation and growth of cavities release stress and reduce the degree of constraints.Although cavitation in rubber has been studied for several decades, the knowledge about the fundamental mechanisms triggering the cavitation process is still very limited. This study aimed to characterize and describe the cavitation process comprehensively using convincing material parameters. Therefore several influenc-ing factors, such as network properties and filler reinforcement, have been consid-ered. Hence, advanced experimental methods, such as dilatometry and microtomog-raphy have been used for in situ investigations. Thin disk-shaped rubber samples have been used to prepare pancake specimens, which are characterized by a high aspect ratio. As a result, the degree of stress triaxiality is high and the dominating hydrostatic tensile stress causes the initiation of cavitation. For unfilled and carbon black reinforced styrene-butadiene-rubbers the onset of cavitation was determined precisely by highly sensitive data acquisition. Both, a stress-related and an energy-based cavitation criterion were found indicating that traditional approaches predicting internal failure indeed overestimate the material resistance against cavitation. Of special interest was the often suspected cavitation in unfilled rubbers, because, cavitation in rubbers is mainly attributed to interfacial failure between soft rubber matrix and rigid filler particles. Furthermore, cavitation in the process zone of notched planar specimens could be monitored by in situ X-ray scattering experiments. As a result, cavities appear in a region along the crack front. To understand the correlation between cavitation and macroscopic crack initiation additional tests were realized, i.e. intrinsic strength analysis. The results have shown that the macro failure is af-fected by microfracture, e.g. growth of cavities, controlled by the breakage of polymer chains. Both, numerical and experimental data indicate that under strain constraints rubbers do not exhibit incompressible deformation behavior. The presented experi-mental methods to characterize cavitation are suitable for future studies to investi-gate further aspects of cavitation, e.g. the behavior under dynamic loading, in rub-bers or other rubber-like materials

New insights into mechanisms affecting the fracture-mechanical behavior of unfilled natural rubber

For elastomers, advanced experimental techniques have been applied to better understand the impact of (micro-)structural phenomena, e.g. strain-induced crystallization (SIC), on the macroscopic fracture-mechanical properties. In this study, the formation and orientation of crystallites formed by SIC in natural rubber (NR) have been investigated at non-uniaxial tension, in fact, in “pure-shear” geometry and at crack tips, using synchrotron wide-angle X-ray scattering (WAXS)

The influence of thermal ageing of natural rubber/styrene butadiene rubber vulcanizates on steady state and dynamic wear behaviour

The aim of this work is to explore the influence of thermal ageing on wear resistance of cured rubber which has been based on varied composition of Natural rubber/Styrene butadiene rubber compounds. The thermal ageing process has been performed in a heating chamber at the temperature 80 degrees C during 4 and 16 days, respectively. The wear behaviour has been analysed at steady state as well as at dynamic conditions. The qualitative parameter "weight loss" has been observed during the analysis based on both of methods. We demonstrate the relationship between rubber composition, based on varied ratio of rubber types, and varied wear processes in dependence on thermal ageing.government of the Czech Republic [CZ.1.05/2.1.00/03.0111]; Internal Grant Agency of the TBU [IGA/FT/2014/014]; Research and Development for Innovations Operational Programme