Synthesis and Investigation of the Physical Properties of Lead-Free BCZT Ceramics

This work presents the structure, microstructure, and physical properties of low sintering temperature lead-free ceramics 0.52(Ba0.7Ca0.3)TiO3-0.48Ba(Zr0.2Ti0.8)O3 doped with nano-sized ZnO particles (noted as BCZT/x, x is the content of ZnO nanoparticles in wt.%, x = 0.00, 0.05, 0.10, 0.15, 0.20, and 0.25). The obtained results of Raman scattering and dielectric measurements have confirmed that Zn2+ has occupied B-site, to cause a deformation in the ABO3-type lattice of the BCZT/x specimens. The 0.15 wt.% ZnO-modified ceramic sintered at 1350°C exhibited excellent piezoelectric parameters: d33 = 420 pC/N, d31 = −174 pC/N, kp = 0.483, kt = 0.423, and k33 = 0.571. The obtained results indicate that the high-quality lead-free BCZT ceramic could be successfully synthesized at a low sintering temperature of 1350°C with an addition of appropriated amount of ZnO nanoparticles. This work also reports the influence of the sintering temperature on structure, microstructure, and piezoelectric properties of BCZT/0.15 compound. By rising sintering temperature, the piezoelectric behaviors were improved and rose up to the best parameters at a sintering temperature of 1450°C (d33 = 576 pC/N and kp = 0.55). The corresponding properties of undoped BCZT ceramics were investigated as a comparison. It also presented that the sintering behavior and piezo-parameters of doped BCZT samples are better than the undoped BCZT samples at each sintering temperature

ẢNH HƯỞNG CỦA TỈ LỆ Ba/Ti LÊN ĐẶC TRƯNG CỦA HẠT NANO BaTiO3 TỔNG HỢP BẰNG PHƯƠNG PHÁP THỦY NHIỆT

Highly dispersed BaTiO3 nanospheres with a uniform particle size were synthesized with the hydrothermal method. The influence of Ba/Ti molar ratios on the formation of BaTiO3 nanospheres was studied by analyzing the XRD and SEM data. The TiO2·H2O synthesized with the sulfuric acid method assisted by ultrasonication was used as a starting material. Highly dispersed BaTiO3 nanospheres with an average size of about 100 nm were obtained at 200 °C in 12 hours with a Ba/Ti ratio of 1.5. The Ba/Ti ratios have a strong influence on the formation of nano BaTiO3 and the phase transition. The particle size increases with the Ba/Ti ratio, while the uniformity decreases.Vật liệu BaTiO3 nano hình cầu phân tán cao với kích thước đồng đều được tổng hợp bằng phương pháp thủy nhiệt. Ảnh hưởng của tỉ lệ mol Ba/Ti lên sự hình thành vật liệu được nghiên cứu bằng cách phân tích dữ liệu XRD và SEM. TiO2·nH2O tổng hợp bằng phương pháp axit sunfuric với sự hỗ trợ sóng siêu âm được sử dụng làm nguyên liệu ban đầu. Vật liệu nano BaTiO3 hình cầu với độ phân tán cao và kích thước trung bình khoảng 100 nm đã thu được tại 200 °C trong 12 giờ với tỉ lệ Ba/Ti = 1,5. Tỷ lệ Ba/Ti ảnh hưởng mạnh đến sự hình thành BaTiO3 nano hình cầu với quá trình chuyển pha. Khi tăng tỉ lệ Ba/Ti, kích thước hạt tăng và tính đồng nhất giảm

MÀNG DẪN ĐIỆN TỪ SỢI NANO BẠC TỔNG HỢP BẰNG PHƯƠNG PHÁP POLYOL

In this paper, silver nanowires were prepared with the polyol method under ultrasonication. The optimal concentration of polyvinyl pyrrolidone in the reaction mixture was also determined. These nanowires were characterized with the XRD, SEM, and UV-Vis techniques. The conductive solution possesses a low resistance, good adhesion, high flexibility, and thermal stability. The solution was utilized to fabricate a conductive film, which might open up new technology applications.Trong bài báo này, sợi nano bạc đã được tổng hợp bằng phương pháp polyol dưới tác động của siêu âm. Đã xác định được nồng độ tối ưu của polyvinyl pyrrolidone cho quá trình chế tạo dung dịch. Sản phẩm sợi nano được khảo sát bằng kỹ thuật XRD, SEM và UV-Vis. Dung dịch dẫn điện có điện trở thấp, bám dính tốt, tính linh hoạt cao và ổn định nhiệt. Dung dịch này đã được sử dụng để chế tạo màng dẫn điện. Sản phẩm có thể mở ra một hướng mới cho các ứng dụng công nghệ sau này

AI is a viable alternative to high throughput screening: a 318-target study

: High throughput screening (HTS) is routinely used to identify bioactive small molecules. This requires physical compounds, which limits coverage of accessible chemical space. Computational approaches combined with vast on-demand chemical libraries can access far greater chemical space, provided that the predictive accuracy is sufficient to identify useful molecules. Through the largest and most diverse virtual HTS campaign reported to date, comprising 318 individual projects, we demonstrate that our AtomNet® convolutional neural network successfully finds novel hits across every major therapeutic area and protein class. We address historical limitations of computational screening by demonstrating success for target proteins without known binders, high-quality X-ray crystal structures, or manual cherry-picking of compounds. We show that the molecules selected by the AtomNet® model are novel drug-like scaffolds rather than minor modifications to known bioactive compounds. Our empirical results suggest that computational methods can substantially replace HTS as the first step of small-molecule drug discovery

Relaxor ferroelectric properties of PZT-PZN-PMnN Ceramics

555-560xPb(Zr0.47Ti0.53)O3-(0.925-x)Pb(Zn1/3Nb2/3)O3-0.075Pb(Mn1/3Nb2/3)O3+0.7%wt Li2CO3 (PZT-PZN-PMnN) ceramics with x=0.65-0.9 have been prepared by two-stage calcination method. The effect of the PZT content on the relaxor behavior and ferroelectric properties of ceramics has been investigated. The degree of diffuseness () from 1.72 to 1.85 indicates that all of compositions show a diffused phase transition with the strong frequency dispersion, which is characteristic of relaxor ferroelectric materials. The sharpness of the permittivity peak shows that the compositions are gradually approached normal ferroelectric behavior when the mol fraction of PZT increases. At x = 0.80, dielectric and ferroelectric properties of ceramics are optimal with the mass density () of 7.81 g/cm3, the dielectric constant (εr) of 1230, the dielectric loss (tan) of 0.005 and the remanent polarization (Pr) of 27 mC/cm2. </span

CẢI THIỆN TÍNH CHẤT MÀNG PVDF BẰNG CÁCH PHA TẠP GRAPHEN OXÍT TRONG PHƯƠNG PHÁP QUAY ĐIỆN

In this paper, graphene oxide doped Polyvinylidene Fluoride (PVDF/GO) films were prepared by electrospinning method. The obtained results indicate that the film involved the fibers with size about 700÷1200 nm. The effects of GO concentration of the film on mechanical and ferro-electrical properties were presented and discussed.Bài báo này trình bày một số kết quả nghiên cứu về màng Polyvinylidene Fluoride/Graphen oxit (PVDF/GO) dạng sợi được chế tạo bằng phương pháp quay điện (PPQĐ). Kết quả cho thấy, màng PVDF/GO được tạo bởi các sợi có đường kính cỡ 700÷1200 nm. Mặc khác, nồng độ tạp GO không những tăng cường độ bền cơ học mà còn ảnh hưởng đến các tính chất sắt điện của vật liệu

Structure and Physical Properties of PZT-PMnN-PSN Ceramics Near the Morphological Phase Boundary

The 0.9Pb(ZrxTi1−x)O3-0.07Pb(Mn1/3Nb2/3)O3-0.03Pb(Sb1/2Nb1/2)O3 (PZT-PMnN-PSN) ceramics were prepared by columbite method. The phase structure of the ceramic samples was analyzed. Results show that the pure perovskite phase is in all ceramics specimens. The effect of the Zr/Ti ratio on the region of morphotropic phase boundary for PZT-PMnN-PSN ceramics was studied. Experimental results show that the phase structure of ceramics changes from tetragonal to rhombohedral with the increase of the content of Zr/Ti ratio in the system. The composition of PZT-PMnN-PSN ceramics near the morphotropic phase boundary obtained is the ratio of Zr/Ti: 49/51. At this ratio, the ceramic has the optimal electromechanical properties: the kp=0.61, the εmax=29520, the d31=-236 pC/N, the Qm=2400, high remanent polarization (Pr=49.2 μC·cm−2), and low coercive field Ec=10.28 kV·cm−1

ẢNH HƯỞNG CỦA SIÊU ÂM CÔNG SUẤT ĐẾN KHẢ NĂNG XỬ LÝ KHUẨN VIBRIO SPP.

This paper presents the results of the application of power ultrasound to disinfect Vibrio spp. The results showed that the 150 W power ultrasound with a frequency of 26 kHz can disinfect Vibrio spp. quite effectively. On the other hand, the combination of the ultrasound (26 kHz, 150 W) and the oxidizing agent H2O2 can significantly improve Vibrio spp. disinfection.Bài báo trình bày kết quả nghiên cứu ứng dụng siêu âm công suất để xử lý khuẩn Vibrio spp. Các kết quả đã chỉ ra rằng sử dụng siêu âm công suất 150 W tần số 26 kHz có khả năng xử lý khuẩn Vibrio spp. khá hiệu quả. Mặt khác, khi kết hợp siêu âm công suất 150 W tần số 26 kHz, với tác nhân oxi hóa H2O2 thì hiệu suất xử lý khuẩn Vibrio spp. được nâng cao đáng kể

Accessing land cover change in Bo Trach district, Quang Binh province based on highresolution satellite imagery based on objectoriented perspective

This paper aims to assess land cover change by high-resolution remote satellite images in Bo Trach district, Quang Binh province. The study used eCognition Developer 9.1 to classify SPOT and Sentinal-2 images of the study area. Objects on the images are characterized by values of Channels, including Red, Green, Blue, NIR, Brightness, NDVI, and RIV. Since then, maps of land cover status in the year of 2005, 2010, and 2017 were created with high accuracy 92.22%, 91.28%, 94.22%, respectively. Overlaid three land cover maps to develop the land cover change maps of two periods 2005-2010 (period 1) and 2010-2017 (period 2). The results show that there is a variation in the area of land cover types, especially agriculture and forest land. Of which, agrarian land increased by 7.7% in period 1 and 9.95% in period 2. Whereas, forest land decreased by 0.6% in period 1 and 1.5% in period 2.Bài báo này nhằm mục đích đánh giá biến động sử dụng đất bằng viễn thám độ phân giải cao tại huyện Bố Trạch, tỉnh Quảng Bình. Nghiên cứu sử dụng phần mềm eCognition Developer 9.1để phân loại ảnh ảnh SPOT và Sentinal-2 trên địa bàn nghiên cứu. Các đặc trưng của đối tượng trên ảnh được xác định dựa trên giá trị độ sáng các Kênh 1, Kênh 2, Kênh 3, Kênh 4, giá trị độ sáng trung bình (Brightness), chỉ số khác biệt thực vật (NDVI) và tỷ số thực vật (RIV). Từ đó xây dựng được các bản đồ lớp phủ mặt đất các năm 2005, 2010, 2017 với độ chính xác lần lượt là 92,22%, 91,28%, 94.22%. Chồng ghép các bản đồ lớp phủ mặt đất, xây dựng bản đồ biến động sử dụng đất giữa hai thời kỳ 2005-2010 và 2010-2017. Kết quả nghiên cứu cho thấy có sự thay đổi giữa các loại hình lớp phủ gồm: đất nông nghiệp tăng khoảng 7,7% giai đoạn 1 và 9,95% giai đoạn 2. Đất lâm nghiệp giảm khoảng 0,6% giai đoạn 1 và 1,5% giai đoạn 2

Structure, microstructure and dielectric properties of lead-free BCT-<i>x</i>BZT ceramics near the morphotropic phase boundary

409-415There is an urgent demand for high performance Pb-free piezoelectrics to substitute for the current workhorse, the lead zirconate titanate (PZT) family. In the present study, the high performance lead-free BCT-xBZT ceramics near the morphotropic phase boundary (MPB) were prepared by traditional method. The structure, microstructure of the ceramics samples were analyzed. Results show that MPB for these ceramics is achieved with BZT component of x = 0.48. Dielectric properties show ferroelectric-relaxor behaviour of this system. Furthermore, the combination of ImageJ and Lince software allows analyzing SEM images of the ceramics for estimating average particle size and particle size distribution