9 research outputs found
Optically Enhanced Bonding Workstation for Robust Bonding
Process control is one of the methods recommended by the FAA to reduce risk in fabrication of structurally bonded composite joints for aircraft structure based on guidance provided in circular AC-107B for certification of structurally bonded joints. An Optically Enhanced Bonding Workstation is presented here that reduces the risk in bonded joint fabrication. Results will be presented demonstrating the benefits of process monitoring and its ability to reduce risk in performing pre-bond composite surface preparation steps. This supports reduction in the timeline to certification of bonded composite structures through development of a robust bonding process upstream of any part certification steps. Sanding surface preparation has been identified as a high risk process step that is known to impact bond performance. Control of sanding during surface preparation can be performed using portable surface analysis tools previously identified including included gloss, color, Fourier Transform Infrared spectroscopy (FTIR) and optically stimulated electron emissions (OSEE). Threshold limits for the surface analysis tool measurements were determined based on an example objective bonding system utilizing a common EA9394 paste adhesive measured using standard double cantilever beam fracture toughness testing. The patented Optically Enhanced Bonding Workstation (OEBW), was tailored to monitor and control the epoxy composite surface preparation step. Surface analysis tool threshold limits were incorporated into the OEBW to demonstrate improved composite bond performance through process control. The surface analysis tools investigated here can easily be incorporated into an automated system due to their applicability to rapidly quantify the composite sanded surface treatment and their portability
Efficient, environmentally acceptable method for waterproofing insulation material
A process of waterproofing alumina-rich or silica-rich fibrous thermal insulation material, the process including the steps of: (a) providing an alumina-rich or a silica-rich fibrous material; (b) providing a waterproofing solution including: (1) a carrier solvent selected from the group consisting of aliphatic alcohols having from 1C to 6C, water, and mixtures thereof; and (2) an alkoxysilane defined by the formula R.sub.4-x -Si-(O-R').sub.x where x is 1-3 and R is selected from the group consisting of alkyl groups having from 1C to 10C, hydrogen, or fluorocarbon groups having from 1F to 15F; and where O-R' is an alkoxy group having from 1C to 5C, or a mixture of alkoxysilanes defined by the above formula R.sub.4-x -Si-(O-R').sub.x ; and optionally (3) modifiers including acids, such as acetic acid or nitric acid, or bases, such as ammonium hydroxide, RNH.sub.2, R.sub.2 NH, or R.sub.3 N, or MOH, where R is selected from the group consisting of alkyl groups having from 1C to 10C or hydrogen, and where M=Na, Li, or K; (c) contacting the fibrous material with the waterproofing solution for a sufficient amount of time to waterproof the fibrous material; and (d) curing the coated fibrous material to render it sufficiently waterproof. A chemical solution for waterproofing alumina-rich or silica-rich fibrous thermal insulation materials, the solution including: (a) a carrier solvent selected from the group consisting of aliphatic alcohols having from 1C to 6C, water, and mixtures thereof; and (b) an alkoxysilane defined by the formula R.sub.4-x -Si-(O-R').sub.x where x is 1-3 and R is selected from the group consisting of alkyl groups having from 1C to 10C, hydrogen, or fluorocarbon groups having from 1F to 15F; and where O-R' is an alkoxy group having from 1C to 5C, or a mixture of alkoxysilanes defined by the above formula R.sub.4-x -Si-(O-R').sub.x ; and optionally (c) modifiers including acids, such as acetic acid or nitric acid, or bases, such as ammonium hydroxide, RNH.sub.2, R.sub.2 NH, or R.sub.3 N, or MOH, where R is selected from the group consisting of alkyl groups having from 1C to 10C or hydrogen, and where M=Na, Li, or K
Supersonic Retropulsion Surface Preparation of Carbon Fiber Reinforced Epoxy Composites for Adhesive Bonding
Surface preparation is widely recognized as a key step to producing robust and predictable bonds in a precise and reproducible manner. Standard surface preparation techniques, including grit blasting, manual abrasion, and peel ply, can lack precision and reproducibility, which can lead to variation in surface properties and subsequent bonding performance. The use of a laser to ablate composite surface resin can provide an efficient, precise, and reproducible means of preparing composite surfaces for adhesive bonding. Advantages include elimination of physical waste (i.e., grit media and sacrificial peel ply layers that ultimately require disposal), reduction in process variability due to increased precision (e.g. increased reproducibility), and automation of surface preparation, all of which improve reliability and process control. This paper describes a Nd:YAG laser surface preparation technique for composite substrates and the mechanical performance and failure modes of bonded laminates thus prepared. Additionally, bonded specimens were aged in a hot, wet environment for approximately one year and subsequently mechanically tested. The results of a one year hygrothermal aging study will be presented
Laser Surface Preparation of Epoxy Composites for Secondary Bonding: Optimization of Ablation Depth
Surface preparation has been identified as one of the most critical aspects of attaining predictable and reliable adhesive bonds. Energetic processes such as laser ablation or plasma treatment are amenable to automation and are easily monitored and adjusted for controlled surface preparation. A laser ablation process was developed to accurately remove a targeted depth of resin, approximately 0.1 to 20 micrometers, from a carbon fiber reinforced epoxy composite surface while simultaneously changing surface chemistry and creating micro-roughness. This work demonstrates the application of this process to prepare composite surfaces for bonding without exposing or damaging fibers on the surface. Composite panels were prepared in an autoclave and had a resin layer approximately 10 micrometers thick above the fiber reinforcement. These composite panels were laser surface treated using several conditions, fabricated into bonded panels and hygrothermally aged. Bond performance of aged, experimental specimens was compared with grit blast surface treated specimens using a modified double cantilever beam test that enabled accelerated saturation of the specimen with water. Comparison of bonded specimens will be used to determine how ablation depth may affect average fracture energies and failure modes
Further Investigation Into the Use of Laser Surface Preparation of Ti-6Al-4V Alloy for Adhesive Bonding
Adhesive bonding offers many advantages over mechanical fastening, but requires robust materials and processing methodologies before it can be incorporated in primary structures for aerospace applications. Surface preparation is widely recognized as one of the key steps to producing robust and predictable bonds. This report documents an ongoing investigation of a surface preparation technique based on Nd:YAG laser ablation as a replacement for the chemical etch and/or abrasive processes currently applied to Ti-6Al-4V alloys. Laser ablation imparts both topographical and chemical changes to a surface that can lead to increased bond durability. A laser based process provides an alternative to chemical-immersion, manual abrasion, and grit blast process steps which are expensive, hazardous, environmentally unfriendly, and less precise. In addition, laser ablation is amenable to process automation, which can improve reproducibility to meet quality standards for surface preparation. An update on work involving adhesive property testing, surface characterization, surface stability, and the effect of laser surface treatment on fatigue behavior is presented. Based on the tests conducted, laser surface treatment is a viable replacement for the immersion chemical surface treatment processes. Testing also showed that the fatigue behavior of the Ti-6Al-4V alloy is comparable for surfaces treated with either laser ablation or chemical surface treatment
Contamination and Surface Preparation Effects on Composite Bonding
Results presented here demonstrate the effect of several prebond surface contaminants (hydrocarbon, machining fluid, latex, silicone, peel ply residue, release film) on bond quality, as measured by fracture toughness and failure modes of carbon fiber reinforced epoxy substrates bonded in secondary and co-bond configurations with paste and film adhesives. Additionally, the capability of various prebond surface property measurement tools to detect contaminants and potentially predict subsequent bond performance of three different adhesives is also shown. Surface measurement methods included water contact angle, Dyne solution wettability, optically stimulated electron emission spectroscopy, surface free energy, inverse gas chromatography, and Fourier transform infrared spectroscopy with chemometrics analysis. Information will also be provided on the effectiveness of mechanical and energetic surface treatments to recover a bondable surface after contamination. The benefits and drawbacks of the various surface analysis tools to detect contaminants and evaluate prebond surfaces after surface treatment were assessed as well as their ability to correlate to bond performance. Surface analysis tools were also evaluated for their potential use as in-line quality control of adhesive bonding parameters in the manufacturing environment
Surface modification of aircraft used composites for adhesive bonding
Due to the inherent low surface energy of the polymer matrix portion of a given composite material, poor adhesion properties are exhibited and must be overcome in order to achieve strong adhesive bonds. Mechanical methods to improve adhesion have typically included manual abrasion like sanding or grit blasting. Energetic techniques, such as laser and plasma, are garnering continued attention towards the same end. This work describes results of recent investigations of atmospheric pressure plasma treatment (APPT) of composite materials based on glass and carbon fiber reinforced toughened epoxy resin systems for adhesive bonding. Chemical, physical and APPT treatments were compared in terms of enhancing surface energy and interfacial fracture toughness. Surface treatments were followed by characterization of wetting properties using traditional contact angle techniques as well as ballistic liquid deposition. The effects of APPT on the substrates were characterized by taking into account both chemical and morphological changes. Attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) and X-ray photoelectron spectroscopy (XPS) were used to confirm the elimination of fluorine and the introduction of oxygen and nitrogen. Etching effects of plasma were studied by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The double cantilever beam (DCB) test configuration was used to investigate treatment effects on adhesive bond performance. Results exhibited the effectiveness of physical procedures in cleaning surfaces, while APPT generated a higher hydrophilic behavior. All the samples tested by DCB yielded cohesive failure mode within the laminates.Depto. de Ingeniería Química y de MaterialesFac. de Ciencias QuímicasTRUEpu