Effect of Cyclic Martensitic γ-ε-γ Transformations on Diffusion Characteristics of Carbon in an Iron–Manganese Alloy

Carbon-diffusion characteristics in metastable Г18C2 iron–manganese alloy after the cyclic γ-ε-γ (f.c.c.–h.c.p.–f.c.c.) martensitic transitions were investigated using the radioactive-isotope method. As shown, the process of carbon transport acceleration in the alloy phase-hardened by means of the γ-ε-γ transformations was caused by two independent mechanisms.Методом радиоактивных изотопов исследованы диффузионные характеристики углерода в метастабильном железомарганцевом сплаве Г18С2, наклёпанном циклическими мартенситными превращениями γ-ε-γ (ГЦК–ГПУ–ГЦК).Методою радіоактивних ізотопів досліджено дифузійні характеристики Карбону у метастабільному залізоманґановому стопі Г18С2, наклепаному циклічними мартенситними перетвореннями γ-ε-γ (ГЦК–ГЩП–ГЦК)

Effect of cyclic martensitic γ-ε transformations on diffusion characteristics of cobalt in an iron–manganese alloy

This review article analyses the results of experimental investigations of the influence of the cyclic direct γ−ε (f.c.c.–h.c.p.) and reverse ε−γ (h.c.p.–f.c.c.) martensitic transformations (MT) on the diffusion characteristics of Co atoms in Г18С2 (Fe–18.3 wt.% Mn–2.1 wt.% Si) alloy with low stacking-fault energy.В оглядовій статті аналізуються результати експериментальних досліджень впливу циклічних мартенситних перетворень (МП), прямих (ГЦК ГЩП) і зворотн іх (ГЩП ГЦК), на дифузійні характеристики атомів Co у залізоманановому стопі Г18С2 (Fe 18,3 ваг.% Mn 2,1 ваг.% Si) з низькою енергією дефектів пакування (ДП).В обзорной статье анализируются результаты экспериментальных исследований влияния циклических мартенситных превращений (МП), прямых (ГЦК ГПУ) и обратных (ГПУ ГЦК), на диффузионные характеристики атомов Co в железомарганцевом сплаве Г18С2 (Fe 18,3 вес.% Mn 2,1 вес.% Si) с низкой энергией дефектов упаковки (ДУ)

Registration of atmospheric neutrinos with the Baikal neutrino telescope

We present first neutrino induced events observed with a deep underwater neutrino telescope. Data from 70 days effective life time of the BAIKAL prototype telescope NT-96 have been analyzed with two different methods. With the standard track reconstruction method, 9 clear upward muon candidates have been identified, in good agreement with 8.7 events expected from Monte Carlo calculations for atmospheric neutrinos. The second analysis is tailored to muons coming from close to the opposite zenith. It yields 4 events, compared to 3.5 from Monte Carlo expectations. From this we derive a 90 % upper flux limit of 1.1 * 10^-13 cm^-2 sec^-1 for muons in excess of those expected from atmospheric neutrinos with zenith angle > 150 degrees and energy > 10GeV.Comment: 20 pages, 11 figure

Effect of Cyclic Martensitic γ\gamma-ϵ\epsilon-γ\gamma Transformations on Diffusion Characteristics of Carbon in an Iron–Manganese Alloy

Carbon-diffusion characteristics in metastable Г18C2 iron–manganese alloy after the cyclic γ-ε-γ (f.c.c.–h.c.p.–f.c.c.) martensitic transitions were investigated using the radioactive-isotope method. As shown, the process of carbon transport acceleration in the alloy phase-hardened by means of the γ-ε-γ transformations was caused by two independent mechanisms.Методом радиоактивных изотопов исследованы диффузионные характеристики углерода в метастабильном железомарганцевом сплаве Г18С2, наклёпанном циклическими мартенситными превращениями γ-ε-γ (ГЦК–ГПУ–ГЦК).Методою радіоактивних ізотопів досліджено дифузійні характеристики Карбону у метастабільному залізоманґановому стопі Г18С2, наклепаному циклічними мартенситними перетвореннями γ-ε-γ (ГЦК–ГЩП–ГЦК)

Iron alloys with new functional properties obtained during reverse martensitic transformation

It was shown that different types of the austenite (homogeneous and inhomogeneous polyhedral, or submicrocrystalline and nanocrystalline plate austenite) can be formed, providing new functional properties of various steels and alloys. The austenite formed during a partial $\alpha\to\gamma$ transformation increases considerably the strength of the martensite, enhances the coercive force and improves the square shape of the hysteresis loop of maraging steels. The thermal expansion coefficient of the austenitic alloy type 32Ni can be adjusted over broad limits thanks to different $\alpha\to\gamma$ transformation conditions. A stainless steel with a structure of alternating laths of the martensite and the austenite has a high resistance to radiation void formation