Electron-beam modification of coating-aluminum substrate systems

Multiphase surface alloys with improved strength and tribological characteristics have been synthesized by exposing coating/A7 substrate systems to a pulsed electron beam. Optimum modes of electron-ion-plasma treatment of commercially pure aluminum have been found at which the wear resistance and hardness of the surface layer were observed to increase by a factor of about 7.5 and up to 18, respectively

Surface structure of commercially pure VT1-0 titanium irradiated by an intense pulsed electron beam

It is shown that pulsed electron beam irradiation of commercially pure titanium at a beam energy density of 10 J/cm{2}, pulse duration of 150 [mu]s, number of pulses of N=5 pulses, and pulse repetition frequency of 0.3 Hz with attendant polymorphic [alpha]->[beta]->[ alpha] transformations allows a more than five-fold decrease in the grain and subgrain sizes of the material structure

Improving the Mechanical Properties of SiC-ceramics by means of Vacuum Electron-ion-plasma Alloying with Titanium

The investigation results of elemental and phase composition, state of defective substructure and microhardness of the surface layer of "film (Ti)/substrate (SiC-ceramics)" system (Ti film 0.5 [mu]m thick was deposited on the surface of SiC-ceramics) subjected to treatment with an intense pulsed low-energy electron beam (15 J/cm{2}, 200 [mu]s, 0.3 s{-1}, 20 pulses) are presented. It is shown that irradiation of the "film (Ti)/substrate (SiC-ceramics)" system with an electron beam is accompanied by the formation of multielement multiphase (SiC; TiC; Ti5Si[3]) surface layer having submicro- and nanocrystalline structure. Microhardness of the irradiated surface layer reaches a value of 74 GPa, that is twice the value of microhardness of SiC-ceramics (36 GPa)

Formation of the surface alloys by high-intensity pulsed electron beam irradiation of the coating/substrate system

The results of the analysis of the structure and properties of the surface layer of aluminum A7 subjected to alloying by the intense pulsed electron beam melting of the film / substrate system. Fold increase in strength and tribological properties of the modified surface layer due to the formation of submicro - nanoscale multiphase structure have been revealed

Improving the Mechanical Properties of SiC-ceramics by means of Vacuum Electron-ion-plasma Alloying with Titanium

The investigation results of elemental and phase composition, state of defective substructure and microhardness of the surface layer of "film (Ti)/substrate (SiC-ceramics)" system (Ti film 0.5 [mu]m thick was deposited on the surface of SiC-ceramics) subjected to treatment with an intense pulsed low-energy electron beam (15 J/cm{2}, 200 [mu]s, 0.3 s{-1}, 20 pulses) are presented. It is shown that irradiation of the "film (Ti)/substrate (SiC-ceramics)" system with an electron beam is accompanied by the formation of multielement multiphase (SiC; TiC; Ti5Si[3]) surface layer having submicro- and nanocrystalline structure. Microhardness of the irradiated surface layer reaches a value of 74 GPa, that is twice the value of microhardness of SiC-ceramics (36 GPa)

Nonequilibrium structural condition in the medical TiNi-based alloy surface layer treated by electron beam

The research is devoted to study the structural condition and their evolution from the surface to the depth of TiNi specimens treated by low-energy high-current electron beams with surface melting at a beam energy density E = 10 J/cm2, number of pulses N = 10, and pulse duration [tau] = 50 Ps. Determined thickness of the remelted layer, found that it has a layered structure in which each layer differs in phase composition and structural phase state. Refinement B2 phase lattice parameters in local areas showed the presence of strong inhomogeneous lattice strain