Initial aging phenomena in copper-chromium alloys

The effects of quenching and aging temperatures on the initial aging curves of Cu-Cr alloy were examined mainly by means of electrical resistivity measurements. Three Cu-Cr alloy specimens having 0.24, 0.74, and 1.0% Cr were solution-treated at 950-1050 C, quenched into ice-water, and subsequently aged at 300-500 C. The results were as follows: (1) At the very early stage of aging (within about 30 sec), an abrupt decrease of resistivity with lowering aging tempratures. (T sub A) and rising solution temperatures (T sub S) was observed at (T sub A) up to about 400 C. In contrast, a transient increase of resistivity with rising T sub A and lowering T sub S was observed at T sub A from about 450 to 500 C. These phenomena seem to be caused by a rapid formation of solute clusters and the reversion of clusters formed during quenching, which are enhanced by quenched-in vacancies, respectively. (2) The amount of precipitation increased at the latter stage of aging with rising T sub S and T sub A as generally expected, where T sub S was not so high as to form secondary defects. (3) As a result, the initial aging phenomena in Cr-Cr alloy were revealed to be complicated against expectations. This was considered to be due to the migration energy of vacancies so larger in Cu-base

Quadrupole moments in chiral material DyFe3(BO3)4 observed by resonant x-ray diffraction

By means of circularly polarized x-ray beam at Dy L3 and Fe K absorption edges, the chiral structure of the electric quadrupole was investigated for a single crystal of DyFe3(BO3)4 in which both Dy and Fe ions are arranged in spiral manners. The integrated intensity of the resonant x- ray diffraction of space-group forbidden reflections 004 and 005 is interpreted within the electric dipole transitions from Dy 2p3 to 5d and Fe 1s to 4p, respectively. We have confirmed that the 2 handedness of the crystal observed at Dy L3 and Fe K edges is consistent with that observed at Dy M5 edge in the previous study. By analyzing the azimuth scans of the diffracted intensity, the electronic quadrupole moments of Dy 5d and Fe 4p are derived. The temperature profiles of the integrated intensity of 004 at the Dy L3 and the Fe K edges are similar to those of Dy-O and Fe-O bond lengths, while that at the Dy M5 edge does not. The results indicate that the helix chiral orientations of quadrupole moments due to Dy 5d and Fe 4p electrons are more strongly affected by the crystal fields than Dy 4f

Development Of Climate Change Information Database And Its Use In Civic Consciousness Enlightenment

GCM outputs such as CMIP3 are available via network access to PCMDI web site. Meteorological researchers are familiar with the usage of the GCM data, but the most of researchers other than meteorology such as agriculture, civil engineering, etc., and general people are not familiar with the GCM. There are some difficulties to use GCM; 1) to download the enormous quantity of data, 2) to understand the GCM methodology, parameters and grids. In order to provide a quick access way to GCM, Climate Change Information Database has been developed. The purpose of the database is to bridge the users and meteorological specialists and to facilitate the understanding the climate changes. The resolution of the data is unified, and climate change amount or factors for each meteorological element are provided from the database. All data in the database are interpolated on the same 80km mesh. Available data are the present-future projections of 27 GCMs, 16 meteorological elements (precipitation, temperature, etc.), 3 emission scenarios (A1B, A2, B1). We showed the summary of this database to residents in Toyama prefecture and measured the effect of showing and grasped the image for the climate change by using the Internet questionary survey. The persons who feel a climate change at the present tend to feel the additional changes in the future. It is important to show the monitoring results of climate change for a citizen and promote the understanding for the climate change that had already occurred. It has been shown that general images for the climate change promote to understand the need of the mitigation, and that it is important to explain about the climate change that might occur in the future even if it did not occur at the present in order to have people recognize widely the need of the adaptation

Image-based quantitative determination of DNA damage signal reveals a threshold for G2 checkpoint activation in response to ionizing radiation

Background: Proteins involved in the DNA damage response accumulate as microscopically-visible nuclear foci on the chromatin flanking DNA double-strand breaks (DSBs). As growth of ionizing radiation (IR)-induced foci amplifies the ATM-dependent DNA damage signal, the formation of discrete foci plays a crucial role in cell cycle checkpoint activation, especially in cells exposed to lower doses of IR. However, there is no quantitative parameter for the foci which considers both the number and their size. Therefore, we have developed a novel parameter for DNA damage signal based on the image analysis of the foci and quantified the amount of the signal sufficient for G2 arrest.Results: The parameter that we have developed here was designated as SOID. SOID is an abbreviation of Sum Of Integrated Density, which represents the sum of fluorescence of each focus within one nucleus. The SOID was calculated for individual nucleus as the sum of (area (total pixel numbers) of each focus) x (mean fluorescence intensity per pixel of each focus). Therefore, the SOID accounts for the number, size, and fluorescence density of IR-induced foci, and the parameter reflects the flux of DNA damage signal much more accurately than foci number. Using very low doses of X-rays, we performed a "two-way" comparison of SOID of Ser139-phosphorylated histone H2AX foci between G2-arrested cells and mitosis-progressing cells, and between mitosis-progressing cells in the presence or absence of ATM or Chk1/2 inhibitor, both of which abrogate IR-induced G2/M checkpoint. The analysis revealed that there was a threshold of DNA damage signal for G2 arrest, which was around 4000~5000 SOID. G2 cells with < 4000 SOID were neglected by G2/M checkpoint, and thus, the cells could progress to mitosis. Chromosome analysis revealed that the checkpoint-neglected and mitosis-progressing cells had approximately two chromatid breaks on average, indicating that 4000~5000 SOID was equivalent to a few DNA double strand breaks.Conclusions: We developed a novel parameter for quantitative analysis of DNA damage signal, and we determined the threshold of DNA damage signal for IR-induced G2 arrest, which was represented by 4000~5000 SOID. The present study emphasizes that not only the foci number but also the size of the foci must be taken into consideration for the proper quantification of DNA damage signal

Heterogeneous integration approach based on flip-chip bonding and misalignment self-correction elements for electronics-optics integration applications

This paper presents a high precision bonding approach, capable of submicron alignment accuracy, based on the thermosonic flip-chip bonding technique and misalignment self-correction elements. The precision of the bonding technique is guaranteed by using of misalignment self-correction bump (convex) and hollow (concave) elements. Metal cone bump and conductive sloped hollow bonding pad elements are created using micro-machining techniques, on a chip specimen and substrate, respectively. The chip and substrate are bonded face-to-face using of an ultrasonic-enhanced flip-chip bonder. By introducing of misalignment self-correction elements, repeatable bonding accuracies of less than 500 nm were confirmed through experimental investigation. Bond properties, including electrical and mechanical properties, are also characterized to confirm the success of the bonding approach. With the obtained results, the proposed bonding approach is capable of being use in electronics-optics heterogeneous integration applications