Estudo da viabilidade da reciclagem de biocompósitos à base de polipropileno e fibras de curauá
This research presents an approach about the polypropylene recycling process reinforced with curauá reprocessed fibers. As an alternative proposal reinforcement to polymeric composites. Levels of 10 %, 20 % and 30 % of fibers in the biocomposites were analyzed to check their mechanical properties comparing them, even with the properties of polypropylene (PP). Pellets biocomposites were prepared by the extrusion process, and the specimens were manufactured by injection process and subjected to mechanical tests of uniaxial tensile, three point bending and impact. To check for damage to the specimens was used to analysis by scanning electron microscopy (SEM). These biocomposites were also subjected to testing physical – chemistry of index of fluidity (IF). It was observed that the polypropylene biocomposites with 30 % curauá fibers showed higher elastic modulus for both traction and to flexion and less resistance to impact. For all biocomposites, the values found in tensile tests to the limits of flow and maximum voltage have approximate values as they were added the curauá fibers. Another important point was increased resistance to bending in biocomposite as promoting the addition of curauá fibers and decrease as they were reprocessed also decreased thermal degradation of the polypropylene blends and curauá fibers, and no impairment of so in general, the production of biocomposites, when analyzed by scanning electron microscopy.Esta pesquisa apresenta uma abordagem a cerca do processo de reciclagem do polipropileno reforçado com fibras de curauá reprocessado. Sendo uma proposta alternativa de reforço aos compósitos poliméricos. Teores de fibras de 0%, 10%, 20% e 30% foram analisados para verificação de suas propriedades mecânicas comparando-as, inclusive com as propriedades do polipropileno (PP). Os biocompósitos granulados foram preparados em uma extrusora. Os corpos de prova foram moldados por processo de injeção e submetidos aos ensaios mecânicos de tração uniaxial, flexão em três pontos e impacto. Para verificação de danos aos corpos de prova utilizou-se da análise por microscopia eletrônica de varredura (MEV). Estes biocompósitos também foram submetidos a ensaios físico - químicos de índice de fluidez (IF). Observou-se que os biocompósitos de polipropileno com 30% de fibras de curauá apresentaram maior módulo de elasticidade e menor resistência ao impacto. Para todos os biocompósitos, os valores encontrados nos ensaios de tração para os limites de escoamento e tensão de ruptura não sofreram alterações à medida que se adicionavam as fibras. Outros pontos relevantes foram o aumento da resistência à flexão, a redução da degradação térmica das misturas polipropileno e fibras de curauá, e o não comprometimento de uma forma em geral, da fabricação dos biocompósitos, quando analisados por microscopia eletrônica de varredura
Estudo das propriedades mecânicas de biocompósitos de polipropileno reforçados com fibras naturais
This research presents an approach to the addition of curauá fibers and licuri fibers in
a polypropylene resin matrix, such as an alternative proposal to reinforce the polymeric
composites. Fiber content of 0 %, 5 %, 10 %, and 20% were analyzed for verification of their
mechanical properties comparing them, inclusive with the properties of polypropylene. The
grainulated biocomposites had been prepared in an extrusora. The test bodies had been
molded by injection and submitted to the mechanical essays uniaxial traction, flexion on three
points, impact, in addition to thermal tests (HDT). These biocomposites had been also
subjected the essay physicist-chemistry index of fluidity (IF). It was observed that the
biocomposites of PP with 20% curauá, obtained bigger increase in the modulus of elasticity
and a bigger reduction in the resistance to the impact. In the mechanical behavior, for all the
biocomposites, these were increases in values of the limit of drainage and tension of rupture,
when tested by uniaxial traction, as they added the fibers. Another important point was the
increase of the resistance the flexion. It was also noted that the addition of fibers reduced the
thermal degradation of the mixture natural fibers / polypropylene.Esta pesquisa apresenta uma abordagem da adição de fibras de licuri e curauá em uma
matriz de resina de polipropileno, essa como uma proposta alternativa de reforço aos
compósitos poliméricos. Teores de fibras de 0 %, 5 %, 10 %, e 20 % foram analisados para
verificação de suas propriedades mecânicas comparando-as, inclusive com as propriedades do
polipropileno. Os biocompósitos granulados foram preparados em uma extrusora. Os corpos
de prova foram moldados por injeção e submetidos aos ensaios mecânicos de tração uniaxial,
flexão em três pontos, impacto, além de ensaios térmicos (HDT). Estes biocompósitos
também foram submetidos a ensaio físico-químico de índice de fluidez (IF). Observou-se que
os biocompósitos de PP com 20% curauá obteve maior aumento no módulo de elasticidade, e
uma maior diminuição na resistência ao impacto. No comportamento mecânico, para todos os
biocompósitos, houve acréscimos nos valores do limite de escoamento e tensão de ruptura
quando ensaiados por tração uniaxial, à medida que se adicionavam as fibras. Outro ponto
importante foi o aumento da resistência à flexão. Verificou-se também que a adição de fibras
reduziu a degradação térmica da mistura fibras naturais / polipropileno