Effect of the over-ageing treatment on the mechanical properties of AA2024 aluminum alloy.

The evolution of the hardness of the over-ageing AA2024 alloy scale was followed by measurements of Vickers hardness. The nanoindentation is adapted to the determination of elastoplastic properties (hardness and Young’s modulus) of the matrix and also of coarse intermetallic precipitates. Influence of the artificial over-ageing time to hardness and to mechanical properties as the local scale was investigated

EFFECT OF NORMAL FORCE ON TRIBOCORROSION BEHAVIOUR OF Ni-30Cr MODEL ALLOY IN LiOH - H3BO3 SOLUTION

International audienceTribocorrosion of Ni - 30Cr model alloy was investigated for different contact pressures in LiOH H3BO3 solution at room temperature. The sliding tests were performed with a pin-on-disc tribometer designed to evaluate the synergistic effect between corrosion and wear. The combined corrosion wear degradation during sliding tests was monitored and evaluated by open circuit potential measurements and electrochemical impedance spectroscopy measurements. The sliding track morphology was investigated by SEM and profilometric measurements after sliding tests. The total material loss generated by the deterioration of the protective oxide layer due to combined chemical / electrochemical and mechanical interactions in the sliding track area was assessed from quantitative and qualitative point of view

Effect of the Over-ageing Treatment on the Mechanical Properties of AA2024 Aluminum Alloy

The evolution of the hardness of the over-ageing AA2024 alloy scale was followed by measurements of Vickers hardness. The nanoindentation is adapted to the determination of elastoplastic properties (hardness and Young's modulus) of the matrix and also of coarse intermetallic precipitates. Influence of the artificial over-ageing time to hardness and to mechanical properties as the local scale was investigated. Keywords: AA2024 aluminum alloy, over-ageing treatment, mechanical properties, hardness, Young's modulus The aluminum alloys of the 2000 series, AA2024-T351 alloy, are used in the aerospace industry for the wings and fuselage skins of the aircraft, due to the high strength to weight ratio associated with good fracture toughness. A combination of alloying elements, heat treatment and ageing induce the improvement of mechanical properties, as well as good damage tolerance and resistance to fatigue The precipitation of the equilibrium phase, S -Al2CuMg phases and the phases S" and S' is the main responsible for final hardening. Most authors considered that the dislocations serve as the heterogeneous nucleation sites for the S (Al2CuMg) phase in Al-Cu-Mg alloy during artificial ageing The mechanical properties are improved due to hardening precipitation that lead to peak-ageing condition and to the over-ageing condition with increasing ageing. During ageing treatment, the change in mechanical properties function of the treatment time can be plotted as a belle-shape curve, with a maximum value. The evolution of mechanical properties can be described by three successive stages: under-aged temper, aged temper and over-aged temper. In the figure 1 are represented the evolution of hardness and mechanical strength of the aluminum alloy during ageing treatment The present work was aimed to investigate effects of over-ageing treatment on the mechanical properties of the

Romanian-French Collaboration for Master and Doctoral Studies in ``Materials Engineering''

Innovative Manufacturing Engineering Conference (IManE), Chisinau, MOLDOVA, MAY 29-30, 2014International audienceThe present paper describes the collaboration between the University of Pitesti at international level in educational for scientific research at Master and Doctoral studies in ``Materials Engineering'' filed. The international cooperation of higher education institutions in the academic research field can be manifested in different ways. The most important characteristics of various forms of international cooperation are the cohesion and the close relations that are built between higher education institutions