30 research outputs found
Transformation kinetics of selected steel grades after plastic deformation
The aim of this article was to assess the impact of previous plastic deformation on the kinetics of transformations of four selected steels. The research was conducted with use of the universal plastometer GLEEBLE 3800, when Continuous Cooling Transformation (CCT) and Deformation Continuous Cooling Transformation (DCCT) diagrams of selected steels were constructed on the basis of dilatometric tests. The research confirmed that the strain accelerates the particularly the transformations controlled by diffusion. Bainitic transformation was accelerated in three of the four steels. In the case of martensitic transformation the effect of the previous deformation was relatively small, but with clearly discernible trend
Hot flow stress models of the steel C45
Flows stress of the steel C45 were predicted on the basis of experimentally obtained flow stress curves, using uniaxial hot compression tests on the plastometer HDS-20, by two completely different types of mathematical models, moreover with comparison to a model comprised in the FEM database of the FORGE software. The tests were carried out within the temperature range from 900 to 1 280 °C, at the strain rate from 0,1 to 100 s<sup>-1</sup> and deformations up to 1,0. It follows from the results of flow stress prediction that models designed on the basis of experimental measurements have much better information capability than the generated model implemented into the database of the FORGE software, however, their extrapolation for larger deformations is limited