98 research outputs found
Investigating the cytotoxicity of dual-cure bulk-fill resin materials on L929 cells
The aim of this in vitro study was to investigate cytotoxic effects of dual-cure bulk-fill resin materials polymerized with a third-generation LED light-curing unit (LCU) on L929 fibroblast cells in terms of morphology and viability. Three novel dual-cure, flowable bulk-fill materials (Fill-Up!(TM)) a bioactive material (ACTIVA (TM) BioACTIVE-RESTORATIVE (TM)), and a dual-cure bulk-fill composite material (HyperFIL (R) HAp) polymerized by LED LCU (VALO (TM) Cordless) were tested. Each material was placed in plastic rings (4 mm x 5 mm) in a single layer. Unpolymerized rings filled with each material were placed in direct contact with cells and then polymerized. After polymerization, the removed medium was readded to wells. In this study, four control groups were performed: the medium-free control group, medium control group, physical control group, and light applied control group. Three samples were prepared from each group. After 24 h, the morphology of cells was examined and a WST-1 test was performed. The percentage of cell viability (PCV) of each group was calculated. The experiment was repeated three times. Data were analyzed by a Kruskal-Wallis Test and a Mann-Whitney U test. p 0.05). All control groups showed acceptable PCV (>70%) and cells were spindle-like, similar to the original fibroblast cells. It can be suggested that clinicians should pay attention when applying dual-cure bulk-fill materials in deep cavities, or they should use a liner material under these materials.Bezmialem Vakif Universit
Profundidad de curado, propiedades mecánicas y morfología de resinas compuestas duales
This study evaluated selected structural and physical properties, such as degree of conversion (DC), Vickers hardness (VHN), and compression strength (CS), of three new dual-cure bulk-fill resin-based composites (RBCs; ACTIVA, HyperFIL, and Fill-Up) and compared them to those of a conventional RBC (Filtek Z250) at three clinically relevant depths. Samples (n=180) were prepared in three depths (2,4, and 6mm). Fourier-transform infrared spectroscopy (FTIR) analysis and VHN and CS tests were performed. The DC value was calculated by considering the relative change in the aliphatic C=C peaks. The fractured surfaces of representative samples were characterized using scanning electron microscopy (SEM). Data were statistically evaluated using two-way analysis of variance and post hoc Bonferroni tests (p<0.05). According to the VHN results, Filtek Z250 showed the highest bottom/top hardness ratio (97.94±1.01) at 2mm thickness and ACTIVA showed the lowest bottom/top hardness ratio (43.48±5.64) at 6mm thickness (p<0.001). According to the FTIR results, the DC decreased with increasing thickness in all materials (p<0.05). Filtek Z250 showed the highest (301±12.4 MPa) and ACTIVA exhibited the lowest (232±17.2 MPa) CS values at 2mm thickness (p<0.05). The lowest CS values were obtained for ACTIVA, and the highest values were obtained for Filtek Z250 for samples with thicknesses of 4 and 6mm, respectively (p<0.05). The structural features of restorative composites, such as the resin chemistry and filler type and content, and the operational parameters (i.e., material thickness and curing conditions) strongly affect crosslinking reactions and thus the DC, VHN, and CS values.RESUMEN: Este estudio evaluó propiedades físicas y estructurales, como el grado de conversión (DC), la dureza Vickers (VHN) y la resistencia a la compresión (CS), de tres nuevos compósitos a base de resina de curado dual tipo bulk (RBC; ACTIVA , HyperFIL y Fill-Up) y los comparó con los de una resina compuesta convencional (Filtek Z250) en tres profundidades clínicamente relevantes. Se prepararon muestras (n=180) en tres profundidades (2,4 y 6mm). Se realizaron análisis de espectroscopia infrarroja por transformada de Fourier (FTIR) y pruebas VHN y CS. El valor de DC se calculó considerando el cambio relativo en los picos alifáticos C=C. Las superficies fracturadas de muestras representativas se caracterizaron mediante microscopía electrónica de barrido (MEB). Los datos se evaluaron estadísticamente mediante análisis de varianza de dos vías y pruebas post hoc de Bonferroni (p<0,05). De acuerdo con los resultados de VHN, Filtek Z250 mostró la relación de dureza inferior/superior más alta (97,94±1,01) con un espesor de 2mm y ACTIVA mostró la relación de dureza inferior/superior más baja (43,48±5,64) con un espesor de 6mm (p<0,001). De acuerdo con los resultados de FTIR, la DC disminuyó al aumentar el espesor en todos los materiales (p<0,05). Filtek Z250 mostró los valores de CS más altos (301±12,4 MPa) y ACTIVA los más bajos (232±17,2 MPa) a 2mm de espesor (p<0,05). Los valores más bajos de CS se obtuvieron para ACTIVA y los valores más altos para Filtek Z250 para muestras con espesores de 4 y 6mm, respectivamente (p<0,05). Las características estructurales de las resinas compuestas de restauración, como la química; además del tipo y contenido del relleno, y los parámetros operativos (es decir, el espesor del material y las condiciones de curado) afectan en gran medida las reacciones de interacción química y, por lo tanto, los valores de DC, VHN y CS
Characterisation and microleakage of a new hydrophilic fissure sealant – UltraSeal XT® hydro™
Objectives: The new hydrophilic fissure sealant, UltraSeal XT® hydro™ (Ultradent Products, USA), was characterised and its in vitro resistance to microleakage after placement on conventionally acid etched and sequentially lased and acid etched molars was investigated.
Materials and Methods: The sealant was characterised by Fourier transform infra-red spectroscopy, (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and Vickers indentation test. Occlusal surfaces of extracted human molars were either conventionally acid etched (n = 10), or sequentially acid etched and laser irradiated (n = 10). UltraSeal XT® hydro™ was applied to both groups of teeth which were then subjected to 2500 thermocycles between 5 and 55 °C prior to microleakage assessment by fuchsin dye penetration.
Results: UltraSeal XT® hydro™ is an acrylate-based sealant which achieved a degree of conversion of 50.6 ± 2.2% and a Vickers microhardness of 24.2 ± 1.5 under standard light curing (1000 mWcm-2 for 20 s). Fluoride ion release was negligible within a 14-day period. SEM and EDX analyses indicated that the sealant comprises irregular sub-micron and nano-sized silicon-, barium- and aluminium-bearing filler phases embedded within a ductile matrix. Laser preconditioning was found to significantly reduce microleakage (Mann-Whitney U test, p < 0.001). The lased teeth presented enhanced surface roughness on a 50 to 100 μm scale which caused the segregation and concentration of the filler particles at the enamel-sealant interface.
Conclusion: Laser preconditioning significantly decreased microleakage and increased enamel surface roughness which caused zoning of the filler particles at the enamel-sealant interface
Effect of Er:YAG laser enamel conditioning and moisture on the microleakage of a hydrophilic sealant
For a given sealant, successful pit and fissure sealing is principally governed by the enamel conditioning technique and the presence of moisture contamination. A new generation of hydrophilic resin sealants is reported to tolerate moisture. This study investigates the impact of Er:YAG laser pre-conditioning and moisture contamination on the microleakage of a recent hydrophilic sealant. Occlusal surfaces of extracted human molars were either acid etched (n = 30), or successively lased and acid etched (n = 30). Ten teeth from each group were either air-dried, water-contaminated, or saliva-contaminated prior to sealing with UltraSeal XT® hydro™. Samples were inspected for penetration of fuchsin dye following 3000 thermocycles between 5 and 50 °C, and the enamel–sealant interfaces were observed by scanning electron microscopy (SEM). Significant differences in microleakage were evaluated using the Mann–Whitney U test with Bonferroni adjustment (p = 0.05). Laser pre-conditioning significantly reduced dye penetration irrespective of whether the enamel surface was moist or dry. Microleakageof water-contaminated acid etched teeth was significantly greater than that of their air-dried or saliva-contaminated counterparts. SEM analysis demonstrated good adaptation in all groups with the exception of water-contaminated acid etched teeth which exhibited relatively wide gaps. In conclusion, this hydrophilic sealant tolerates the presence of saliva, although water was found to impair its sealing ability. Laser pre-conditioning significantly decreases microleakage in all cases
The Investigation of The Anisotropic Analytical Algorithm (AAA) and the Acuros XB (AXB) Dose Calculation Algorithms Accuracy in Surface and Buildup Region for 6 MV Photon Beam Using Gafchromic EBT3 Film
Do the differences in organic contents of composite resins affect surface roughness and Streptococcus mutans adhesion?
The aim of this in vitro study was to evaluate the surface properties of four composite materials with different organic contents and Streptococcus mutans (S. mutans) adhesion to the surfaces after 4 h. TCD-based (CT; Charisma Topaz), Bis-GMA-based (ESQ; Estelite Sigma Quick), UDMA-based (GA;G-aenial Anterior), ormocer-based composites (AF;Admira Fusion) were selected. Polystyrene was used as a control group. Fifteen cylindrical specimens (10 mm diameter x 2 mm depth) were prepared for each group. Surface roughness (SR) was investigated with AFM. Hydrophobicity and surface free energy (SFE) was determined by the sessile drop method. Early adhesion of S. mutans on the materials were evaluated by optical density readouts on a spectrophotometer. Surface morphology and S. mutans bacterial adhesion (SMBA) were examined using SEM. Data were analyzed by ANOVA, post-hoc Dunnett (p 0.05) while a statistically significant difference was obtained between the test groups in terms of surface SMBA (p < 0.05).The highest SMBA was observed in GA while ESQ showed the lowest. There was a significant correlation between SMBA and SR in the AF (r = 0.929; p = 0.001), CT (r = 0.976; p = 0.001) and ESQ(r = 0.731; p = 0.040).There is a correlation between the SR of composite materials with different organic contents and SMBA. It can be stated that the Bis-GMA based composite material has clinically acceptable physical properties due to its low SR and S. mutans adhesion
- …