Response of human pulps following acid conditioning and application of a bonding agent in deep cavities

Objectives. The aim of this in vivo study was to evaluate the human dental pulp response when a one-bottle adhesive system was applied on etched or unetched deep dentine.Methods. Eighteen class V deep cavity preparations were divided in three groups: group 1-total etching + two coats of single bond (SB) + composite resin (Z-100); group 2-enamel etching + two coats of SB + Z-100, group 3-cavity floor lined with a calcium hydroxide liner (Dycal) + acid-etching of enamel and lateral walls + two coats of SB + Z-100. Two teeth were used as intact control group. After 30 days the teeth were extracted and processed through H and E, Masson's trichrome and Brown and Brenn staining techniques.Results. Moderate inflammatory response, disorganization of pulp tissue, as well as, deposition of thin layer of reactionary dentin were observed in group 1 teeth in which the remaining dentin thickness (RDT) was less than 300 mum. These histological findings appear to be related to long resin tags formation and bonding agent diffusion through dentinal tubules. In group 2, slight inflammatory response was observed only in one tooth in which the RDT was 162 mum. In group 3, all the teeth showed normal histological characteristics which were similar to the intact control group. Presence of bacteria was not correlated with the intensity of pulpal response. The patients reported no symptoms during the experiment. Radiographic evaluation showed no periapical pathology for any of the teeth,Significance and conclusions. Acid-etched deep dentin (RDT less than 300 mum) lined with SB causes more intense pulpal response than unetched deep dentin. Based on the results observed in the present study and the conditions in which it was carried out, we recommend the application of a biocompatible liner before etching deep dentin and applying SB. (C) 2002 Academy of Dental Materials. Published by Elsevier B.V. Ltd. All rights reserved

In vivo evaluation of the biocompatibility of three current bonding agents

The aim of this in vivo study was to evaluate the biocompatibility of three current bonding agents and calcium hydroxide cement. Sixty polyethylene tubes filled with the following materials: Group 1: Prime & Bond NT (PB - Dentsply, US; Group 2: Bond 1 (BO - Jeneric/Pentron, US); Group 3: Optibond Solo (OP - Kerr, US); and Group 4 (control): calcium hydroxide cement - Dycal (CH - Dentsply, US) were implanted into the connective tissue of 30 rats. After 15, 30 and 60 days, the implants were excised and the animals sacrificed. The biopsies were immersed in Karnovsky (pH, 7.2) fixative solution for 48 hours, and processed using routine histological technique. Six-micron-thick sections were cut and stained with hematoxilin and eosin and Masson's trichome technique. Microscopic evaluation was used to compare the connective tissue reactions caused by the experimental and control materials adjacent to the tube opening. At 15 days, the experimental and control materials triggered a moderate to intense inflammatory response which gave rise to a thick capsule adjacent to the tube opening. With time, the inflammatory reaction decreased. At 60 days, the connective tissue adjacent to the bonding agents exhibited a persistent inflammatory response mediated by macrophages and giant cells which were engulfing displaced resin components. on the other hand, for the control group (calcium hydroxide) no inflammatory response associated with a thin capsule adjacent to the material was observed even at the 30-day period. The hard-setting calcium hydroxide cement allowed complete healing and was considered more biocompatible than the bonding agents

Biocompatibility of an adhesive system and 2-hydroxyethylmethacrylate

The aim of the study was to evaluate the biocompatibility of an adhesive system and a resin component when implanted into connective tissue of rats. Forty sponges embedded in both materials: Scotchbond MP (SBMP/3M - Group A) and 2 - hydroxyethyl-methacrylate (HEMA - Group B), were implanted into dorsal connective tissue of 20 animals. After 7, 15, 30, or 60 days of the implantation, the animals were sacrificed; implant sites were excised and immersed for 24 hours in Kamovisky's fixative. The samples were processed under routine histologic technique, being stained with H & E. Histological evaluation showed that both materials promoted at 7 days intense inflammatory response with predominance of neutrophils and macrophages. The intense connective reaction was replaced for fibroblastic proliferation associated with macrophages and foreign body giant cells over time. The persistent moderate inflammatory reaction adjacent to scattered fragments of materials was greater to HEMA than to the SBMP. Both experimental materials did not show acceptable biocompatibility with connective tissue of rats in spite of allowing an evident connective tissue healing

Biocompatibility of a resin-modified glass-ionomer cement applied as pulp capping in human teeth

Purpose: to evaluate the human pulp response following pulp capping with calcium hydroxide (CI-I, Group 1), and the resin-modified glass-ionomer Vitrebond (VIT, Group 2). Materials and Methods: Intact teeth with no cavity preparation were used as control Group (ICG, Group 3). Buccal Class V cavities were prepared in 34 sound human premolars. After exposing the pulps, the pulp capping materials were applied and the cavities were Filled using Clearfil Liner Bond 2 bonding agent and Z100 resin-based composite. The teeth were extracted after 5, 30, and from 120 to 300 days, fixed in 10% buffered formalin solution, and prepared according to routine histological techniques. 6-mu m sections were stained with hematoxylin and eosin, Masson's trichrome, or Brown gr Brenn technique for bacterial observation. Results: At 5 days, CH caused a large zone of coagulation necrosis, the mononuclear inflammatory reaction underneath the necrotic zone was slight to moderate. VIT caused a moderate to intense inflammatory pulp response with a large necrotic zone. A number of congested venules associated with plasma extravasation and neutrophilic infiltration was observed. Over time, only CH allowed pulp repair and complete dentin bridging around the pulp exposure site. VIT components displaced into the pulp tissue triggered a persistent inflammatory reaction which appeared to be associated with a lack of dentin bridge formation. After 30 days a few histological sections showed a number of bacteria on the lateral dentin walls. In these samples the pulp response was similar to those samples with no microleakage. VIT was more irritating to pulp tissue than CH, which allowed pulp repair associated with dentin bridge formation. These results suggested that VIT is not an appropriate dental material to be used in direct pulp capping for mechanically exposed human pulps

Short-term evaluation of the pulpo-dentin complex response to a resin-modified glass-ionomer cement and a bonding agent applied in deep cavities

Objectives. To evaluate the response of the pulpo-dentin complex following application of a resin-modified glass-ionomer cement or an adhesive system in deep cavities performed in human teeth.Methods. Deep class V cavities were prepared on the buccal surface of 26 premolars. In Group I the cavity walls (dentin) and enamel were conditioned with 32% phosphoric acid and the dentin adhesive system One Step (Bisco, Inc., Itasca, IL, USA) was applied. In Groups 2 and 3, before total etching and application of bonding agent, the cavity floor was lined with the resin-modified glass-ionomer cement-Vitrebond (3M ESPE Dental Products Division, St. Paul, MN, USA) or the calcium hydroxide cement-Dycal (control group, Dentsply, Mildford, DE, USA), respectively. The cavities were restored using light-cured Z-100 composite resin (3M ESPE). The teeth were extracted between 5 and 30 days and prepared for microscopic assessment. Serial sections were stained with H/E, Masson's trichrome, and Brown and Brenn techniques.Results. In Group 1, the inflammatory response was more evident than in Groups 2 and 3. Diffusion of dental material components across dentinal tubules was observed only in Group 1, in which the intensity of the pulp response increased as the remaining dentin thickness decreased. Bacteria were evidenced in the lateral walls of two samples (Group 2) which exhibited no inflammatory response or tissue disorganization.Conclusions. Based on the experimental conditions, it was concluded total acid etching followed by application of One Step bonding agent cannot be recommended as adequate procedures. In this clinical condition the cavity walls should be lined with a biocompatible dental material, such as Vitrebond or Dycal. 2003 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved