Anharmonic effects in ZnO optical phonons probed by Raman spectroscopy

We report Raman spectroscopy measurements on ZnO crystals grown by the vapor transport method and annealed. Vacuum annealing is found to yield single crystals with ultra low density of defects. We focus on the optical E2 phonon linewidth temperature dependence in the 10?500 K range. The linewidth decrease at low temperature is analyzed and discussed in the light of anharmonic up- and down-conversion processes, unveiling strongly different behaviors for the two E2 phonons

White light emission from lead-free mixed-cation doped Cs2SnCl6 nanocrystals

We have designed a synthesis procedure to obtain Cs2SnCl6 nanocrystals (NCs) doped with metal ion(s) to emit visible light. Cs2SnCl6 NCs doped with Bi3+, Te4+ and Sb3+ ions emitted blue, yellow and red light, respectively. In addition, NCs simultaneously doped with Bi3+ and Te4+ ions were synthesized in a single run. Combination of both dopant ions together gives rise to the white emission. The photoluminescence quantum yields of the blue, yellow and white emissions are up to 26.5, 28, and 16.6%, respectively under excitation at 350, 390, and 370 nm. Pure white-light emission with CIE chromaticity coordinates of (0.32, 0.33) and (0.32, 0.32) at 340 and 370 nm excitation wavelength, respectively, was obtained. The as-prepared NCs were found to demonstrate a long-time stability, resistance to humidity, and an ability to be well-dispersed in polar solvents without property degradation due to their hydrophilicity, which could be of significant interest for wide application purposes