Improvement of High Temperature Oxidation of Low Carbon Steel Exposed to Ethanol Combustion Product at 700 °C by Hot-dip Aluminizing Coating

Low carbon steel (AISI 1005) was coated by hot-dipping into a molten Al-10% Si bath at 700 °C for 18s. After hotdipping treatment, the coating layers consisted of Al, Si, FeAl3, τ5-Fe2Al8Si, and Fe2Al5. The bare steel and thealuminized steel were isothermally oxidized at 700 °C in ethanol combustion product at atmospheric pressure for 49 h. The aluminized steel shows good performance in high temperature oxidation because the formation of Al2O3 layer on the coating surface. The growth of iron oxide nodules on the surface coating was accelerated by rapid outward diffusion of Fe-ions due to the presence of H2O-vapour generated by ethanol combustion. Thus, the oxidation rate of aluminized steel increased, resulting in a substantial mass-gain as the oxidation time increased. After longer exposure, the τ1-(Al,Si)5Fe3 phase was completely transformed to the FeAl in the outer layer. The FeAl formed near the steel substrate was due to Fe-atoms diffusing into the Fe2Al5 layer when the time and temperature increased

Studi Perilaku Kegagalan Sambungan Las Tipe TConjunctions Pada Baja Karbon Rendah Dengan Pendekatan Experimen Dan Numerik

This research is conducted to investigate failure behavior of welding structure in T-conjunctions type. Welding joint failures were analyzed by both experimental and finite element analysis (2D) approach in terms of stress intensity factor mode I (KI). The stress at the welding zone was strongly influenced by specimen geometries and the ratio of L/h1. The stress intensity factor (SIF) was increased significantly. Whereas, the minimum SIF of specimen #X1 and #Y3 are 58 MPa.√m and 165 MPa.√m, respectively. Failure of welding specimen was more dominated in the zone with the highest stress concentration and also affected by material discontinuity at which the stress was not generated continuously, but localized in any certain area. Specimen without welding did not yield a maximum stress. However, plastic zone formation locally decreases the stress concentration. Discontinuity in the welding specimen does not give rise to plastic stream, thus it will raise the stress concentration at the welding extension region. Discontinuity can be observed by the Von Misses stress pattern at stress welding zone for the welding specimen whereas the specimen without welding was only occurred near the extension zone

Perbandingan Hidrodinamika Flokulator Berbentuk Setengah Lingkaran Dan Persegi Panjang Pada Proses Flokulasi Menggunakan Aliran Melaluimedia Kelereng

Teori Camp & Stein menyebutkan bahwa untuk mendapatkan hasil flokulasi yang baik harus memenuhi nilai Gtd tertentu. Tetapi dalam flokulasi melalui media berbutir dengan nilai Gtd yang relatif lebih rendah dari yang disyaratkan telah didapatkan hasil flokulasi yang baik. Berdasarkan hal tersebut maka diduga ada faktor lain yang berpengaruh pada proses flokulasi menggunakan aliran melalui media berbutir selain Gtd.Penelitian ini bertujuan untuk mengetahui kinerja dari dua buah flokulator dengan media kelereng dalam aplikasinya sebagai flokulator dan mengetahui aspek hidrodinamika yang berpengaruh dalam flokulasi. Flokulator yang digunakan adalah flokulator saluran terbuka berbentuk setengah lingkaran dan flokulator saluran terbuka berbentuk persegi panjang. Variasi debit yang digunakan adalah 1 liter/menit, 1,5 liter/menit, 1,7 liter/menit, 2 liter/menit, dan 2,2 liter/menit. Metode analisis hasil penelitian yang digunakan adalah berupa analisis laboratorium dan analisis perhitungan.Penurunan kekeruhan dengan air baku buatan mencapai lebih dari 98%, dan 94,49% untuk air baku alami. Penurunan kadar organik mencapai 65,23% dan 38,10% untuk penurunan TSS. Angka kehilangan tekan yang terjadi pada flokulator berbentuk setengah lingkaran berkisar antara 0,20 hingga 6,95 cm, dan 0,60 hingga 7,85 cm untuk flokulator berbentuk persegi panjang. Nilai G berkisar antara 33,035 hingga 166,751/detik dan nilai Gtd berkisar antara 306,464 hingga 25304,741. Bilangan Reynolds yang diperoleh berkisar antara 245,392 hingga 708,225. Nilai bilangan Froude untuk kedua flokulator berkisar antara 0,030 hingga 0,064. Angka kecepatan gerusan pada flokulator berbentuk setengah lingkaran berkisar antara 0,026 hingga 0,033 cm/detik, dan antara 0,020 hingga 0,025 cm/detik untuk flokulator berbentuk persegi panjang. Waktu detensi aktual untuk kedua flokulator lebih kecil jika dibandingkan dengan waktu detensi teoritisnya

Pengaruh Kadar Karbon Dalam Baja Pada Proses Pelapisan Aluminium Celup Panas

Carbon steel is widely used as a component of engineering work in high temperature conditions. During the application decreases of oxidation resistance drastically. A steel coating is very needed to increase an oxidation resistance. One technique is inexpensive and used to be coating for large components are hot dip coating. This experiment aimed to determine the effect of carbon content in steel AISI 1020, AISI 1045 and AISI 1090 against hot dip aluminium coating on hot dip aluminium coating process and to study the influence of immersion time in the tub aluminium molten steel on the growth of intermetallic layer. Immersion times used were 4, 9, and 16 seconds with a temperature of 700 °C. Volume composition used for each solution is 100 ml flux with three variations, namely Y1 flux ( 1.5 g KF, NaF 1.5 g, 8.5 g Borax , and 2.5 g of acetic acid ), Y2 ( 2.0 KF g, 2.0 g NaF, 9.5 g Borax, and 3.0 acetic acid ) and Y3 ( 2.5 g of KF, 2.5 g NaF, 10 g Borax, 3.5 g acetic acid ). Then do the impact test , SEM , OM and XRD. For the most thick aluminium layer was AISI 1020 steel with immersion time of 4 seconds is 0.118 mm and Fe - Al intermetallic layer ( FeAl3+Fe2Al5 ) is the thickest on AISI 1045 steel with immersion time of 9 seconds. Energy values were greatest impact on AISI 1020 steel is 187.2 J, means less carbon content of the energy generated greater impact

Posisi Indonesia pada Kerja Sama Energi Regional dalam Memasuki Era Masyarakat Ekonomi ASEAN Studi Kasus: ASEAN Power Grid

ASEAN Power Grid merupakan sebuah kerja sama interkoneksi listrik ASEAN yang telah diamanatkan pada tahun 1997 di bawah Visi ASEAN 2020. Selain itu, percepatan pembangunan ASEAN Power Grid juga dicantumkan dalam cetak biru Masyarakat Ekonomi ASEAN menuju 2015. ASEAN menyadari bahwa energi memiliki peranan penting dalam medukung aktivitas ekonomi, termasuk listrik. Namun, sampai pada tahun 2015 realisasi pembangunan ASEAN Power Grid masih belum mengalami kemajuan yang signifikan. Sebagai pengguna energi terbesar di ASEAN dan aktivitas ekonomi serta industri yang terus berkembang, kerja sama ASEAN Power Grid ini dapat dimanfaatkan untuk memenuhi kebutuhan pasokan energi dalam memasuki era Masyarakat Ekonomi ASEAN. Di Indonesia belum ada ASEAN Power Grid yang sudah selesai terinterkoneksi, namun proyek interkoneksi listrik tersebut sedang dalam konstruksi sebesar 600 MW yang akan menghubungkan Sumatra dengan Malaysia, dan sebesar 230 MW yang akan menghubungkan Kalimantan dengan Serawak. Adapun interkoneksi yang akan mengubungkan Batam – Singapura, serta Singapura – Sumatera yang masing-masing sebesar 600 MW masih dalam tahap perencanaan. Tujuan dari penelitian ini adalah untuk meninjau kembali posisi Indonesia pada kerja sama enerhi regional demi mempersiapkan diri dalam memasuki era Masyarakat Ekonomi ASEAN. Metode yang digunakan dalam penelitian ini adalah deskriptif kualitatif dengan jenis penelitian studi kasus. Hasil penelitian ini menemukan bahwa Indonesia, melalui HAPUA, telah berupaya dalam melakukan realisasi atas komitmen perwujudan ASEAN Power Grid. Namun, oleh karena adanya kendala, maka realisasi ASEAN Power Grid di Indonesia cenderung bergerak lambat. Adapun pola kerja ASEAN Power Grid, yaitu melibatkan ASEAN sebagai institusi supra nasional, investor sebagai aktor non negara, dan negara anggota ASEAN sebagai aktor negara

DEKONSTRUKSI KONSEP KEPEMIMPINAN KARAENG PATTINGALLOANG DALAM DRAMA KARAENG PATTINGALLOANG KARYA FAHMI SYARIFF

This paper aims to deconstruct the leadership of Karaeng Pattingalloang. as the center of leadership and the roles of subordinates around it. The presence of Karaeng Pattinggaloang has also undergone a process of meaning and has become the value of leadership itself. This research also uses descriptive research and then analyzes it. Data was collected from various sources of literature study. This data is managed to be analyzed to find the meaning of the drama text Karaeng Pattingalloang. The results show that there is a leader-subordinate binary opposition. This hierarchical binary opposition is then disassembled by deconstructing readings so that the angle that is considered to be the bottom position of the first binary shows that the two support each other. Leadership does not stand alone. Instead, subordinates have a central role to support leadership.