Review of Dental Impression Materials

Major advances in impression materials and their application have occurred during the last decade, with greater emphasis being placed on rubber impression materials than on dental compound, zinc oxide-eugenol, and agar and alginate. Of particular interest has been the effect of disinfection solutions on the qualities of impressions and the biocompatibility of impression materials. The principal advance in hydrocolloids has been the introduction of the agar/alginate impression technique, which has simplified the procedure and improved the quality of gypsum dies compared with those prepared in alginate impressions. The tear strength of some alginates has been improved, and some have been formulated so that the powder is dustless, thus reducing the health hazard as a result of patient inhalation of dust during the dispensing process. Polyether and silicone impression materials have been modified so that the working time, viscosity, and flexibility of the polyethers have been improved and, with the introduction of addition silicones, their accuracy has become exceptional. Although the early addition silicones liberated hydrogen after setting, thus delaying the pouring of models and dies, most addition silicones have been improved so that no hydrogen is released and dies can be poured immediately. The introduction of automatic mixing systems for addition silicones has simplified their manipulation, has reduced the number of voids in impressions, and has reduced the amount of material wasted. The incorporation of surfactants into addition silicones has made them hydrophilic, with wetting properties similar to those of polyethers, and has made pouring bubble-free gypsum dies easier. This review is confined to published and unpublished information of the past decade. It will also suggest trends that should be anticipated in the near future based on this information. The review will not present information developed before 1975, which is available in several textbooks on dental materials by Craig (1985a), Phillips (1982), and Williams and Cunningham (1979).Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/66604/2/10.1177_08959374880020012001.pd

Sorption and solubility of 12 soft denture liners,

The long-term stability of a soft denture liner depends to a large extent on the sorption and solubility of the liner. Because sorption and solubility are accompanied by a volumetric change, bacterial infestation, hardening, and color change, it is a physical property of importance. The purpose of this investigation was to determine the sorption and solubility of 12 soft denture liners (Verno-Soft, Super Soft, ProTech, Soft-Pak, Flexor, Novus, Molloplast-B, Durosoft, Justi Soft, Velvesoft, VinaSoft and Prolastic). They include nine copolymers, two silicones and one polyphosphazene fluoroelastomer. The sorption and solubility test was performed as outlined in American Dental Association (ADA) specification 12 for denture base polymers. Five specimens of each material were tested and data were collected at 1 week, 1 month, 3 months, 6 months, and 1 year. Sorption data varied from 0.2 to 5.6 mg/cm2 at 1 week; 0.3 to 12.5 mg/cm2 at 1 month; 0.1 to 22.0 mg/cm2 at 3 months; 0,1 to 13.6 mg/cm2 at 6 months; and 0.1 to 35.7 mg/cm2 at 12 months. Solubility data varied from 0,0 to 0.4 mg/cm2 at 1 week; 0.1 to 0.8 mg/cm2 at 1 month; +0.1 to 1.2 mg/cm2 at 3 months; 0.0 to 1.9 mg/cm2 at 6 months; and +0.2 to 2.3 mg/cm2 at 1 year. A statistical analysis of the data by two-way ANOVA and calculated Tukey intervals showed significant differences between materials at all time intervals. The results of this study have clinical implications because the sorption and solubility may affect the long-term life expectancy of the soft denture liner.Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/31265/1/0000171.pd

Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations Influência da intensidade de luz e métodos de fotoativação no selamento marginal de restaurações classe V em resina composta

The aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized class V cavities in all dentin margins. Teeth were divided into 5 equal groups according to the curing cycle. The cavities were incrementally restored with a composite resin (Single Bond/Z-100, 3M). Light curing was applied as follows: Group I: PAC light continuous-cycle curing at 1600 mW/cm² for 3s; Group II: PAC light step-cycle curing (2s at 800 mW/cm² then 4s at 1600 mW/cm²); Group III: QTH light continuous-cycle curing at 400 mW/cm² for 40s; Group IV: QTH light ramp-cycle curing (from 100 to 600 mW/cm² in 15s followed by 25s at 600 mW/cm²); Group V: QTH light pulse-delay curing (200 mW/cm² for 3s followed by 3 min delay then 600 mW/cm² for 30s). Teeth were stored in distilled water at 37ºC for 30 days and then subjected to thermocycling for 500 cycles at 5 and 55ºC. Root apices were sealed and teeth coated with nail varnish before they were immersed in 0.5% fuchsine red dye solution. Teeth were then sectioned and slices were scanned with a computer scanner to determine the area of dye leakage using a computer program (Image Tools). Images of tooth slices were also visually examined under magnification and dye penetration along the tooth/restoration interface was scored. Significant differences in the degree of dye penetration and leakage were detected between groups (p<.05). Groups I and II had significantly higher values of dye penetration and leakage than groups III, IV and V. In conclusion, the use of PAC light curing in a continuous or step cycle modes resulted in increased microleakage of Class V resin composite restorations compared with medium intensity QTH light curing. Pulse, ramp and continuous-cycle curing modes with QTH light resulted in similar degrees of microleakage.<br>O objetivo deste estudo foi determinar o efeito da polimerização gradual, mediante a utilização de aparelhos de Quartzo-Tungustênio-Halógena (QTH) e Arco de Plasma de Xenônio (PAC), no selamento marginal de restaurações classe V em resina composta com margens localizadas em dentina. Setenta e cinco incisivos bovinos receberam preparos de cavidades classe V, na raiz, com o intuito de situar as margens cavitárias em dentina. Os dentes foram divididos em cinco grupos de acordo com o método de fotoativação. As cavidades, depois de condicionadas, foram tratadas com o sistema adesivo Single Bond (3M Dental) e restauradas com a resina composta Z100 (3M Dental) pela técnica incremental. A fotoativação foi realizada para cada grupo como descrito a seguir: Grupo I: PAC pelo método de fotoativação constante: 1600mW/cm² - 3s; Grupo II: PAC pelo método de fotoativação por passos (800mW/cm² - 2s, subindo automaticamente para 1600mW/cm² - 4s); Grupo III: QTH pelo método de fotoativação constante: 400 mW/cm² - 40s; Grupo IV: QTH pelo método de fotoativação em rampa: 100 a 600 mW/cm² - 15s, permanecendo a 600mW/cm2 por mais 25s; Grupo V: QTH pelo método de fotoativação por pulso: 200 mW/cm² - 3s, tempo de espera de 3min.e a seguir 600mW/cm² - 30s. Os dentes foram armazenados em água destilada a 37ºC por 30 dias e então submetidos à ciclagem térmica, por 500 ciclos à 5 ºC e 55 ºC. Os ápices dos dentes foram selados com resina composta e os dentes foram cobertos com duas camadas de esmalte para unha, antes da sua imersão em fucsina básica a 0,5%. Os dentes foram seccionados e os cortes foram escaneados para avaliação da área infiltrada por corante por um programa de computador (Image Tools). Os cortes foram também visualizados com lupa para a determinação do grau de penetração do corante na interface dente-restauração por escores. Diferenças estatisticamente significantes foram observadas entre os grupos quanto ao grau e à área de penetração de corante (p < 0,05). Os grupos I e II apresentaram valores significantemente mais altos de infiltração e penetração do corante que os grupos III, IV e V. Em conclusão, o uso da fonte de PAC, no modo constante e por passos, resultou em valores significantemente maiores de infiltração marginal quando comparados com a intensidade de luz média emitida pelos aparelhos de QTH. Os métodos de fotoativação por pulso, rampa e continuo com a fonte de QTH resultaram num grau similar de microinfiltração