Correlation between metal-ceramic bond strength and coefficient of linear thermal expansion difference

The purpose of this study was to evaluate the metal-ceramic bond strength (MCBS) of 6 metal-ceramic pairs (2 Ni-Cr alloys and 1 Pd-Ag alloy with 2 dental ceramics) and correlate the MCBS values with the differences between the coefficients of linear thermal expansion (CTEs) of the metals and ceramics. Verabond (VB) Ni-Cr-Be alloy, Verabond II (VB2), Ni-Cr alloy, Pors-on 4 (P), Pd-Ag alloy, and IPS (I) and Duceram (D) ceramics were used for the MCBS test and dilatometric test. Forty-eight ceramic rings were built around metallic rods (3.0 mm in diameter and 70.0 mm in length) made from the evaluated alloys. The rods were subsequently embedded in gypsum cast in order to perform a tensile load test, which enabled calculating the CMBS. Five specimens (2.0 mm in diameter and 12.0 mm in length) of each material were made for the dilatometric test. The chromel-alumel thermocouple required for the test was welded into the metal test specimens and inserted into the ceramics. ANOVA and Tukey's test revealed significant differences (p=0.01) for the MCBS test results (MPa), with PI showing higher MCBS (67.72) than the other pairs, which did not present any significant differences. The CTE (10-6 oC-1) differences were: VBI (0.54), VBD (1.33), VB2I (-0.14), VB2D (0.63), PI (1.84) and PD (2.62). Pearson's correlation test (r=0.17) was performed to evaluate of correlation between MCBS and CTE differences. Within the limitations of this study and based on the obtained results, there was no correlation between MCBS and CTE differences for the evaluated metal-ceramic pairs.FAPES

Quality of martensitic stainless steel type AISI-420 utilized in the manufacture surgical implements

Até o presente momento, o aço inoxidável martensítico do tipo AISI-420 é muito utilizado na confecção de ferramentas cirúrgicas. Tais ferramentas vêm apresentando corrosão prematura, identificada após processo de limpeza e esterilização, perda de corte e/ou quebra durante os processos cirúrgicos. Esse trabalho avalia esse aço sobre à composição química, dureza, microestrutura e resistência à corrosão por pite em solução de detergente enzimático diluída em água por polarização cíclica anódica. Essa mistura é utilizada na limpeza das ferramentas que são submersas por 2h nessa solução antes da lavagem e esterilização. Os resultados mostram aços com microestrutura composta de martensita com fase ferrita e impurezas. Os referidos aços apresentam baixos valores de potencial de pite em comparação aos aços com microestrutura totalmente martensítica que possuem maiores valores.Until now the martensitic stainless steel type AISI-420 is widely used in the manufacture of surgical implements. These implements present premature corrosion problems identified after cleaning, , sterilization and cutting edge loss and/or rupture during the surgical processes. This study evaluates the steel as to the chemical composition, hardness, microstructure and pitting corrosion resistance in a solution of enzyme detergent diluted in water by anodic cyclic polarization. This mixture is used in the cleaning of surgical implements that are submerged in this solution for 2 h before cleaning and sterilization. The results show steels with martensite microstructures in the ferrite phase, together wth impurities. These presented low pitting potential values in compariston to steels with a fully martensitic microstructure.Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior (CAPES)CNPqFAPES

Effects of aluminum-copper alloy filtration on photon spectra, air kerma rate and image contrast

This study evaluated the performance of aluminum-copper alloy filtration, without the original aluminum filter, for dental radiography in terms of x-ray energy spectrum, air kerma rate and image quality. Comparisons of various thicknesses of aluminum-copper alloy in three different percentages were made with aluminum filtration. Tests were conducted on an intra-oral dental x-ray machine and were made on mandible phantom and on step-wedge. Depending on the thickness of aluminum-copper alloy filtration, the beam could be hardened and filtrated. The use of the aluminum-copper alloy filter resulted in reductions in air kerma rate from 8.40% to 47.33%, and indicated the same image contrast when compared to aluminum filtration. Aluminum-copper alloy filtration may be considered a good alternative to aluminum filtration.Este estudo avaliou a redução da taxa de kerma no ar, o espectro de energia dos raios X e alterações na qualidade da imagem radiográfica. Comparações com várias espessuras do filtro de liga de alumínio-cobre em três diferentes porcentagens foram feitas com o filtro de alumínio. Os experimentos foram feitos utilizando-se um aparelho de raios X odontológico convencional, obtendo radiografias com auxílio de um fantoma de segmento de mandíbula e de uma escala de densidade confeccionada com alumínio laminado. Dependendo da espessura da filtração da liga de alumínio-cobre, o feixe de raios X pôde ser endurecido em relação ao filtro de alumínio. O uso do filtro de liga de alumínio-cobre resultou em 8,40% a 47,33% de redução da taxa média de kerma no ar e indicou contraste da imagem radiográfica sem alteração, quando comparado com a filtração de alumínio, mostrando que os filtros de liga de alumínio-cobre tornam-se alternativas aceitáveis em relação aos filtros de alumínio.214219Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES

Effects of aluminum-copper alloy filtration on photon spectra, air kerma rate and image contrast

Este estudo avaliou a redução da taxa de kerma no ar, o espectro de energia dos raios X e alterações na qualidade da imagem radiográfica. Comparações com várias espessuras do filtro de liga de alumínio-cobre em três diferentes porcentagens foram feitas com o filtro de alumínio. Os experimentos foram feitos utilizando-se um aparelho de raios X odontológico convencional, obtendo radiografias com auxílio de um fantoma de segmento de mandíbula e de uma escala de densidade confeccionada com alumínio laminado. Dependendo da espessura da filtração da liga de alumínio-cobre, o feixe de raios X pôde ser endurecido em relação ao filtro de alumínio. O uso do filtro de liga de alumínio-cobre resultou em 8,40% a 47,33% de redução da taxa média de kerma no ar e indicou contraste da imagem radiográfica sem alteração, quando comparado com a filtração de alumínio, mostrando que os filtros de liga de alumínio-cobre tornam-se alternativas aceitáveis em relação aos filtros de alumínio.This study evaluated the performance of aluminum-copper alloy filtration, without the original aluminum filter, for dental radiography in terms of x-ray energy spectrum, air kerma rate and image quality. Comparisons of various thicknesses of aluminum-copper alloy in three different percentages were made with aluminum filtration. Tests were conducted on an intra-oral dental x-ray machine and were made on mandible phantom and on step-wedge. Depending on the thickness of aluminum-copper alloy filtration, the beam could be hardened and filtrated. The use of the aluminum-copper alloy filter resulted in reductions in air kerma rate from 8.40% to 47.33%, and indicated the same image contrast when compared to aluminum filtration. Aluminum-copper alloy filtration may be considered a good alternative to aluminum filtration.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES