Experimental measurement of stress at a four-domain junction in lead zirconate titanate

A junction between two lamellar bands of ferroelectric domains in a lead zirconate titanate (PZT) ceramic is analysed using Kikuchi diffraction patterns in the transmission electron microscope. Indexing of the diffraction patterns allowed the determination of the 3D relative orientation of the 4 different domains at the junction and thus the characterisation of the domain boundaries. The local c/a ratio could also be determined from the misorientations at the domain boundaries. Analysis of the data showed that large stresses were concentrated at the junction, and that this is inevitable at such band junctions. Such stress concentrations could act as nuclei for cracking of the ceramic under additional loading in service, perhaps particularly as a consequence of extended electromechanical cycling. Moreover, the stresses would increase with increasing c/a making the issues all the more serious for Ti-rich compositions having larger c/a ratios

Feasibility and Limitations of High-Voltage Lithium-Iron-Manganese Spinels

Positive electrodes with high energy densities for Lithium-ion batteries (LIB) almost exclusively rely on toxic and costly transition metals. Iron based high voltage spinels can be feasible alternatives, but the phase stabilities and optimal chemistries for LIB applications are not fully understood yet. In this study, LiFe$_{x}$Mn$_{2-x}$O$_{4}$ spinels with x = 0.2 to 0.9 were synthesized by solid-state reaction at 800 °C. High-resolution diffraction methods reveal gradual increasing partial spinel inversion as a function of x and early secondary phase formation. Mössbauer spectroscopy was used to identify the Fe valences, spin states and coordination. The unexpected increasing lattice parameters with Fe substitution for Mn was explained considering the anion-cation average bond lengths determined by Rietveld analysis and Mn$^{3+}$ overstoichiometries revealed by cyclic voltammetry. Finally, galvanostatic cycling of Li-Fe-Mn-spinels shows that the capacity fading is correlated to increased cell polarization for higher upper charging cut-off voltage, Fe-content and C-rate. The electrolyte may also contribute significantly to the cycling limitations