Well controlled in length and highly aligned ZnO nanorods were grown on the gold-coated glass substrate by hydrothermal growth method. ZnO nanorods were functionalised with selective thallium (I) ion ionophore dibenzyldiaza-18-crown-6 (DBzDA18C6). The thallium ion sensor showed wide linear potentiometric response to thallium (I) ion concentrations ( M to  M) with high sensitivity of 36.87 ± 1.49 mV/decade. Moreover, thallium (I) ion demonstrated fast response time of less than 5 s, high selectivity, reproducibility, storage stability, and negligible response to common interferents. The proposed thallium (I) ion-sensor electrode was also used as an indicator electrode in the potentiometric titration, and it has shown good stoichiometric response for the determination of thallium (I) ion

Single nanowire-based UV photodetectors for fast switching

Relatively long (30 µm) high quality ZnO nanowires (NWs) were grown by the vapor-liquid-solid (VLS) technique. Schottky diodes of single NW were fabricated by putting single ZnO NW across Au and Pt electrodes. A device with ohmic contacts at both the sides was also fabricated for comparison. The current-voltage (I-V) measurements for the Schottky diode show clear rectifying behavior and no reverse breakdown was seen down to -5 V. High current was observed in the forward bias and the device was found to be stable up to 12 V applied bias. The Schottky barrier device shows more sensitivity, lower dark current, and much faster switching under pulsed UV illumination. Desorption and re-adsorption of much smaller number of oxygen ions at the Schottky junction effectively alters the barrier height resulting in a faster response even for very long NWs. The NW was treated with oxygen plasma to improve the switching. The photodetector shows high stability, reversibility, and sensitivity to UV light. The results imply that single ZnO NW Schottky diode is a promising candidate for fabricating UV photodetectors

Effect of intersubband scattering on weak localization in 2D systems

The theory of weak localization is generalized for multilevel 2D systems taking into account intersubband scattering. It is shown that weak intersubband scattering which is negligible in a classical transport, affects strongly the weak-localization correction to conductivity. The anomalous magnetoresistance is calculated in the whole range of classically low magnetic fields. This correction to conductivity is shown to depend strongly on the ratios of occupied level concentrations. It is demonstrated that at relatively low population of the excited subband, it is necessary to use the present theory because the high-field limit asimptotics is shown to be achieved only in classical magnetic fields.Comment: 18 pages, 4 figures. Accepted to Phys. Rev. B 6

The Synthesis of NiO/TiO 2

In this work, a heterojunction based on p-type NiO/n-type TiO2 nanostructures has been prepared on the fluorine doped tin oxide (FTO) glass substrate by hydrothermal method. Scanning electron microscopy (SEM) and X-Ray diffraction techniques were used for the morphological and crystalline arrays characterization. The X-ray photoelectron spectroscopy was employed to determine the valence-band offset (VBO) of the NiO/TiO2 heterojunction prepared on FTO glass substrate. The core levels of Ni 2p and Ti 2p were utilized to align the valence-band offset of p-type NiO/n-type TiO2 heterojunction. The valence band offset was found to be ∼0.41 eV and the conduction band was calculated about ∼0.91 eV. The ratio of conduction band offset and the valence-band offset was found to be 2.21

Influence of helium-ion bombardment on the optical properties of ZnO nanorods/p-GaN light-emitting diodes

Light-emitting diodes (LEDs) based on zinc oxide (ZnO) nanorods grown by vapor-liquid-solid catalytic growth method were irradiated with 2-MeV helium (He+) ions. The fabricated LEDs were irradiated with fluencies of approximately 2 × 1013 ions/cm2 and approximately 4 × 1013 ions/cm2. Scanning electron microscopy images showed that the morphology of the irradiated samples is not changed. The as-grown and He+-irradiated LEDs showed rectifying behavior with the same I-V characteristics. Photoluminescence (PL) measurements showed that there is a blue shift of approximately 0.0347 and 0.082 eV in the near-band emission (free exciton) and green emission of the irradiated ZnO nanorods, respectively. It was also observed that the PL intensity of the near-band emission was decreased after irradiation of the samples. The electroluminescence (EL) measurements of the fabricated LEDs showed that there is a blue shift of 0.125 eV in the broad green emission after irradiation and the EL intensity of violet emission approximately centered at 398 nm nearly disappeared after irradiations. The color-rendering properties show a small decrease in the color-rendering indices of 3% after 2 MeV He+ ions irradiation

White Electroluminescence Using ZnO Nanotubes/GaN Heterostructure Light-Emitting Diode

We report the fabrication of heterostructure white light–emitting diode (LED) comprised of n-ZnO nanotubes (NTs) aqueous chemically synthesized on p-GaN substrate. Room temperature electroluminescence (EL) of the LED demonstrates strong broadband white emission spectrum consisting of predominating peak centred at 560 nm and relatively weak violet–blue emission peak at 450 nm under forward bias. The broadband EL emission covering the whole visible spectrum has been attributed to the large surface area and high surface states of ZnO NTs produced during the etching process. In addition, comparison of the EL emission colour quality shows that ZnO nanotubes have much better quality than that of the ZnO nanorods. The colour-rendering index of the white light obtained from the nanotubes was 87, while the nanorods-based LED emit yellowish colour