Macroporous silicon membranes as electron and x-ray transmissive windows

Macroporous silicon membranes are fabricated whose pores are terminated with 60 nm thin silicon dioxide shells. The transmission of electrons with energies of 5 kV-25 kV through these membranes was investigated reaching a maximum of 22% for 25 kV. Furthermore, the transmission of electromagnetic radiation ranging from the far-infrared to the x-ray region was determined. The results suggest the application of the membrane as window material for electron optics and energy dispersive x-ray detectors

Three-dimensional macroporous silicon photonic crystal with large photonic band gap

Three-dimensional photonic crystals based on macroporous silicon are fabricated by photoelectrochemical etching and subsequent focused-ion-beam drilling. Reflection measurements show a high reflection in the range of the stopgap and indicate the spectral position of the complete photonic band gap. The onset of diffraction which might influence the measurement is discussed

Evolution of the interface structure of bonded Si wafers after high temperature annealing

n/

Measurement of the Bending Strength of Vapor-Liquid-Solid Grown Silicon Nanowires

The fracture strength of silicon nanowires grown on a [111] silicon substrate by the vapor-liquid-solid process was measured. The nanowires, with diameters between 100 and 200 nm and a typical length of 2 μm, were subjected to bending tests using an atomic force microscopy setup inside a scanning electron microscope. The average strength calculated from the maximum nanowire deflection before fracture was around 12 GPa, which is 6% of the Young's modulus of silicon along the nanowire direction. This value is close to the theoretical fracture strength, which indicates that surface or volume defects, if present, play only a minor role in fracture initiation. © 2006 American Chemical Society