Microstructure, Elastic and Inelastic Properties of Partially Graphitized Biomorphic Carbons

The microstructural characteristics and amplitude dependences of the Young’s modulus E and internal friction (logarithmic decrement δ) of biocarbon matrices prepared by beech wood carbonization at temperatures Tcarb = 850–1600°C in the presence of a nickelcontaining catalyst have been studied. Using Xray diffraction and electron microscopy, it has been shown that the use of a nickel catalyst during carbon ization results in a partial graphitization of biocarbons at Tcarb ≥ 1000°C: the graphite phase is formed as 50 to 100nm globules at Tcarb = 1000°C and as 0.5 to 3.0μm globules at Tcarb = 1600°C. It has been found that the measured dependences E(Tcarb) and δ(Tcarb) contain three characteristic ranges of variations in the Young’s modulus and logarithmic decrement with a change in the carbonization temperature: E increases and δ decreases in the ranges Tcarb 1300°C; in the range 1000 < Tcarb < 1300°C, E sharply decreases and δ increases. The observed behavior of E(Tcarb) and δ(Tcarb) for biocarbons carbonized in the presence of nickel correlates with the evolution of their microstructure. The largest values of E are obtained for samples with Tcarb = 1000 and 1600°C. However, the samples with Tcarb = 1600°C exhibit a higher suscep tibility to microplasticity due to the presence of a globular graphite phase that is significantly larger in size and total volume.Peer reviewe