Texture analysis of thick bismuth ferrite lead titanate layers
The template grain growth technique was used to synthesis textured 60BiFeO3-PbTiO3(60:40BFPT) by using platelets of BaTiO3 as template. Synchrotron measurement clearly showed textured 60:40BFPT. Moreover, in situ high energy synchrotron radiation was employed to investigate the influence of an external electric filed on crystallographic structure of mixed phase 60:40BFPT. Application of an electric field ≥ 1 kV/mm resulted in phase transformation from mixed rhombohedral/tetragonal phases (≈ 73.5% tetragonal / 26.5% rhombohedral) to predominately tetragonal phase (≈ 95%) at applied field of 6 kV/mm. A crystallographic texture refinement was done by using software package materials analysis using diffraction (MAUD) with a 4th order spherical harmonic orientation distribution function (ODF). This refinement was completed using a P4mm+Cm structure model. Texture coefficients were constrained such that the equivalent texture coefficients of each phase are the same. The resulting texture refinement determined that sample has a 1.3 multiples of random distribution (MRD) {100} crystallographic texture
Correct use of non-indexed eGFR for drug dosing and renal drug-related problems at hospital admission
PURPOSE Two to seven percent of the German adult population has a renal impairment (RI) with an estimated glomerular filtration rate (eGFR) < 60 ml/min/1.73m2. This often remains unrecognized and adjustment of drug therapy is lacking. To determine renal function in clinical routine, the CKD-EPI equation is used to calculate an indexed eGFR (ml/min/1.73m2). For drug dosing, it has to be individualized to a non-indexed eGFR (ml/min) by the patient's body surface area. Here, we investigated the number of patients admitted to urological wards of a teaching hospital with RI between July and December 2016. Additionally, we correctly used the eGFRnon-indexed for drug and dosage adjustments and to analyse the use of renal risk drugs (RRD) and renal drug-related problems (rDRP).
METHODS In a retrospective observational study, urological patients with pharmacist-led medication reconciliation at hospital admission and eGFRindexed (CKD-EPI) of 15-59 ml/min/1.73m2 were identified. Indexed eGFR (ml/min/1.73m2) was recalculated with body surface area to non-indexed eGFR (ml/min) for correct drug dosing. Medication at admission was reviewed for RRD and based on the eGFRnon-indexed for rDRP, e.g. inappropriate dose or contraindication.
RESULTS Of 1320 screened patients, 270 (20.5%) presented with an eGFRindexed of 15–59 ml/min/1.73m2. After readjustment, 203 (15.4%) patients had an eGFRnon-indexed of 15–59 ml/min. Of these, 190 (93.6%) used ≥ 1 drugs at admission with 660 of 1209 (54.7%) drugs classified as RRD. At least one rDRP was identified in 115 (60.5%) patients concerning 264 (21.8%) drugs.
CONCLUSION Renal impairment is a common risk factor for medication safety in urologic patients admitted to a hospital. Considerable shifts were seen in eGFR-categories when correctly calculating eGFRnon-indexed for drug dosing purposes. The fact that more than half of the study patients showed rDRP at hospital admission underlines the need to consider this risk factor appropriately
Effects of dietary crude protein on the growth performance, carcass characteristics and serum biochemical indexes of Lueyang black-boned chickens from seven to twelve weeks of age
Crystallographic and magnetic investigations of textured bismuth ferrite lead titanate layers
In present work we demonstrate the synthesis of textured 60BiFeO3–40PbTiO3 (60:40 BFPT) by using the templated grain growth technique with platelets of BaTiO3. Synthesised 60:40 BFPT has been examined by High-energy x-ray diffraction utilizing a synchrotron x-ray source. The crystallographic structure refinement results revealed the co-existence of monoclinic and tetragonal phases. By employing an external electric field, the mixed monoclinic/tetragonal phases transformed to the predominantly tetragonal phase. In addition, a crystallographic texture refinement was completed on unpoled state of 60:40 BFPT which showed the sample had 1.3 multiples of random distribution (MRD) {100} crystallographic textured in tetragonal phase. However, magnetic measurements showed isotropic ferromagnetism for the sample which is not in agreement with the crystallographic texture properties of the sample. Low temperature magnetic transition has been found in zero field cooled—field cooled (ZFC-FC) measurements. This could be due to the possible existence of a secondary magnetic phase, which dominated the magnetic result
Recommended from our members
Residual stresses and microstructure within Allvac 718Plus laser powder bed fusion bars
The residual stresses within Allvac 718Plus bars built using LBPF with different laser powers, speeds and table displacements were measured using diffraction and mechanical methods and modelled with the baseplate attached and then removed. The residual stress profiles within the bars from the top surface down through the bulk were all quite similar, becoming less tensile due to a strain hardening mechanism. Table displacement has the greatest impact on residual stress, decreasing with increasing displacement/powder layer thickness. There was good agreement amongst the modeling and measurements. The microstructures were examined and varied slightly with energy density with higher densities having larger grains and enhanced post solidification diffusion. Energy density had minimal impact on the residuals stresses within the parameters to produce dense material
Characterization of thick bismuth ferrite-lead titanate films processed by tape casting and templated grain growth
The templated grain growth technique was used to synthesise textured 60BiFeO3–40PbTiO3 (60:40BFPT). Both Aurivillius (Bi4Ti3O12, PbBi4Ti4O15) and perovskite templates (BaTiO3, SrTiO3) were used to prepare 60:40BFPT. Only BaTiO3 templates were found to successful impart a texture to the ceramic matrix. In the case of perovskite templates, ferroelectricity was evident from saturated polarisation hysteresis loops. Saturated polarisation loops were achieved due to the substitution of Ba2+ or Sr2+, which reduces the coercive field. SrTiO3 and BaTiO3 templated ceramics showed remanent polarisation of 30 and 36 μC/cm2, respectively. Aurivillius templates did not generate ferroelectric materials. Because of their high chemical stability in this system, BaTiO3 templates appear to be the best candidate for fabricating textured BFPT by the reactive templated grain growth method