Thermal conductivity and thermal expansion of graphite fiber/copper matrix composites

The high specific conductivity of graphite fiber/copper matrix (Gr/Cu) composites offers great potential for high heat flux structures operating at elevated temperatures. To determine the feasibility of applying Gr/Cu composites to high heat flux structures, composite plates were fabricated using unidirectional and cross-plied pitch-based P100 graphite fibers in a pure copper matrix. Thermal conductivity of the composites was measured from room temperature to 1073 K, and thermal expansion was measured from room temperature to 1050 K. The longitudinal thermal conductivity, parallel to the fiber direction, was comparable to pure copper. The transverse thermal conductivity, normal to the fiber direction, was less than that of pure copper and decreased with increasing fiber content. The longitudinal thermal expansion decreased with increasing fiber content. The transverse thermal expansion was greater than pure copper and nearly independent of fiber content

Precipitation strengthened high strength, high conductivity Cu-Cr-Nb alloys produced by chill block melt spinning

A series of Cu-based alloys containing 2 to 10 a/o Cr and 1 to 5 a/o Nb were produced by chill block melt spinning (CBMS). The melt spun ribbons were consolidated and hot rolled to sheet to produce a supersaturated Cu-Cr-Nb solid solution from which the high melting point intermetallic compound Cr2Nb could be precipitated to strengthen the Cu matrix. The results show that the materials possess electrical conductivities in excess of 90 percent that of pure Cu at 200 C and above. The strengths of the Cu-Cr-Nb alloys were much greater than Cu, Cu-0.6 Cr, NARloy-A, and NARloy-Z in the as-melt spun condition. The strengths of the consolidated materials were less than Cu-Cr and Cu-Cr-Zr below 500 C and 600 C respectively, but were significantly better above these temperatures. The strengths of the consolidated materials were greater than NARloy-Z, at all temperatures. The GLIDCOP possessed similar strength levels up to 750 C when the strength of the Cu-Cr-Nb alloys begins to degrade. The long term stability of the Cu-Cr-Nb alloys was measured by the microhardness of aged samples and the growth of precipitates. The microhardness measurements indicate that the alloys overage rapidly, but do not suffer much loss in strength between 10 and 100 hours which confirms the results of the electrical resistivity measurements taken during the aging of the alloys at 500 C. The loss in strength from peak strength levels is significant, but the strength remains exceptionally good. Transmission electron microscopy (TEM) of the as-melt spun samples revealed that Cr2Nb precipitates formed in the liquid Cu during the chill block melt spinning, indicating a very strong driving force for the formation of the precipitates. The TEM of the aged and consolidated materials indicates that the precipitates coarsen considerably, but remain in the submicron range

Advanced materials for space nuclear power systems

The overall philosophy of the research was to develop and characterize new high temperature power conversion and radiator materials and to provide spacecraft designers with material selection options and design information. Research on three candidate materials (carbide strengthened niobium alloy PWC-11 for fuel cladding, graphite fiber reinforced copper matrix composites for heat rejection fins, and tungsten fiber reinforced niobium matrix composites for fuel containment and structural supports considered for space power system applications is discussed. Each of these types of materials offers unique advantages for space power applications

Cu-Cr-Nb-Zr Alloy for Rocket Engines and Other High-Heat- Flux Applications

Rocket-engine main combustion chamber liners are used to contain the burning of fuel and oxidizer and provide a stream of high-velocity gas for propulsion. The liners in engines such as the Space Shuttle Main Engine are regeneratively cooled by flowing fuel, e.g., cryogenic hydrogen, through cooling channels in the back side of the liner. The heat gained by the liner from the flame and compression of the gas in the throat section is transferred to the fuel by the liner. As a result, the liner must either have a very high thermal conductivity or a very high operating temperature. In addition to the large heat flux (>10 MW/sq m), the liners experience a very large thermal gradient, typically more than 500 C over 1 mm. The gradient produces thermally induced stresses and strains that cause low cycle fatigue (LCF). Typically, a liner will experience a strain differential in excess of 1% between the cooling channel and the hot wall. Each time the engine is fired, the liner undergoes an LCF cycle. The number of cycles can be as few as one for an expendable booster engine, to as many as several thousand for a reusable launch vehicle or reaction control system. Finally, the liners undergo creep and a form of mechanical degradation called thermal ratcheting that results in the bowing out of the cooling channel into the combustion chamber, and eventual failure of the liner. GRCop-84, a Cu-Cr-Nb alloy, is generally recognized as the best liner material available at the time of this reporting. The alloy consists of 14% Cr2Nb precipitates in a pure copper matrix. Through experimental work, it has been established that the Zr will not participate in the formation of Laves phase precipitates with Cr and Nb, but will instead react with Cu to form the desired Cu-Zr compounds. It is believed that significant improvements in the mechanical properties of GRCop-84 will be realized by adding Zr. The innovation is a Cu-Cr-Nb-Zr alloy covering the composition range of 0.8 to 8.1 weight percent Cr, 0.7 to 7.2 weight percent Nb, 0.1 to 1.5 weight percent Zr, and balance Cu. The alloy combines two known strengthening mechanisms - dispersion strengthening by Cr2Nb precipitates (GRCop-84), and precipitation strengthening by CuxZr (AMZIRC) - to produce a synergistic increase in the capabilities of the alloy with the goal of achieving properties greater than either of the methods could achieve alone. The anticipated advantages of the alloy are higher strength at temperatures up to 700 C, improved creep strength, and significantly higher LCF lives relative to GRCop-84. The thermal expansion, thermal conductivity, and processing of the alloy are anticipated to remain largely unchanged relative to GRCop-84

Effects of Long Term Thermal Exposure on Chemically Pure (CP) Titanium Grade 2 Room Temperature Tensile Properties and Microstructure

Room temperature tensile testing of Chemically Pure (CP) Titanium Grade 2 was conducted for as-received commercially produced sheet and following thermal exposure at 550 and 650 K for times up to 5,000 h. No significant changes in microstructure or failure mechanism were observed. A statistical analysis of the data was performed. Small statistical differences were found, but all properties were well above minimum values for CP Ti Grade 2 as defined by ASTM standards and likely would fall within normal variation of the material

Conductivity of GRCop-42 Alloy Enhanced

GRCop-84, a material developed at the NASA Glenn Research Center, has shown considerable promise for staged combustion rocket engine cycles such as the Space Shuttle Main Engine. However, for an expander cycle rocket engine, the transfer of heat to the fuel is a paramount factor in determining the efficiency of the engine. Examples of current and potential future expander cycle rocket engines are the Pratt & Whitney RL-10, RL-60, and RLX engines. Development of a higher conductivity version of GRCop-84 was undertaken to meet these needs. All expander cycle engines need a main combustion chamber liner with the maximum possible thermal conductivity. In an effort at Glenn to trade some of the greatly increased mechanical properties of GRCop-84 for improved thermal conductivity, the amounts of chromium and niobium were halved. The new Cu-4 at.% Cr-2 at.% Nb alloy was designated GRCop-42

Graphite/copper alloy interfacial energies determined using the sessile drop method

Graphite surfaces are not wet by pure copper. This lack of wetting is responsible for a debonding phenomenon that was found in continuous graphite fiber/copper matrix composites materials subjected to elevated temperatures. By suitably alloying copper, its capability to wet graphite surfaces can be enhanced. In situ measurements of graphite/copper alloy wetting angles were made using the sessile drop method. Interfacial energy values were calculated based upon these measurements

GRCop-84: A High Temperature Copper-based Alloy For High Heat Flux Applications

While designed for rocket engine main combustion chamber liners, GRCop-84 (Cu-8 at.% Cr-4 at.% Nb) offers potential for high heat flux applications in industrial applications requiring a temperature capability up to approximately 700 C (1292 F). GRCop-84 is a copper-based alloy with excellent elevated temperature strength, good creep resistance, long LCF lives and enhanced oxidation resistance. It also has a lower thermal expansion than copper and many other low alloy copper-based alloys. GRCop-84 can be manufactured into a variety of shapes such as tubing, bar, plate and sheet using standard production techniques and requires no special production techniques. GRCop-84 forms well, so conventional fabrication methods including stamping and bending can be used. GRCop-84 has demonstrated an ability to be friction stir welded, brazed, inertia welded, diffusion bonded and electron beam welded for joining to itself and other materials. Potential applications include plastic injection molds, resistance welding electrodes and holders, permanent metal casting molds, vacuum plasma spray nozzles and high temperature heat exchanger applications

Production and processing of Cu-Cr-Nb alloys

A new Cu-based alloy possessing high strength, high conductivity, and good stability at elevated temperatures was recently produced. This paper details the melting of the master alloys, production of rapidly solidified ribbon, and processing of the ribbon to sheet by hot pressing and hot rolling

MINIMIZING MARKET DURATION: THE STRATEGIC SELECTION OF THE LISTING BROKERAGE FIRM

Approximately five million homes are sold each year with every seller having similar objectives; to minimize the duration of the marketing period while simultaneously maximizing sales price. Once the decision to sell has been made, individuals are faced with the dilemma of marketing and selling the property themselves or acquiring the services of a real estate professional to assist in the sale of their property. It is logical to speculate that homeowners wishing to acquire the services of a real estate broker or salesperson will desire to select a salesperson that can help achieve the optimization objective of minimizing time on market (TOM) and maximizing sales price. This research examines whether the experience of the listing/selling agent (defined as the number of years an agent has possessed a real estate license) and the experience of the listing/selling firm (defined as the number of years a specific brokerage firm has been in operation) has a significant impact on the TOM