Effect of different concentrations of specific inhibitor of matrix metalloproteinases on the shear bond strength of self-adhesive resin cements to dentin

Considering the probability of chemical and enzymatic reactions between matrix metalloproteinases (MMPs) in the dentin structure and their specific inhibitors, the aim of the present study was to evaluate the effect of different concentrations of specific inhibitor of MMPs (galardin) on the shear bond strength of self-adhesive resin cements to dentin. Forty-eight sound human premolars were mounted in self-cured acrylic resin after removal of the enamel on the buccal and lingual surfaces. The dentin surfaces achieved were polished and prepared with 600-grit silicon carbide paper. The samples were divided into 3 groups (n=16) based on the concentration of galardin used (with no galardin, galardin at a high concentration and galardin at a low concentration). In addition, 96 composite resin blocks, measuring 3 mm in height and diameter, were prepared. The composite resin blocks were bonded to the buccal and lingual surface dentin with Rely-X Unicem (RXC) and Speed CEM (SPC) self-adhesive resin cements, respectively, according to manufacturers? instructions. After 24 hours of storage in distilled water at 37°C, the shear bond strength values were determined in MPa and fracture modes were evaluated under a stereomicroscope. Data were analyzed with two-way ANOVA and post-hoc Bonferroni test (?=0.05). The shear bond strength of galardin at high concentration was significantly higher than that in the control group and galardin at a low concentrations (P<0.001). In addition, galardin at a low concentration exhibited higher shear bond strength compared to the control group (P=0.005). Furthermore, higher shear bond strength values were reported with the use of RXC compared to SPC (P<0.001). Irrigation with galardin increased the shear bond strength of self-adhesive resin cements to dentin and this increase had a direct relationship with the concentration of galardin in the solution

Effect of intraradicular reinforcement strategies on the fracture strength of endodontically treated anterior teeth with overflared canals

This study is done to evaluate the effect of different reinforcement techniques of overflared root canals with fiber posts on the fracture resistance of endodontically treated anterior teeth. It also introduces a new technique for simultane

Effect of different application strategies of universal adhesive used for immediate and delayed dentin sealing on the microtensile bond strength of self-adhesive resin cement to dentin with and without aging

Bond strength of indirect restorations is a very important issue that should be given special attention. Immediate dentin sealing (IDS) technique has been suggested in recent years. The aim of the present study was to investigate the effect of different

Effect of 15% carbamide peroxide bleaching gel on color stability of giomer and microfilled composite resin: an in vitro comparison

Objectives: The effect of 15% carbamide peroxide bleaching gel on color stability and surface topography of a giomer and a microfilled composite resin was evaluated in the present in vitro study. Study design: Forty discs measuring 10 mm in diameter and 1 mm in thickness were prepared from a giomer and a microfilled composite resin. Each material yielded 20 discs with completely smooth surfaces. Then a spectrophotometer was used to measure L* (lightness), a* (redness, greenness) and b* (blueness, yellowness) color coordinates of all the discs. Subsequently, the specimens were subjected to 15% carbamide peroxide bleaching gel. After measuring the color coordinates once again, color changes (DE*) were calculated by the CIELAB system. Six specimens from each material (three specimens before bleaching agent application and three specimens thereafter) were viewed under an atomic force microscope (AFM) for surface topography evaluation. Data were analyzed by Mann-Whitney U and Kruskal-Wallis tests at a=0.05. Results: There were no statistically significant differences in color changes (DE*) between the two materials (P>0.05). In addition, no significant differences were detected in surface roughness between composite resin and giomer discs before and after bleaching (P>0.05 for both). However, in both materials the differences in surface roughness were significant before and after bleaching procedures (P<0.001). Conclusions: Based on the results of the present study it was concluded that 15% carbamide peroxide does not induce clinically detectable color changes in composite resin and giomer despite an increase in surface roughness

Effect of sodium ascorbate on the bond strength of all-in-one adhesive systems to NaOCl-treated dentin

Background: Ascorbic acid and its salts are low-toxicity products, which are routinely used in food industries as antioxidants. The aim of the present study was to evaluate the effect of 10% sodium ascorbate on the bond strength of two all-in-one adhesive systems to NaOCl-treated dentin. Material and Methods: After exposing the dentin on the facial surface of 90 sound human premolars and mounting in an acrylic resin mold, the exposed dentin surfaces were polished with 600-grit SiC paper under running water. Then the samples were randomly divided into 6 groups of 15. Groups 1 and 4 were the controls, in which no surface preparation was carried out. In groups 2 and 5 the dentin surfaces were treated with 5.25% NaOCl alone for 10 minutes and in groups 3 and 6 with 5.25% NaOCl for 10 minutes followed by 10% sodium ascorbate for 10 minutes. Then composite resin cylinders, measuring 2 mm in diameter and 2 mm in height, were bonded on the dentin surfaces in groups 1, 2 and 3 with Clearfil S 3 Bond and in groups 4, 5 and 6 with Adper Easy One adhesive systems according to manufacturers’ instructions. The samples were stored in distilled water for 24 hours at 37°C and then thermocycled. Finally, the samples underwent shear bond strength test in a universal testing machine at a strain rate of 1 mm/min. Data were analyzed with two-way ANOVA and post hoc Tukey tests at α=0.05. Results: The differences between groups 1 and 2 ( P =0.01), 1 and 5 ( P =0.003). 1 and 6 ( P =0.03) and 4 and 5 ( P =0.03) were statistically significant. Two-by-two comparisons did not reveal any significant difference between other groups ( P >0.05). Conclusions: Use of 10% sodium ascorbate for 10 minutes restored the decreased bond strength of the adhesive systems to that of the control groups

Effect of Relining with Different Composite Resins on the Push-out Bond Strength of Anatomical Fiber Posts to Root Canal Dentin

Introduction: Relining fiber posts using composite resins helps the posts adapt to the anatomical space of the root canals. The aim of this study was to evaluate the effect of composite resin type on the push-out bond strength of anatomical fiber posts to intra canal dentin. Methods and Materials: Forty-eight bovine upper incisors were prepared for post space after root canal therapy and randomly divided in to six groups. Five different types of composite resin (GrandioSO, GrandioSO Heavy Flow, X-tra Fil, X-tra base and everX Posterior) were used for relining the prepared fiber posts. In the control group, the prepared post was cemented into the post space without relining. Cervical, middle and apical cross-sections were achieved from each root and push-out test was conducted at a crosshead speed of 0.5 mm/min. One sample from each group was scanned using a micro-CT scanner which provided views from the apical, middle and coronal thirds. Data were analyzed using Kolmogorov-Smirnov test, repeated measures ANOVA and post hoc tests using SPSS 17 (P&lt;0.05). Results: Statistical analysis showed significant differences in terms of mean push-out bond strengths between different composite resin types and cross-sections (P&lt;0.001). The mean push-out bond strength of the samples relined with Grandio SO composite resin (15.48±2.32) and X-tra Fil Bulk-fill composite resin (14.09±1.98) were significantly higher than that of other groups (P&lt;0.05). The unrelined group had a mean push-out bond strength (5.94±1.45) which was significantly lower than that in other groups (P&lt;0.05). In addition, there was a relationship between cross-sections and composite resin types (P&lt;0.05). Conclusion: This in vitro study showed that the composite resins used for relining can affect the push-out bond strength to intra canal dentin based on their physical and mechanical properties.Keywords: Dental Adhesion; Post Technique; Root Canal

The effect of pre-heating on monomer elution from bulk-fill resin composites

The present study was aimed to evaluate the effect of pre-heating of bulk -fill resin composites on monomer elution from them. Three different types of resin composites were used including Tetric N-Ceram Bulk Fill, X-tra Fill and X-tra Base. 10 cylindrical samples were prepared from each resin composites. Before light curing, 5 samples were pre-heated until reaching 68?C, then 5 other samples were polymerized at room temperature. After 24 hours, release of UDMA, TEGDMA and BIS-GMA monomers were measured by High-Performance Liquid Chromatography analysis. Data analysis was performed by two-way ANOVA test, Games-Howell and Sidak post hoc tests. Pre-heating did not have any statistically significant effect on the mean values of UDMA, TEGDMA and Bis-GMA elution (p>0.05). The greatest amount of released Bis-GMA and UDMA was obtained from Tetric N-Ceram Bulk-fill composite. The greatest amount of released TEGDMA was obtained from X-tra Fill composite. X-tra Base composite showed the lowest amount of monomer release (P<0.001). Pre-heating did not have any effect on monomer release from bulk-fill resin composites. Moreover, the amount and the type of monomers released from various bulk-fill resin composites were not similar

The effect of repeated preheating of dimethacrylate and silorane-based composite resins on marginal gap of class V restorations

Background. One of the problems with composite resin restorations is gap formation at resin‒tooth interface. The present study evaluated the effect of preheating cycles of silorane- and dimethacrylate-based composite resins on gap formation at the gingival margins of Class V restorations. Methods. In this in vitro study, standard Class V cavities were prepared on the buccal surfaces of 48 bovine incisors. For restorative procedure, the samples were randomly divided into 2 groups based on the type of composite resin (group 1: di-methacrylate composite [Filtek Z250]; group 2: silorane composite [Filtek P90]) and each group was randomly divided into 2 subgroups based on the composite temperature (A: room temperature; B: after 40 preheating cycles up to 55°C). Marginal gaps were measured using a stereomicroscope at ×40 and analyzed with two-way ANOVA. Inter- and intra-group comparisons were analyzed with post-hoc Tukey tests. Significance level was defined at P < 0.05. Results. The maximum and minimum gaps were detected in groups 1-A and 2-B, respectively. The effects of composite resin type, preheating and interactive effect of these variables on gap formation were significant (P<0.001). Post-hoc Tukey tests showed greater gap in dimethacrylate compared to silorane composite resins (P< 0.001). In each group, gap values were greater in composite resins at room temperature compared to composite resins after 40 preheating cycles (P<0.001). Conclusion. Gap formation at the gingival margins of Class V cavities decreased due to preheating of both composite re-sins. Preheating of silorane-based composites can result in the best marginal adaptation

Effect of smear layer thickness and pH of self-adhesive resin cements on the shear bond strength to dentin

Context: There are concerns in relation to the bonding efficacy of self-adhesive resin cements to dentin covered with the smear layer. Aims: This study aims to evaluate the effect of smear layer thickness and different pH values of self-adhesive resin cements on the shear bond strength to dentin. Materials and Methods: The dentin on the buccal and lingual surfaces of 48 sound human premolars were abraded with 60- and 600-grit silicon carbide papers to achieve thick and thin smear layers, respectively. The samples were divided into three groups (n = 16) based on the cement pH: Rely-X Unicem (RXU) (pH 0.05). The cumulative effect of these variables was not significant, either (P = 0.11). Conclusion: The shear bond strengths of SPC and CSL self-adhesive resin cements were similar and significantly lower than that of RXU. The smear layer thickness was not a determining factor for the shear bond strength value of self-adhesive resin cements

Shear Bond Strengths of Methacrylate- and Silorane-based Composite Resins to Feldspathic Porcelain using Different Adhesive Systems

Background and aims. Use of porcelain as inlays, laminates and metal-ceramic and all-ceramic crowns is common in modern dentistry. The high cost of ceramic restorations, time limitations and difficulty of removing these restorations result in delays in replacing fractured restorations; therefore, their repair is indicated. The aim of the present study was to compare the shear bond strengths of two types of composite resins (methacrylate-based and silorane-based) to porcelain, using three adhesive types. Materials and methods. A total of 156 samples of feldspathic porcelain surfaces were prepared with air-abrasion and randomly divided into 6 groups (n=26). In groups 1‒3, Z250 composite resin was used to repair porcelain samples with Ad-per Single Bond 2 (ASB), Clearfil SE Bond (CSB) and Silorane Adhesive (SA) as the bonding systems, afterapplication of silane, respectively. In groups 4‒6, the same adhesives were used in the same manner with Filtek Silorane composite resin. Finally, the shear bond strengths of the samples were measured. Two-way ANOVA and post hoc Tukey tests were used to compare bond strengths between the groups with different adhesives at P<0.05. Results. There were significant differences in the mean bond strength values in terms of the adhesive type (P<0.001). In addition, the interactive effect of the adhesive type and composite resin type had no significant effect on bond strength (P=0.602). Conclusion. The results of the present study showed the highest repair bond strength values to porcelain with both com-posite resin types with the application of SA and ASB