Failure of Zr50 Ti16.5 Cu15 Ni18.5 amorphous metallic ribbon

The deformation and fracture behavior of Zr50Ti165Cu15Ni185 bulk amorphous metal in the form of a thin ribbon have been determined in tensile test at room temperature. The fracture is localized in a major shear band and the fracture angle between the tensile stress axis and the fracture plane is close to 45°. Fractographic observations have revealed that the fracture surface of the amorphous metallic glass consists mainly of a vein-like pattern morphology We present a scheme of three zones of fracture surface morphology: progressive smooth sliding region (A), dominating vein like pattern (B), and river-like ripples (C).Исследованы особенности деформирования и разрушения массивного аморфного металла 2г50Т116.5Си15№185 в виде тонкой ленты при испытании на растяжение при комнатной температуре. Разрушение локализуется в главной полосе сдвига, при этом угол разрушения между осью растягивающего напряжения и плоскостью разрушения близок к 45°. Фрактографические исследования показали, что поверхность излома аморфного металлического стекла состоит в основном из жильной морфологии. Приведена схема трех зон морфологии поверхности излома: область последовательного непрерывного скольжения (А), преобладающая жильная структура (В) и “речная” рябь (С)

ABOUT THE METHODS USED IN PROCESS OF MANAGEMENT OF SOCIAL STABILITY OF THE ENTERPRISE OF TRANSPORT BUSINESS

Implementation of the basic principle of the concept of the sustainable development consisting in need of ensuring cost efficiency, social justice and an ecological safety is one of modern requirements to activities of the enterprise. According to the designated purposes within general stability were allocated functional, financial and economic, social and ecological stability of the enterprise. Process of management of stability assumes the choice and adaptation of the corresponding methods and technologies. For the purpose of development of methodology of management of stability of the enterprise the approach to assessment of effectiveness of management based on use of indicators of organizational and labor capacities of the enterprise is offered. A number of offers was made on the basis of results of the researches conducted by the author in the motor transportation enterprises of St. Petersburg in 2014. Methodical approaches to assessment of the indicators characterizing social stability of the entity are given in article. The role of methods of management of organizational changes, in particular, of methods of overcoming resistance of personnel, in the course of ensuring social stability of the enterprise is designated

Thermally activated deformation of nanocrystalline and coarse grained CoCrFeNiMn high entropy alloy in the temperature range 4.2–350 K

Mechanical properties of a nanocrystalline (~ 60 nm) and a coarse grained (grain sizes ~ 4 µm) CoCrFeNiMn high entropy alloys were studied in uniaxial compression in the temperature range 4.2–350 K. Temperature dependences of yield strength, flow stress and strain rate sensitivity have been registered and analyzed in the framework of two thermal activation deformation models, that of thermal activation of local barrier overcoming, and that of Peierls valley double kink formation. Microscopic parameters of dislocation interaction with the barriers for thermally activated motion are estimated and low temperature deformation mechanisms are discussed.Механічні властивості нанокристалічного (середній розмір зерен ~ 60 нм) та крупнозернистого (середній розмір зерен ~ 4 мкм) високоентропійного сплаву CoCrFeNiMn вивчались шляхом одноосного стискання в інтервалі температур 4,2–350 К. Температурна залежність межі плинноcті, напруження течії та швидкісної чутливості деформуючого напруження виміряно та проаналізовано в рамках двох термоактиваційних моделей: моделі взаємодії дислокацій з локальними бар’єрами та моделі Пайєрлса щодо утворення подвійних перегинів. Визначено мікроскопічні параметри взаємодії дислокацій з бар’єрами при термоактивованому русі та обговорюються низькотемпературні механізми, які контролюють пластичну деформацію.Механические свойства нанокристаллического (средний размер зерен ~ 60 нм) и крупнозернистого (средний размер зерен ~ 4 мкм) высокоэнтропийного сплава CoCrFeNiMn изучались путем одноосного сжатия в интервале температур 4,2–350 К. Температурная зависимость предела текучеcти, напряжения течения и скоростной чувствительности деформирующего напряжения измерены и проанализированы в рамках двух термоактивационных моделей: модели взаимодействия дислокаций с локальными барьерами и модели Пайерлса образования двойных перегибов. Определены микроскопические параметры взаимодействия дислокаций с барьерами при термоактивированном движении и обсуждаются низкотемпературные механизмы, которые контролируют пластическую деформацию

Structure and properties of nanostructured Cobalt processed by high pressure torsion at temperatures of 300 and 77 K

Several nanostructured states of high purity cobalt were achieved by highpressure torsion (HPT) at pressures of 4 and 8 GPa and temperatures of 300 and 77 K.Changes of crystallographic texture, grain sizes and phase transformations as a resultof HPT and subsequent annealing have been measured and analyzed. Mechanicalproperties of nanostructured Co were studied by microhardness measurements at300 K, and uniaxial compression at temperatures 300, 77 and 4.2 K. Comparison ofthe strength characteristics, plasticity and strain hardening of the nanostructured andcoarse grained Co has been carried out. Micromechanisms of plastic deformation of Coduring HPT deformation and uniaxial compression are discussed

Вплив стану евентрованих органів при неускладненому гастрошизисі на клінічний перебіг і прогноз цієї вади

Background. According to current literature, intestinal damage in gastroschisis (GS) leads to an increase in morbidity and mortality. However, the impact of intestinal affect severity on the clinical course and prognosis remains unresolved issue.Objective: to study the influence of eventrated organs status on the clinical course and prognosis of simple gastroschisis (SGS).Material and methods. The data of 83 patients with SGS were studied. The analysis of the frequency and nature of complications of clinical course, duration of hospitalization and levels of lethality depending on the degree of pathological changes of the evolved organs has been carried out. To investigate the influence of eviscerated organs status on the clinical course and prognosis of SGS, all patients were divided into three groups. Group 1 included patients with intact bowel (n=12; 14.5%). Newborns with moderate intestinal damage were included to the 2nd group (n=29; 34.9%). In the 3rd group, severe intestinal damage was diagnosed (n=42, 50.6%).Results. During evaluation of the statistical significance, the significant differences of the studied parameters between the 1 and 2 groups were not detected (P>0.05; p=0.07 — 0.4). When comparing the 2nd and 3rd groups, there is a significant increase in the length of hospital stay, the mortality and complications rate (P<0.05; p=0.00510.006) among patients in the third group. In children with severe pathological changes of the eventated organs, the development of respiratory distress syndrome, sepsis, cardiovascular and multiple organ failure was significantly more frequent (P<0.05; p=0.00310.007).Conclusions. Severe damage of eventrated organs in SGS was observed in 50.6% of patients. They have a significant impact on the incidence of clinical complications and increase the mortality of these newborns.По данным современной литературы, поражения кишечника при гастрошизисе приводят к увеличению заболеваемости и смертности. Однако влияние степени изменений эвентрированых органов на клиническое течение и прогноз этого порока изучено недостаточно.Цель: изучить влияние состояния эвентрированых органов при неосложненном гастрошизисе на клиническое течение и прогноз этого порока.Материалы и методы. Изучены данные 83 пациентов с неосложненным гастрошизисом. Проведен анализ частоты и характера осложнений клинического течения, длительности госпитализации и уровней летальности в зависимости от степени патологических изменений эвентрированых органов. Для исследования влияния состояния эвентрированых органов на клиническое течение и прогноз порока все пациенты были разделены на три группы. К 1-й группе отнесены пациенты, у которых эвентрированые органы были не изменены (n=12; 14,5%); во 2-ю группу вошли новорожденные, у которых обнаружены умеренные изменения эвентрированых петель (n=29; 34,9%); у детей 3-й группы диагностированы выраженные изменения эвентрированых органов (n=42; 50,6%).Результаты. При оценке статистической значимости достоверных различий исследуемых показателей между 1 и 2 группами не обнаружено (Р>0,05; р=0,07–0,4). А при сравнении 2-й и 3-й групп установлено достоверное увеличение длительности пребывания в стационаре, летальности и частоты осложнений (Р<0,05; р=0,005–0,006) среди пациентов 3-й группы. У детей с выраженными патологическими изменениями эвентрированых органов достоверно чаще наблюдалось развитие респираторного дистресс-синдрома, сепсиса, сердечно-сосудистой и полиорганной недостаточности (Р<0,05; р=0,003–0,007).Выводы. Выраженные изменения эвентрированых органов при неосложненном гастрошизисе наблюдаются у 50,6% пациентов. Они имеют достоверное влияние на частоту осложнений клинического течения и увеличивают летальность этих новорожденных.За даними сучасної літератури, ураження кишечника при гастрошизисі призводить до збільшення захворюваності та смертності. Проте вплив ступеня змін евентрованих органів на клінічний перебіг і прогноз цієї вади вивчено недостатньо.Мета: вивчити вплив стану евентрованих органів при неускладненому гастрошизисі на клінічний перебіг і прогноз цієї вади.Матеріали і методи. Вивчено дані 83 пацієнтів з неускладненим гастрошизисом. Проведено аналіз частоти та характеру ускладнень клінічного перебігу, тривалості госпіталізації та рівнів летальності залежно від ступеня патологічних змін евентрованих органів. Для дослідження впливу стану евентрованих органів на клінічний перебіг і прогноз вади усі пацієнти були розділені на три групи. До 1-ї групи зараховані пацієнти, у яких евентровані органи були не змінені (n=12; 14,5%); до 2-ї групи увійшли новонароджені, у яких виявлено помірні зміни евентрованих петель (n=29; 34,9%); у дітей 3-ї групи діагностовано виразні зміни евентрованих органів (n=42; 50,6%).Результати. При оцінці статистичної значущості достовірних відмінностей досліджуваних показників між 1 і 2 групами не виявлено (Р>0,05; р=0,0710,4). А при порівнянні 2-ї та 3-ї груп встановлене достовірне збільшення тривалості перебування у стаціонарі, летальності та частоти ускладнень (Р<0,05; р=0,005–0,006) серед пацієнтів 3-ї групи. У дітей з виразними патологічними змінами евентрованих органів достовірно частіше спостерігався розвиток респіраторного дистрес-синдрому, сепсису, серцево-судинної та поліорганної недостатності (Р<0,05; р=0,003–0,007).Висновки. Виразні зміни евентрованих петель кишечника при неускладненому гастрошизисі спостерігаються у 50,6% пацієнтів. Вони мають достовірний вплив на частоту ускладнень клінічного перебігу та збільшують летальність цих новонароджених

Fragmentation of Co-Fe-Ta-B Soft Magnetic Amorphous Alloy

The main limitation of high-strength Co-based bulk metallic glasses for their application as structural materials is the large brittleness. Spontaneously emerging cracks in the alloy degrade the magnetic properties. We analyzed the failure characteristics of $Co_{43}Fe_{20}Ta_{5.5}B_{31.5}$ bulk soft magnetic metallic glass deformed in the compression at room temperature and the low strain rate. Under loading the amorphous structure stores high elastic energy. During the failure this energy is released and the alloy breaks into small particles or powder exhibiting a fragmentation mode