The effect of resin on the impact damage tolerance of graphite-epoxy laminates
The effect of the matrix resin on the impact damage tolerance of graphite-epoxy composite laminates was investigated. The materials were evaluated on the basis of the damage incurred due to local impact and on their ability to retain compression strength in the presence of impact damage. Twenty-four different resin systems were evaluated. Five of the systems demonstrated substantial improvements compared to the baseline system including retention of compression strength in the presence of impact damage. Examination of the neat resin mechanical properties indicates the resin tensile properties influence significantly the laminate damage tolerance and that improvements in laminate damage tolerance are not necessarily made at the expense of room temperature mechanical properties. Preliminary results indicate a resin volume fraction on the order of 40 percent or greater may be required to permit the plastic flow between fibers necessary for improved damage tolerance
Concepts for improving the damage tolerance of composite compression panels
The residual strength of specimens with damage and the sensitivity to damage while subjected to an applied inplane compression load were determined for flatplate specimens and blade-stiffened panels. The results suggest that matrix materials that fail by delamination have the lowest damage tolerance capability. Alternate matrix materials or laminates which are transversely reinforced suppress the delamination mode of failure and change the failure mode to transverse shear crippling which occurs at a higher strain value. Several damage-tolerant blade-stiffened panel design concepts are evaluated. Structural efficiency studies conducted show only small mass penalties may result from incorporating these damage-tolerant features in panel design. The implication of test results on the design of aircraft structures was examined with respect to FAR requirements
Preliminary rotor wake measurements with a laser velocimeter
A laser velocimeter (LV) was used to determine rotor wake characteristics. The effect of various fuselage widths and rotor-fuselage spacings on time averaged and detailed time dependent rotor wake velocity characteristics was defined. Definition of time dependent velocity characteristics was attempted with the LV by associating a rotor azimuth position with each velocity measurement. Results were discouraging in that no apparent time dependent velocity characteristics could be discerned from the LV measurements. Since the LV is a relatively new instrument in the rotor wake measurement field, the cause of this lack of periodicity is as important as the basic research objectives. An attempt was made to identify the problem by simulated acquisition of LV-type data for a predicted rotor wake velocity time history. Power spectral density and autocorrelation function estimation techniques were used to substantiate the conclusion that the primary cause of the lack of time dependent velocity characteristics was the nonstationary flow condition generated by the periodic turbulence level that currently exists in the open throat configuration of the wind tunnel
Underperforming policy networks : the biopesticides network in the United Kingdom
Loosely integrated and incomplete policy networks have been neglected in the literature. They are important to consider in terms of understanding network underperformance. The effective delivery and formulation of policy requires networks that are not incomplete or underperforming. The biopesticides policy network in the United Kingdom is considered and its components identified with an emphasis on the lack of integration of retailers and environmental groups. The nature of the network constrains the actions of its agents and frustrates the achievement of policy goals. A study of this relatively immature policy network also allows for a focus on network formation. The state, via an external central government department, has been a key factor in the development of the network. Therefore, it is important to incorporate such factors more systematically into understandings of network formation. Feedback efforts from policy have increased interactions between productionist actors but the sphere of consumption remains insufficiently articulated
The effect of impact damage and circular holes on the compressive strength of a graphite-epoxy laminate
Specimens were impacted by 1.27-cm-diameter aluminum spheres with speeds ranging from 52 to 101 m/s. Some specimens were impacted without any applied compressive load and then loaded to failure to determine their residual strength. Other specimens were loaded to a prescribed axial compressive strain and impacted while at that applied load. Loaded specimens that did not fail catastrophically on impact were subsequently loaded to failure to determine their residual strength. Low-velocity impact damage was found to degrade seriously the laminate static compressive strength. Low-strain compression-compression cyclic loading was found to degrade further the compressive strength of impact-damaged specimens. Specimens with circular holes having diameters up to a third of the specimen width were loaded to failure in compression. It was found that circular holes can also degrade the static compressive strength of the laminate. The effects of circular holes and impact damage on the compressive strength of the laminate are compared
Comprehensive Spectral Analysis of Human EEG GENERATORS in Posterior Cerebral Regions
Human electroencephalogram generator spectral analysis in posterior cerebral region
Effect of Low Velocity Impact Damage on the Compressive Strength of Graphite/Epoxy Hat-Stiffened Panels
Low velocity impact damage on the compressive strength of graphite/epoxy hat stiffened panels is studied. Fourteen panels, representative of minimum-mass designs for two compression load levels were tested. Eight panels were damaged by impact and the effect on compressive strength was evaluated by comparing the results with data for undamaged panels. The impact tests consisted of firing 1.27 cm diameter aluminum projectiles normal to the plane of the panel at a velocity of approximately 55 m/sec to simulate impact from runway debris. The results of this investigation indicate that impact damage in the panels designed for 0.53 MN/m was contained locally and the damaged panels were capable of carrying the design load. The panels designed for 1.58 MN/m failed between 50 and 58 percent of the design load due to impact damage in the high axial stiffness region. The extent of damage in the high axial stiffness region of both panel designs increased with the magnitude of applied axial load. Damage in this region was the most significant factor in reducing panel strength. Limited damage that was not visually detectable reduced ultimate strength as much as extensive visible damage
Histidine nutrition and genotype affect cataract development in Atlantic salmon, Salmo salar L.
The aim of this study was to investigate effects of dietary levels of histidine (His) and iron (Fe) on cataract development in two strains of Atlantic salmon monitored through parr-smolt transformation. Three experimental diets were fed: (i) a control diet (CD) with 110 mg kg-1 Fe and 11.7 g kg-1 His; (ii) CD supplemented with crystalline His to a level of 18 g kg-1 (HD); and (iii) HD with added iron up to 220 mg kg-1 (HID). A cross-over design, with two feeding periods was used. A 6-week freshwater (FW) period was followed by a 20-week period, of which the first three were in FW and the following 17 weeks in sea water (SW). Fish were sampled for weighing, cataract assessment and tissue analysis at five time points. Cataracts developed in all groups in SW, but scores were lower in those fed high His diets (P < 0.05). This effect was most pronounced when HD or HID was given in SW, but was also observed when these diets were given in FW only. Histidine supplementation had a positive effect on growth performance and feed conversion ratio (P < 0.05), whereas this did not occur when iron was added. Groups fed HD or HID had higher lens levels of His and N-acetyl histidine (NAH), the latter showing a marked increase post-smoltification (P < 0.05). The HD or HID groups also showed higher muscle concentrations of the His dipeptide anserine (P < 0.05). There was a strong genetic influence on cataract development in the CD groups (P < 0.001), not associated with tissue levels of His or NAH. The role of His and His-related compounds in cataractogenesis is discussed in relation to tissue buffering, osmoregulation and antioxidation
The Compressional Behaviour of Perforated Elements
The behaviour of stub columns with a series of different perforation patterns is examined on the basis of tests. The tests concentrate on plain channel cross sections with perforation layouts systematically varied to examine the effects of perforation position, dimensions and number on the section performance. The application of existing cold formed steel design codes to perforated members is examined on the basis of comparison with the tests, and various modifications to the design codes are considered to take perforations into account These are described and the comparison with test results is illustrated
- …