Spectrophotometric analysis of crown discoloration induced by MTA- and ZnOE-based sealers

Crown discoloration can be induced by root canal sealer remnants following root canal treatment. OBJECTIVE: The aim of this study was to evaluate chromatic alterations in human tooth crowns induced by a Mineral Trioxide Aggregate-based sealer (MTA Fillapex(®) and a commonly used ZnOE-based sealer (Roth-811). The tested null hypothesis was that the application of the materials did not induce clinically perceptible crown discoloration (Ho: CIE color difference ΔE<3.7). MATERIAL AND METHODS: Forty five fully developed, intact, mandibular third molars were sectioned 1 mm below the cemento-enamel junction. The pulp chambers were chemomechanically debrided via the cervical access. The specimens were randomly assigned into three groups Group 1: MTA Fillapex, Group 2: Roth 811, Group 3: Negative control (unfilled) and immersed in individually marked vials containing distilled water up to the cervix (37±1º C). The spectral reflectance lines were recorded by utilizing a UV-VIS spectrophotometer equipped with integration sphere in the visual spectrum at baseline, 1 week, 1 and 3 months after material placement. Data were transformed into values of the CIE L*a*b* color system and the corresponding ΔE values were calculated. Statistical analysis was performed using two-way mixed ANOVA models, at p=0.05 level of significance. RESULTS: A statistically significant increase in a* and b* chromatic parameters of the MTA Fillapex Group was measured. However, ΔE values did not exceed the human eye perceptibility threshold (set at ΔE<3.7) during the experimental period (ΔEt3=2.88). In Roth-811 Group, a statistically significant decrease in L* and a statistically significant increase in a* and b* chromatic parameters was measured, during all observation periods. Resultant ΔE values exceeded the human eye perceptibility threshold after 1 week (ΔEt1=5.65). CONCLUSIONS: Application of MTA Fillapex in tooth crowns resulted in minimal color alterations, while Roth 811 induced severe discoloration, in vitro. It could be suggested that, in terms of aesthetics, the use of MTA Fillapex appears to be favorable

Dynamic sealing ability of MTA root canal sealer

To evaluate (i) the sealing ability of two sealers, mineral trioxide aggregate sealer (MTAS) and Pulp Canal Sealer (PCS), used with gutta-percha utilizing the fluid filtration method, (ii) leaching and surface characteristics in Hank's balanced salt solution (HBSS) over a period of time. METHODOLOGY: Surface characteristics in HBSS were evaluated under the scanning electron microscope after 1 and 28 days, and the leaching of both sealers were assessed by inductively coupled plasma atomic absorption spectrometry (ICP-AAS). In addition, 24 single rooted extracted teeth were root filled using warm vertical compaction with either MTAS or PCS used as sealers with gutta-percha. Four teeth were used as positive and negative controls. Sealing ability was evaluated after 1 or 28 days using the fluid filtration method. RESULTS: Mineral trioxide aggregate sealer exhibited crystalline deposits rich in calcium and phosphorus on its surface when in contact with a physiological solution. These crystalline deposits were absent in PCS and on MTAS stored at 100% humidity. The sealing ability of MTAS was similar to that of PCS. CONCLUSIONS: The novel sealer based on mineral trioxide aggregate had comparable sealing ability to a proprietary brand sealer cement. In contact with a simulated body fluid, the MTA sealer released calcium ions in solution that encouraged the deposition of calcium phosphate crystals