Internal adaptation of cast titanium crowns

As the adaptation of titanium crowns obtained by Rematitan Plus investment, specific for titanium, is not recognized to be suitable, this study evaluated the effect of the concentration of the specific liquid and the temperature of the mold of investments on the internal misfit of crowns cast on commercially pure titanium. Individual dies of epoxy resin were obtained, representing teeth prepared for full-crown restoration with a 6-degree axial surface convergence angle and shoulder (1.0 mm). For the waxing of each crown, a ring-shaped stainless steel matrix (8.0mm internal diameter; 7.5 mm height) was adapted above the individual dies of epoxy resin. The Rematian Plus investment was mixed according to the manufacturer's instructions using two different concentrations of the specific liquid: 100%, 75%. Casting was performed in a Discovery Plasma Ar-arc vacuum-pressure casting machine with molds at temperatures of 430ºC, 515ºC and 600ºC. The crowns were cleaned individually in a solution (1% HF + 13% HNO3) for 10 min using a ultrasonic cleaner, with no internal adaptations, and luted with zinc phosphate cement under a 5 kg static load. The crown and die assemblies were embedded in resin and sectioned longitudinally. The area occupied by cement was observed using stereoscopic lens (10X) and measured by the Leica Qwin image analysis system (mm²). The data for each experimental condition (n=8) were analyzed by Kruskal-Wallis non-parametric test (á=0.05). The results showed that liquid dilution and the increase in mold temperature did not significantly influence the levels of internal fit of the cast titanium crowns. The lowest means (±SD) of internal misfit were obtained for the 430ºC/100%: (7.25 mm² ±1.59) and 600ºC/100% (8.8 mm² ±2.25) groups, which presented statistically similar levels of internal misfit

A homoparentalidade na perspectiva de estudantes do Ensino Superior

Pretendeu-se com este estudo analisar a opinião de estudantes do Ensino Superior (N=115) relativamente à homoparentalidade, através da aplicação de um questionário. Verificou-se que a maioria dos sujeitos (66%) revela uma posição de desacordo relativamente à igualdade de circunstâncias entre homossexuais e heterossexuais no que diz respeito ao exercício da parentalidade, registando-se diferenças significativas no género, com o masculino menos receptivo a essa igualdade (U=654; p=0,001), assim como estudantes de Desporto e Actividade Física, em comparação com os do curso de Educação Social (U=976,5; p=0,010). O mesmo não aconteceu nas V.I. Idade e Urbanidade. A partir dos resultados são tecidas considerações relativas às responsabilidades das instituições do Ensino Superior neste tema

Effect of phosphate-bonded investments on titanium reaction layer and crown fit

This study analyzed the reaction layer and measured the marginal crown fit of cast titanium applied to different phosphate-bonded investments, prepared under the following conditions (liquid concentration/casting temperature): Rema Exakt (RE) - 100%/237°C, 75%/287°C, Castorit Super C (CS)-100%/70°C, 75%/141°C and Rematitan Plus (RP)- 100%/430°C (special to titanium cast, as the control group). The reaction layer was studied using the Vickers hardness test, and analyzed by two way ANOVA and Tukey's HSD tests (α = 0.05). Digital photographs were taken of the crowns seated on the die, the misfit was measured using an image analysis system and One-way ANOVA, and Tukey's test was applied (α = 0.05). The hardness decreased from the surface (601.17 VHN) to 150 μm (204.03 VHN). The group CS 75%/141°C presented higher hardness than the other groups, revealing higher surface contamination, but there were no differences among the groups at measurements deeper than 150 μm. The castings made with CS - 100%/70°C presented the lowest levels of marginal misfit, followed by RE -100%/237°C. The conventional investments CS (100%) and RE (100%) showed better marginal fit than RP, but the CS (75%) had higher surface contamination.(FAPESP) São Paulo Research Foundatio

Influence of microwave sterilization on the cutting capacity of carbide burs

OBJECTIVE: This study compared the cutting capacity of carbide burs sterilized with microwaves and traditional sterilization methods. MATERIAL AND METHODS: Sixty burs were divided into 5 groups according to the sterilization methods: dry heat (G1), autoclave (G2), microwave irradiation (G3), glutaraldehyde (G4) or control - no sterilization (G5). The burs were used to cut glass plates in a cutting machine set for twelve 2.5-min periods and, after each period, they were sterilized (except G5) following the protocol established for each group. The cutting capacity of the burs was determined by a weight-loss method. Data were analyzed statistically by Kruskal-Wallis and Dunn's test. RESULTS: The means of the cutting amount performed by each group after the 12 periods were G1 = 0.2167 ± 0.0627 g; G2 = 0.2077 ± 0.0231 g; G3 = 0.1980 ± 0.0326 g; G4 = 0.1203 ± 0.0459 g; G5 = 0.2642 ± 0.0359 g. There were statistically significant differences among the groups (

Estudo do conteúdo de partículas inorgânicas, da contração de polimerização e da resistência à flexão de materiais restauradores estéticos diretos indicados para dentes posteriores

Recentemente, foram lançados no mercado odontológico novos materiais estéticos para restaurações diretas em dentes posteriores, aos quais são atribuídas propriedades mais adequadas para essa indicação. Entretanto, as informações disponíveis são ainda muito escassas, gerando dúvidas quanto à sua real eficácia, sobre quais as diferenças de suas composições e propriedades físicas e mecânicas em relação aos materiais até então disponíveis e se, de fato, apresentam melhor performance clínica. Em vista do exposto, nos propusemos a estudar contração de polimerização, resistência à flexão e concentração de partículas inorgânicas, por massa e volume, de sete resinas compostas (Alert, Ariston, Solitaire, Definite, Filtek P60, Z-100 e Tetric Ceram). A contração de polimerização foi medida nos materiais inseridos em um anel plástico, e o registro das alterações, durante a polimerização, foi feito por meio de instrumento eletrônico de medida linear, que registra as alterações dimensionais, com sensibilidade de 1 mm. A resistência à flexão foi medida na máquina de ensaios mecânicos MTS 810 e a confecção dos corpos-de-prova e dos dispositivos para o ensaio foi orientada pela norma ISO no 4049:1988. A determinação do conteúdo de partículas inorgânicas por massa foi feita através da pesagem de uma porção de resina composta polimerizada antes e após a eliminação da fase orgânica em forno, à temperatura de 700oC. O porcentual volumétrico de partículas inorgânicas foi calculado com base no Princípio de Arquimedes. Foi determinado o volume da resina composta polimerizada, antes e após a eliminação da fase orgânica, pela diferença da massa do material pesado ao ar e imerso em água. Os dados de conteúdo de partículas inorgânicas por massa e por volume, de contração de polimerização e resistência à flexão foram submetidos...(Resumo completo, clicar acesso eletrônico abaixo)Recently new esthetic materials for direct restorations in posterior teeth were introduced in the dentistry market, which were attributed properties more adequate for this indication. However, the information avaiable is still very scarce, producing uncertainty of its real efficacy. There is existence of doubts regarding the differences in composition, physical and mechanical properties related to the materials available and if, in fact, they present better clinical performance. Due to the exposed, we proposed to study the polymerization contraction, flexural resistance and concentration of inorganic particles by mass and volume of seven composite resins (Alert, Ariston, Solitaire, Definite, Filtek P60, Z-100 and Tetric Ceram). The polymerization contraction was measured with the materials inserted in a plastic ring. The registration of the alterations, during the polymerization was done through an electronic instrument of linear dimension with sensibiligy of 1um. The flexural resistance was measured by the MTS 810 mechanical test machine and the confection of the samples and the device for the tests were orientated by the ISO nº 4049:1998 norm. The determination of the content of inorganic particles per mass was made. A portion of composite resin was weighed before and after the elimination of the organic phase in an oven, at a temperature of 700ºC. The volume percentage of the inorganic particles was calculated based on the Arquimedes's Principle. The volume of ocmposite resin polymerized was determined before and after the elimination of the organic phase, by the difference in the mass of the material weighed in air and immersed in water. The data regarding the content of inorganic particles per mass and volume, polymerization contraction and flexural resistance...(Complete abstract click electronic access below