Estudo do efeito da ciclagem térmica na resistência da união adesiva entre uma cerâmica aluminizada e um cimento resinoso

This study evaluated the effect of thermocycling on the bond strength between Procera AllCeram (Nobel-Biocare) and a resin cement (Panavia F, Kuraray CO). Nine ceramic blocks with dimensions of 5x6x6mm were conditioned at one face with Rocatec System (Espe). After, they were luted with Panavia F to composite resin blocks (Clearfil AP-X, Kuraray CO). The nine groups formed by ceramic, cement and composite resin were split up obtaining 75 samples with dimensions of 12x1x1mm and adhesive surface presenting 1mm²&plusmn;0.1mm² of area. The samples were divided into 3 groups (n=25): G1 - 14 days in distilled water at 37ºC; G2 - 6,000 cycles in water (5ºC - 55ºC - 30s); G3 - 12,000 cycles in water (5ºC - 55ºC - 30s). The samples were tested in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. Data were analyzed by ANOVA and Tukey tests. The results indicated that mean values of rupture tension (MPa) of G1 (10.71 &plusmn; 3.54) did not differ statistically (pEste trabalho avaliou o efeito da ciclagem térmica sobre a resistência adesiva entre a cerâmica aluminizada (Procera AllCeram, Nobel-Biocare) e um cimento resinoso (Panavia F, Kuraray CO). Nove blocos de cerâmica, com dimensões de 5x6x6mm, foram condicionados em uma de suas faces com o Sistema Rocatec (ESPE). A seguir foram cimentados a blocos de resina composta (Clearfil AP-X, Kuraray CO). Os conjuntos cerâmica-cimento-resina foram cortados em 75 corpos-de-prova com formato retangular com dimensões de 12x1x1mm e superfície adesiva apresentando 1mm² &plusmn; 0,1mm². Os corpos-de-prova foram divididos em três grupos (n=25): G1 - 14 dias em água destilada a 37ºC, G2 - 6000 ciclos em água (5ºC e 55ºC) e G3 - 12000 ciclos em água (5ºC e 55ºC). Os corpos-de-prova foram ensaiados sob velocidade de 1mm/min em máquina de ensaio universal (EMIC). Os dados foram tratados estatisticamente com os testes de Anova e Tukey e indicaram que os valores médios de tensão de rupturas (MPa) de G1 (10,71 &plusmn; 3,54) não diferiram estatisticamente (p < 5%) de G2 (9,01 &plusmn; 3,90), porém houve diferença significativa entre G1 e G3 (7,28 &plusmn; 3,00). Concluiu-se que a ciclagem térmica diminuiu a resistência adesiva significativamente quando os corpos-de-prova foram submetidos a 12000 ciclos

Avaliação qualitativa do efeito de agentes de limpeza na camada de lama dentinária: estudo ultra-estrutural em microscopia eletrônica de varredura

Quando qualquer instrumento abrasiona ou corta a dentina, produz na superfície uma camada de lama dentinária ou smear layer. Dependendo do agente de união indicado em Odontologia adesiva, há a necessidade ou não da remoção da camada de lama da superfície dentinária. Com a finalidade de verificar a ação de diferentes substâncias para a limpeza dentinária, utilizamos 20 dentes pré-molares superiores íntegros, mantidos em soro fisiológico, nos quais as coroas foram seccionadas ao meio no sentido mésio-distal. Com instrumento diamantado, removeu-se o esmalte da porção vestibular e da porção lingual da coroa e, com uma broca carbide cilíndrica lisa nº 56, cortou-se aproximadamente 1 mm de dentina com alta rotação sob abundante refrigeração ar/água, para produzir a camada de lama dentinária. em seguida, essa superfície foi tratada com diferentes substâncias e lavada por 30 segundos com spray ar/água. No controle, foi simplesmente utilizado o spray ar/água. Os espécimes foram montados em suportes metálicos, preparados e visualizados no MEV-DSM 950 da Zeiss, em aumentos que variaram de 100 a 5.000 vezes. Os materiais que mais removeram a camada de lama foram, em ordem crescente: 1. spray ar/água; 2. fluoreto de sódio 2%; 3. associação alternada de Dakin/Tergensol; 4. água oxigenada 3%; 5. jateamento com óxido de alumínio 50 mm; 6. flúor acidulado 1,27%; 7. ácido poliacrílico 25%; 8. ácido fosfórico 10%.A smear layer is produced on the dentin surface after abrasion or cutting by instruments. Its removal is indicated or not according to the kind of bonding agent used in adhesive dentistry. The purpose of this study was to evaluate the possible effects of some substances on the smear layer. Twenty upper non-carious premolars, stored in isotonic saline solution, were mesiodistally hemi-sectioned and the buccal and lingual enamel was removed with high speed diamond bur. One millimeter of the dentinal surface was then removed with a water-cooled high speed carbide bur # 56 in order to obtain the smear layer. Different solutions were applied on the dentin surface for 30 seconds, which was then rinsed and dried. The specimens were mounted on metallic holder stubs, prepared, and examined under the scanning electron microscope (DSM 95-Zeiss). Removal of the smear layer by the tested solutions was qualitatively observed, and the solutions, rated according to their performance in increasing order of extent of removal, as follows: 1. air/water spray; 2. 2% NaF; 3. sodium hypochloride/anodic detergent; 4. 3% H2O2; 5. sandblasting with 50 mm aluminum oxide; 6. 1.27% acidulated fluoride; 7. 25% polyacrylic acid; 8. 10% phosphoric acid. The best solutions for the removal of the smear layer were the acid ones

Dossier de travail sur les services aux étudiants /

This study aims to evaluate the role of surface treatments performed on plain carbon fiber posts, in relation to serrated carbon fiber posts, in the retention of the composite core. Fifty carbon fiber posts received surface treatments in order to verify their influence on the retention of the core material. An acrylic resin mold was developed in order to precisely fit the post, leaving a machined space to accommodate a self-curing composite resin. After the surface treatment, a primer was applied on the coronal portion of all posts, which were then dried. They were fitted to the mold and received a 3 mm composite core. All specimens were thermocycled and then stored in distilled water for a week. Tension test was performed at a speed of 0.5 mm/min until there was lack of adhesion or fracture of the core. The conclusions were: a) the values of retention related to aluminum oxide spray (group A), depth cutter diamond burs (group C) and posts with machined coronal portion (group D) were comparable to those of serrated posts (group E), although no statistically significant difference between these groups was found; b) the mean values of core retention in group B (medium grit diamond burs) were statistically lower than those of other groups.Foi avaliado o possível efeito de tratamentos superficiais em pinos de fibra de carbono lisos, quando comparados aos pinos serrilhados, na retenção à resina composta empregada na confecção de núcleos de preenchimento. Foram utilizados cinqüenta pinos de fibra de carbono, divididos em cinco grupos: os quatro primeiros grupos eram constituídos por pinos do tipo liso, cujas superfícies foram tratadas, e o último grupo por dez pinos do tipo serrilhado. Foram desenvolvidas matrizes de resina acrílica com um leito ajustado para conter o pino, com um alargamento na porção coronária para posterior preenchimento com resina composta. Após o tratamento superficial, todos os pinos receberam camadas de "primer", foram secos e então ajustados à matriz de resina, colocando-se a resina composta autopolimerizável na porção coronária para um núcleo de preenchimento de 3 mm. As amostras foram submetidas a termociclagem e armazenadas em água destilada por uma semana. Os espécimes foram testados por meio de ensaios mecânicos de tração, à velocidade de 0,5 mm/min, até o deslocamento do conjunto ou a fratura da resina do núcleo. As conclusões foram as seguintes: a) o tratamento superficial nos grupos tratados por meio de jateamento (Grupo A), pontas diamantadas marcadoras de profundidade para facetas laminadas (Grupo C) e alteração da morfologia da extremidade coronária (Grupo D) conferiu aos pinos lisos valores de retenção comparáveis aos dos pinos serrilhados (Grupo E) nos ensaios de tração, porém sem diferença estatisticamente significativa entre estes grupos; b) os pinos tratados por meio de pontas diamantadas de granulação média (Grupo B) obtiveram valores de retenção menores que os demais grupos

Study of thermocycling effect on the bond strength between an aluminous ceramic and a resin cement

This study evaluated the effect of thermocycling on the bond strength between Procera AllCeram (Nobel-Biocare) and a resin cement (Panavia F, Kuraray CO). Nine ceramic blocks with dimensions of 5x6x6mm were conditioned at one face with Rocatec System (Espe). After, they were luted with Panavia F to composite resin blocks (Clearfil AP-X, Kuraray CO). The nine groups formed by ceramic, cement and composite resin were split up obtaining 75 samples with dimensions of 12x1x1mm and adhesive surface presenting 1mm2±0.1mm2 of area. The samples were divided into 3 groups (n=25): G1 - 14 days in distilled water at 37ºC; G2 – 6,000 cycles in water (5ºC - 55ºC – 30s); G3 – 12,000 cycles in water (5ºC - 55ºC – 30s). The samples were tested in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. Data were analyzed by ANOVA and Tukey tests. The results indicated that mean values of rupture tension (MPa) of G1 (10.71 ± 3.54) did not differ statistically (p <5%) from G2 (9.01 ± 3.90), however there was statistical difference between G1 and G3 (7.28 ± 3.00). It was concluded that thermocycling significantly reduced the bond strength values when samples were submitted to 12,000 cycles.Este trabalho avaliou o efeito da ciclagem térmica sobre a resistência adesiva entre a cerâmica aluminizada (Procera AllCeram, Nobel-Biocare) e um cimento resinoso (Panavia F, Kuraray CO). Nove blocos de cerâmica, com dimensões de 5x6x6mm, foram condicionados em uma de suas faces com o Sistema Rocatec (ESPE). A seguir foram cimentados a blocos de resina composta (Clearfil AP-X, Kuraray CO). Os conjuntos cerâmica-cimento-resina foram cortados em 75 corpos-de-prova com formato retangular com dimensões de 12x1x1mm e superfície adesiva apresentando 1mm2 ± 0,1mm2. Os corpos-de-prova foram divididos em três grupos (n=25): G1 - 14 dias em água destilada a 37ºC, G2 - 6000 ciclos em água (5ºC e 55ºC) e G3 - 12000 ciclos em água (5ºC e 55ºC). Os corpos-de-prova foram ensaiados sob velocidade de 1mm/min em máquina de ensaio universal (EMIC). Os dados foram tratados estatisticamente com os testes de Anova e Tukey e indicaram que os valores médios de tensão de rupturas (MPa) de G1 (10,71 ± 3,54) não diferiram estatisticamente (p < 5%) de G2 (9,01 ± 3,90), porém houve diferença significativa entre G1 e G3 (7,28 ± 3,00). Concluiu-se que a ciclagem térmica diminuiu a resistência adesiva significativamente quando os corpos-de-prova foram submetidos a 12000 ciclos