Precipitated Phase of Titanium Alloy with Adding Nd Elements

通过粉末冶金方法(冷等静压-真空烧结)制备钛合金Ti-6Al-4V-2Cr-1Nd, 经过固溶-时效热处理后, 利用光学显微镜(OM)、; X射线衍射仪(XRD)和透射电镜(TEM)分析合金的微观组织、 物相的组成及析出相的形核特点, 研究添加稀土元素Nd对析出相的影响。; 实验结果表明,在添加1%Nd(质量分数)元素后, 钛合金组织得到了明显细化;通过合金细化成核理论分析发现, 添加稀土元素Nd后,; 固溶时效中Nd_2O_3可以作为形核的基础, 促进形核, 所以稀土Nd元素可以有效促进非均匀形核, 主要析出相Nd_2O_3有利于晶粒的细化,; 是有效的形核剂;在高分辨透射电镜下对离子减薄后的试样进行观察,通过对合金的形貌和析出物进行傅里叶变换(FFT)和反傅里叶变换(IFFT)分析,; 得到清晰的原子排列图, 发现析出相Nd_2O_3与基体alpha-Ti之间存在平行相界面, 经分析为半共格界面。Titanium alloy Ti-6Al-4V-2Cr-1Nd prepared by powder metallurgy method; (cold isostatic pressing and vacuum sintering) was researched. The; microstructure, phase composition and precipitated phase nucleation; process were analyzed by optical microscope (OM), X-ray diffraction; (XRD) and transmission electron microscope (TEM) after solution and; aging treatment. The effect of adding rare earth element Nd to the; titanium alloy on its precipitated phase was studied. The experimental; results showed that the microstructure refinement effect was obvious; after adding rare earth element 1%Nd (mass fraction); based on the; analysis of alloy refining nucleation theory, it was found that after; adding Nd, Nd_2O_3 could serve as the basis of nucleation because of its; high energy, promoting nucleation, there fore Nd could promote the; heterogeneous nucleation effectively, the main precipitation phase; Nd_2O_3 was beneficial to refining crystalline grains and it was; effective nucleating agents. Through high resolution observation of ion; thinning sample, and the morphology of the alloy precipitates were; analyzed by fast Fourier transform (FFT) and inverse fast Fourier; transformation (IFFT). It was found that there was parallel interface; between precipitated phase Nd_2O_3 and matrix alpha-Ti, and it was; semi-coherent interface shown by analysis.河南省重大科技专项项

Effects of Nd element addition on microstructure refinement of Ti-6Al-4V-2Cr alloy

采用冷等静压–真空烧结法制备Ti-6Al-4V-2Cr-1Nd合金,然后进行固溶及时效热处理,通过实验与最小错配度理论计算,研究Nd元素对该合金组织细化的影响,并分析细化机理。结果表明,添加1%(质量分数)的稀土元素Nd后,析出相Nd2O3能有效促进晶粒细化。二维错配度的计算结果证明析出相Nd2O3是有效的形核剂,可促进非均匀形核,增加形核率,从而使晶粒细化。通过对合金试样薄区进行高分辨率观察,发现另一种絮状的、非常细小的、弥散分布的Nd2Ti4O11相,由于其界面错配度较低,也可作为非均匀形核的核心,促进形核,起到细化晶粒的作用。Titanium alloy Ti-6Al-4V-2Cr-1Nd is made by the cold isostatic pressing and vacuum sintering, then the solution and aging heat treatment was carried on the prepared of titanium alloy, the effect of Nd elements on the microstructure refinement and the refinement mechanism were researched and analyzed through the experiment and theory calculation of minimum mismatch degree. The results show that the main precipitation phase Nd_2O_3 can effectively promote the grain refinement after adding rare earth element 1% Nd(mass fraction). The two-dimensional mismatch degree calculation results proved that the precipitated phase Nd2O3 is the effective nucleating agents that can promote the heterogeneous nucleation and increase the nucleation rate, thus promote the grain refinement. Through the high resolution observation of thin area in the sample, another precipitated phase Nd2Ti4O11 is found, which is flocculent, dispersed and very small. Because of the low degree of interface mismatch, Nd2Ti4O11 can also be used as the core of heterogeneous nucleation and promote nucleation, which means it can also play a role in grain refinement.河南省重大科技专项(102105000007

Damage to mangroves from extreme cold in early 2008 in southern China

通讯作者Author for correspondence (E-mail: [email protected])2008年初,我国南方19个省经历了50年一遇的持续低温雨雪冰冻天气。极端气候对华南沿海各省的红树林区造成不同程度的危害。2008年3月,在我国南方各省红树林区的10个代表性地点,对这次寒害造成的红树植物伤害程度进行了系统的调查。结果表明:冬季低温对红树林的影响极为显著,特别是在低纬度的海南、广西和广东湛江,由于极端低温正值夜间退潮,对红树林的影响更为显著;在纬度较高的福建,本地红树种类秋茄(Kandelia obovata)、桐花树(Aegiceras corniculatum)和白骨壤(Avicennia marina)及引种的木榄(Bruguiera gymnorrhiza)等,由于长期适应于冬季较低的气温或在种植前经过抗寒锻炼,具有较强的抗寒能力。各地主要红树植物中,广布种秋茄、桐花树和白骨壤最为耐寒,其耐寒性均大于红树科的木榄、海莲(Bruguiera sexangula)和红海榄(Rhizophora stylosa)。海桑(Sonneratia caseolaris)对温度的敏感性最强,抗寒能力最低,因此,即使在其原产地海南也受到较为严重的寒害,在纬度更高的引种地出现大面积受害甚至全部死亡,而从孟加拉国引种的无瓣海桑(Sonneratia apetala)却显示出一定的抗寒能力。同一地点的红树植物幼苗的抗寒能力低于大树。此次寒害也造成了苗圃场的种苗大量死亡,成熟的植株提前落花落果,这势必会影响后继一两年内红树林的自然更新和人工造林。因此,在未来红树林造林或人工引种中,一定要考虑到红树植物的抗寒能力。国家自然科学基金(30671646和30700092);厦门大学“闽江学者”启动基

呋喃基聚酯的结构与性能关系研究进展

呋喃基聚酯是指以2,5-呋喃二甲酸(FDCA)为主要单体合成的生物基或部分生物基高分子,其主链含有刚性的呋喃环,因而在结构、性能上与大规模使用的传统石油基芳香族聚酯(如PET、PBT)相似,有望在瓶、片、薄膜、化纤等领域部分替代后者。本文综述了呋喃基聚酯的分子结构、聚集态结构以及力学、气体阻隔、降解等性能方面的最新研究进展,讨论了结构与性能之间的关系。重点关注呋喃基聚酯突出的阻隔性能及其对应的影响因素,主要从分子结构(呋喃环的非对称性和极性)和聚集态结构(结晶等)两方面加以阐明。简介了呋喃基聚酯的发展现状及其在包装、纺织等领域的潜在应用,并展望其主要研究趋势

The Application of Sensory Stimulation in The Intervention of Alzheimer's Disease

阿尔茨海默病（Alzheimer&rsquo;s disease，AD）是一种神经退行性疾病，药物治疗是目前AD治疗的主要策略，但仅起到延缓或减轻作用。本文旨在综述各种感觉刺激和多感官刺激对AD的影响，并解释可能的机制，为进一步研究提供新思路。对光刺激疗法、气味刺激疗法、声音刺激疗法、节律性刺激、多感官刺激进行了系统分析，结果显示，这些感觉和多感官刺激可以有效改善AD的病理状态，唤起记忆，改善认知和行为。</p

Thermogravimetric behaviors of biomass′ chemical components under air or syngas

在热重分析仪上,分别在空气和合成气气氛下,对生物质三种化学组分(纤维素、半纤维素和木质素)的热重行为进行了研究,考察了两种不同气氛下生物质及其三种组分的热化学转化温度区间分布;同时通过合成样品(以不同比例混合的三种组分的混合物)热重曲线的实验值和理论计算值的对比分析,考察了生物质化学组分在不同气氛下热重行为的相互作用.结果表明,在空气和合成气气氛下生物质各种化学组分发生热化学反应从难到易的顺序为木质素>纤维素>半纤维素,这是由其不同的化学结构决定的,但不同气氛下各组分的具体热重行为存在一定差别.在合成气气氛下木质素及半纤维素在与纤维素的共热解过程中存在明显的协同作用,而在空气气氛下半纤维素及纤维素在与木质素的共燃烧过程中存在一定的协同作用,这与各组分在不同气氛下所处的热化学反应温度区间具有一定的关系

氢气和合成气下生物质高压液化过程的实验研究

在小型高压反应釜中以四氢萘为溶剂，氢气和合成气为液化反应气，通过对不同液化条件下所得液化产物的收率及性质分析，考察了不同液化条件（反应温度、反应时间、反应气压力）对锯屑高压液化行为的影响；同时在相同液化条件下，通过液化产物收率和性质的分析，考察了气氛对锯屑高压液化行为的影响，探讨了用合成气代替氢气进行液化的可行性。结果表明，在氢气和合成气气氛下，随着反应温度的升高、反应时间的延长或反应压力的提高，液化油的收率都是增加的，但各种条件对液化油收率的影响程度不同。温度影响最大，时间影响次之，而液化气压力的影响最小。其他液化条件完全相同的情况下，氢气和合成气下所得产物的收率及性质相近，用合成气代替氢气液化具有可行性。在此条件下优化的液化反应条件为，以四氢萘为溶剂，反应温度为300℃，气体压力为2MPa，反应时间为30min，转化率为75．1％，液化油收率高达48．4％

含聚乳酸软段聚氨酯材料的结构与性能研究

以左旋丙交酯(L-LA)为原料,首先合成左旋聚乳酸二元醇(PLLA),然后以PLLA、聚四氢呋喃二元醇(PTMG)为软段, 4,4′-二环己基甲烷二异氰酸酯(HMDI)、1,4-丁二醇(BDO)为硬段,采用二步法合成一系列含PLLA软段的聚氨酯化合物。通过核磁氢谱、红外分析、差示扫描量热仪、力学性能测试等手段确认并分析了含PLLA软段的聚氨酯弹性体结构与性能的关系。结果表明,软段的性质如玻璃化转变温度、熔点等会明显影响聚氨酯材料的玻璃化转变温度和熔点;虽然刚性软段PLLA可以显著提升聚氨酯材料的力学性能,但是也会导致材料在大应变下的首次回复性能大幅下降